薄板搅拌摩擦焊焊缝区应力集中的有限元分析；减少热输入控制叶盘焊接变形的数值模拟；引线间距对QFP焊点的可靠性影响的有限元分析；裂解炉管焊接残余应力场中裂纹扩展行为的数值分析     

Effect of Rare Earth Elements on Thermal Fatigue Property of Low Chromium Semi-Steel

The effect of rare earth elements on eutectic carbide‘s morphology of low chromium semi-steel in as-cast state and after heat treatment was investigated, and accordingly, the thermal fatigue property of this material was studied. The results show that RE can improve the eutectic carbide‘s morphology, inhibit the formation and propagation of thermal fatigue cracks, therefore, promote the thermal fatigue property, which is more noticeable in case of the RE modification in combination with heat treatment. The optimal thermal fatigue property can be obtained when treated with 0.2% RE modification as well as normalization at 950℃ for 3h.     

GH150合金叶片的疲劳性能

研究了高压压气机叶片用Ni基高温合金GH150的疲劳性能.试验方式分别为轴向拉伸和旋转弯曲疲劳.试验温度为500℃和600℃,试验按置信度90%和存活率50%进行.轴向拉伸和旋转弯曲疲劳性能试验Kt=1,应力状态分别为r=0.1和r=～1.用升降法求得500℃轴向拉伸疲劳107疲劳极限为481.8MPa,600℃疲劳极限为502MPa;500℃旋转弯曲疲劳107疲劳极限为418.57MPa,600℃为435.71MPa.轴向拉伸和旋转弯曲疲劳S-N曲线显示,随载荷应力的增加,疲劳循环次数呈减小趋势;在低应力长寿命区600℃的疲劳性能较500℃稍优.疲劳试样断口形貌照片显示,断口的源区、扩展区和最后瞬断区特征清晰;扩展区有明显的疲劳条带;瞬断区为韧性断裂.     

905mm末级叶片应力腐蚀和腐蚀疲劳研究

本文研究了引进型300MW汽轮机905mm末级叶片材料在80℃、22％氯化钠介质中的应力腐蚀开裂行为;测定了材料在空气,蒸馏水和80℃、22％氯化钠介质中不同平均应力时的条件疲劳极限。结果表明,在上述介质条件下,905mm末级叶片材料的应力腐蚀敏感性和腐蚀疲劳强度与869mm末级叶片材料相近。     

Fowler—Nordheim高电场应力引起的MOS结构损伤研究

本文研究了Ｆｏｗｌｅｒ－Ｎｏｒｄｈｅｉｍ高电场应力引起的ＭＯＳ结构损伤及其室温退火。结果表明有四种损伤产生，氧化物正电荷建立，Ｓｉ／ＳｉＯ２快界面态增长，慢界面态产生和栅介质电容下降，当终止应力后，前三种损伤在室温下有所恢复，但最后一种损伤没有变化，实验还表明：产生的慢界面态分布在禁带上半部；高电场下栅介电容呈现无规阶梯型下降，对四种损伤及其室温退火机理进行了讨论，还给出产生的慢界面态对高频电容－     

砼受压损伤力学本构模型的研究

本文利用ＭＴＳ公司８１５．０２型电液伺服试验系统对砼进行了等应变速率加载控制的应力一应变全曲线试验，应用不可逆热力学和内变量理论的成果建立了砼损伤力学模型，并用概率统计的观点分析了损伤的演化规律。由于考虑了不可逆变形的影响，本文所建本构模型与实验吻合较好。     

表面有横向裂纹的抽油杆寿命估算

应用断裂力学理论和实验结果,讨论了表面有横向裂纹的抽油杆寿命估算中的4类典型问题,为正确分析抽油杆断裂事故的发生提供了依据,也为抽油杆合理安全使用,旧杆再利用的可能性分析及其剩余寿命计算和制订抽油杆检测周期等方面提供参考。