The samples of the series Co1+ySnyFe2- 2y- xCrxO4 ferrites with x = 0.0, 0.1, 0.2, 0.3, 0.4, 0.5 and y = 0.05, were prepared by the usual double sintering ceramic technique. The single- phase spinel structure of the samples was confirmed by using X- ray diffractometry technique. The lattice parameter ’a’ with an accuracy of ± 0.002 Å were determined using Bragg peaks of XRD pattern. The lattice parameter ’a’ decreases with concentration, x, which is due to the difference in the ionic radii of Cr3+ and Fe3+ ions. The X- ray intensity calculations were carried out in order to determine the possible cation distribution amongst tetrahedral (A) and octahedral [B] sites. The X- ray intensity calculations show Cr3+ ions occupying B site. The saturation magnetization, σs, and magneton number, nB (the saturation magnetization per formula unit), measured at 300 K determined from high field hysteresis loop technique decrease with increase in concentration, x, suggesting a decrease in ferrimagnetic behaviour. Thermal variation of low field a.c. susceptibility measurements from room temperature to about 800 K exhibits almost normal ferrimagnetic behaviour and the Curie temperature, TC determined from a.c. susceptibility data decreases with increase in x.
Mastication of gutta percha (trans-polyisoprene) resulted in the selective scission of molecules, producing a narrower distribution of lower molecular weights. The mechanical properties of the samples also underwent a significant change due to mastication. The greater the content of incompatible substances (salts and oxides) in commercial gutta percha. the more substantial were these effects. The atmosphere (air, N2, O2) in which the experiments were conducted yielded significantly different results. The decrease in molecular weight was far greater in an O2 atmosphere than under a current of nitrogen or air, owing to the combination of double bonds with O2. 相似文献