原料磨机端盖开裂的修复

1磨机进料端盖裂缝某厂2.6m×13m管磨机,生产中发现其进料端盖沿端面法兰裂缝长达1.7m左右,必须更换新的端盖或进行焊接检修。由于缺少备件加上现场生产需要,更换新备件显然是不可能的,因而决定补焊修复。端盖结构及其裂缝位置见图1。表1影响ZG35Ⅱ机械力学性能的化学组成%元素     

旧外墙面维修涂装技术

详细分析了建筑旧外墙面存在开裂、渗漏水、污损等问题的原因。并提出如何对旧墙面进行维修和涂装翻新的处理技术。     

Hydrogen-induced cracking behaviors of Incoloy alloy 825

The effect of hydrogen on the fracture behaviors of Incoloy alloy 825 was investigated by means of slow strain rate testing (SSRT).Hydrogen was introduced into the sample by electrochemical charging.The results show that surface microcracks form gradually during aging at room temperature when desorption of hydrogen takes place after hydrogen charging at a current density of 5 mA/cm 2 for 24 h.SSRT shows that the increase of ductility loss is significantly obvious as the hydrogen charging current density inc...     

Hydrogen induced cracking of X80 pipeline steel

The hydrogen-induced cracking (HIC) behavior of X80 pipeline steel was studied by means of electrochemical charging, hydrogen permeation tests, tension test, and scanning electron microscopy (SEM). The experimental results indicate that the increase of charging time and charging current density or the decrease of the solution pH value leads to an increase of the hydrogen content in X80 steel, which plays a key role in the initiation and propagation of HIC. It is found that the majority of macro-inclusions w...     

结构钢缺口板断裂试验及数值分析

通过对25个结构钢缺口板进行的单向拉伸断裂试验,验证了提出的结构钢广义屈服模型和椭球面断裂准则.用ANSYS软件中的参数化设计语言APDL和用户编程功能UPFs,将提出的静水应力型广义屈服模型编制成子程序模块,对结构钢缺口板断裂试验进行了基于广义屈服模型和椭球面断裂准则的数值模拟分析.试验结果表明:裂纹起始于缺口边缘内侧,裂纹在厚度方向贯通后沿宽度发展,试件最终断裂于缺口薄弱断面.缺口板断裂应力场分析表明,提出的椭球面断裂准则对预测结构钢缺口板初始开裂具有广泛适用性和较高精度.     

Influence of fly ash on early-age cracking behavior of high-flowing concrete

The effects of quality and content of fly ash on the early-age cracking behavior of high-flowing concrete (HFC) were investigated. The early-age cracking behavior of the HFC was analyzed by combining the tests of evaporation capacity and electrical resistivity of the HFC. In these tests, a modified flat-type specimen was adopted. The results show that the HFC will have a lower evaporation capacity when it is mixed with fine fly ash, while it will have a higher evaporation capacity when grade III fly ash is used as mineral admixture. And the electrical resistivity rate of HFC reduces with the increase of the content of fly ash. A nonlinear relationship exists between the cracking time of HFC and the minimum electrical resistivity. The early-age cracking behavior of HFC with fly ash can be enhanced by appropriately increasing the fine particle content and MgO, K₂O, and SO₃ contents of fly ash. The optimal content of fly ash, which makes a satisfied early-age cracking behavior of HFC, is obtained. And when the content of fly ash exceeds a critical value, the early-age cracking behavior of HFC will rapidly decrease. Foundation item: Project(50478003) supported by the National Natural Science Foundation of China; Project(2002F007) supported by the Natural Science Foundation of Fujian Province, China     

周期阵列压痕奇异应力场与开裂（PartⅡ：压痕开裂临界载荷）

周期阵列压痕方法是研究微观摩擦学的工具之一。由于周期阵列刚性压头压在半平面弹性体的表面时,会产生周期的Ⅰ型奇异压应力场,该奇异应力场的应力集中达到一定程度时,即达到临界条件时,该奇异应力场所在的边界将开裂。压痕边界的开裂问题是一个新型的断裂力学问题,通过边界移动的能量释放率的分析给出了压痕边界开裂能量释放率数学表征,并给出边界开裂的临界载荷和临界开裂角。     

水处理容器缠绕不饱和聚酯体系研究

研究了水处理容器缠绕不饱和聚酯树脂体系 ,重点阐述了不饱和聚酯凝胶期控制、表干及树脂增韧方法和纤维缠绕复合层的力学性能 ,分析了水容器受压树脂环向开裂的原因 ,探讨了提高树脂开裂强度的措施     

杨房沟水电站地下洞室关键岩石力学问题及工程对策研究

杨房沟水电站地下洞室群规模宏大、地质条件复杂,施工期围岩稳定问题突出。为解决洞室开挖过程中普遍揭露的脆性岩体高应力破坏、缓倾结构面导致的顶拱变形破坏、喷层开裂脱落等岩石力学问题,结合施工地质、监测成果和数值模拟开展动态反馈分析,对洞群围岩稳定性进行了系统地分析和预测。结果表明,在洞室群开挖过程中,上游侧拱肩位置存在应力集中,是导致脆性硬岩发生片帮破坏的主要原因,而及时、有效的系统支护对抑制围岩应力型破坏至关重要;缓倾结构面对顶拱围岩变形与稳定起着控制性作用,主要表现为断层下盘岩体坍塌破坏和深层变形问题;在中高地应力条件下,受不利地质构造和施工质量等因素控制,洞室顶拱混凝土喷层容易发生开裂、脱落问题。通过开展施工期围岩监测反馈分析,不仅能够解释围岩变形破坏机制,而且能够为支护设计优化和信息化施工提供科学依据。