CJ325NC尾板裂纹分析

用ＳＥＭ对尾板裂纹进行了分析。结果表明，加工不良产生的应力集中是尾板裂纹形成的主要原因。display     

表面缺陷对钢缆寿命的影响

通过对断裂钢缆的检测分析，认为拧成钢缆的钢筋表面缺陷如机械划痕、严重的腐蚀麻坑等是引起钢缆早期断裂的主要原因。     

Observation of atomic steps on CaCO3 crystal surface

By using scanning polarization force microscopy,the deliquescence process and the atomic steps on the cleavage surface of CaCO3 in air were studied in situ.Under an exposure to medium umidity(-57%),the sloiw step movement has been observed.     

THE MECHANISM STUDY OF EFFECT OF CALCIUM AND ALUMINIUM IONS ON FLOCCULATING PROCESS OF KAOLIN

The effects of Ca^2 and Al^3 ious on flocculating process of kaolin using ployacrylamide as flocculant was studied. Mechanism of the effects was investigated and discussed through molecularorbit (MO) theory, solution chemistry calculation and electronic probe examination in this article.     

提高破碎机锤头（板锤）寿命的研究

鞍钢东鞍山烧结厂的反击式破碎机锤头和腭式破碎机板锤,材质为65Mn,热处理工艺为普通淬火加中温回火,使用寿命为76h,满足不了生产要求。在不改变原材质的情况下,采用重新加热或锻后余热薄壳淬火-自回火新工艺后,获得了如下结果:①进一步发挥了材料潜力,使锤头寿命提高40%以上,使板锤寿命提高100%;②表面层获得马氏体组织,心部获得具有一定韧性的混合组织,从而获得了良好的强度与韧性的配合;③采用锻后余热进行薄壳淬火,可降低生产费用。     

节理岩体变形特性的参数研究及等效弹模的数值确定

分析了现场节理岩体变形性质的影响因素，具体研究了节理岩体等效弹模计算方程中的裂纹密度Х和裂纹状态系数ｑ，给出了如何利用已有的节理分布的量测数据及节理面和岩石力学性质的测试结果确定节理化岩体等效弹模的方法，最后用一实例对所给方法进行了验证。     

提高磨削表面完整性的工艺研究

本文报道了使用正交试验设计法寻求合适的磨削工艺参数的实验，揭示了磨削工艺条件对磨削表面完整性的影响。     

严格工艺 减少球铁曲轴裂纹缺陷

<正> 泰兴县农机厂是生产S195柴油机曲轴和492汽车曲轴的专业厂家,生产球铁曲轴已有十多年历史,铁水年熔化量2200多吨,使用3T/h大双热风冲天炉,机器造型。1990年下半年,发现曲轴轴颈在中频淬火后出现微裂纹。严重时,S195曲轴废品达20％以上,492曲轴废品达80％以上,而且基本都在相同的位置上(见下图)。这种裂纹,肉眼看不到,要在磁力探伤机上才能发现。工厂曾采取了多种措施,未能消除,又专门到无锡某研究所取样进行显微分析,结论是存在二次夹渣。