SiC晶须对Si3N4陶瓷基复合材料机械强度的影响

制备了含10vol％,20vol％及30vol％SiC晶须的Si_3N_4基复合材料,对其室温及高温机械强度的测试研究表明,SiC晶须对基体的高温机械性能有明显的增强作用。含20vol％SiC晶须的复合材料1200℃下强度达780MPa,比基体材料提高50％。通过SEM和TEM研究,讨论了SiC晶须增强的原因。     

Coking kinetics of a Cr2O3/Al2O3 catalyst during 1-butene dehydrogenation: Effect of H2 partial pressure

The influence has been studied of the partial pressure of hydrogen (0–30 kPa) upon the coking rate of a Cr₂O₃/Al₂O₃ commercial catalyst during 1-butene dehydrogenation. Coke deposition has been analysed using a monolayer-multilayer reversible coke growth model (MMRC model). This model provides good fits to the experimental data, within the range of partial pressure of H₂ studied, and allows us to estimate the main kinetic parameters involved in the coking-deactivation process. The results obtained reveal a dual effect of hydrogen: competition against 1-butene for the active sites and the removal of coke precursors from the catalyst surface. Bom effects diminish the coking rate as the H₂ partial pressure is increased.     

Kinetic modelling of the catalytic conversion of synthesis gas

A kinetic study for the one-step conversion of synthesis gas to gasoline on a ZnO–Cr₂O₃–ZSM-5 catalyst is described. On this catalyst, three reactions are involved in the overall transformation of synthesis gas: the methanol synthesis, the conversion of methanol to hydrocarbons and the water–gas shift reaction. Under the operating conditions selected for the study, it was found that the water–gas shift was at equilibrium and the methanol was completely converted to hydrocarbons. Consequently, it was postulated that the kinetics of the limiting reaction step, the methanol synthesis on the ZnO–Cr₂O₃ component, was the one that controls the overall reaction rate. Three kinetic model equations describing the rate of synthesis gas conversion on the bifunctional catalyst, were considered to fit the data of the experimental runs performed in a Berty well-mixed reactor. Those equations were derived under very special conditions where the methanol decomposition term could be neglected. It was also observed that in the kinetic equations a term involving the fugacity of CO₂ was required to predict the rate properly. The catalyst deactivation was also taken into account in the analysis.     

On the catalytic C-H activation of some silicon dioxide overlayers on thin metal film systems — An observation on the isokinetic effect

Kinetic data on the exchange reaction betwee hexane and deuterium have recently been reported by Maier and coworkers [1]. The reaction was catalysed by a series of platinum or rhodium systems, some of which had the property that the upper surface was shielded by a silica overlayer. The data are reinterpreted to indicate an isokinetic temperature of 580 K. This observation indicates that all the catalysts behave in a similar manner, which means that the exchange reaction does not require a free metal surface.     

Electrochemical performance of nanocrystalline Li3V2(PO4)3/carbon composite material synthesized by a novel sol–gel method

A novel sol–gel method based on V₂O₅·nH₂O hydro-gel was developed to synthesize nanocrystalline Li₃V₂(PO₄)₃/carbon composite material. In this route, V₂O₅·nH₂O hydro-gel, NH₄H₂PO₄, Li₂CO₃ and high-surface-area carbon were used as starting materials to prepare precursor, and the Li₃V₂(PO₄)₃/carbon was obtained by sintering precursor at 750 °C for 4 h in flowing argon. The sol–gel synthesis ensures homogeneity of the precursors and improved reactivity. The sample was characterized by XRD, SEM and TEM. X-ray diffraction results show Li₃V₂(PO₄)₃ sample is monoclinic structure with the space group of P2₁/n. The TEM image indicates that the Li₃V₂(PO₄)₃ particles modified by conductive carbon are about 70 nm in diameter. The Li₃V₂(PO₄)₃/carbon system showed that the discharge capacities in the first and 50th cycle are about 155.3 and 143.6 mAh/g, respectively, in the range of 3.0–4.8 V. The sol–gel method is fit for the preparation of Li₃V₂(PO₄)₃/carbon composite material which may offer some favorable properties for commercial application.     

浅谈P3软件在电力基建工程中的应用

P3软件是一套体现了现代化项目管理理念的项目管理工具，在建设管理上推广应用P3工程管理软件，可以提高各参建单位的工作效率、加快工程信息交流、数据共享和工程进度管理水平，在管理上尽快与国际接轨，本文就P3软件在电力基建工程中的应用做以简单介绍。     

Scrolls and nested tubes in multiwall carbon nanotubes

Recent high-resolution transmission electron microscopy (HREM) studies of multiwalled carbon nanotubes (MWCNTs) reveal a class of defects analogous to edge dislocations in a crystal. These defects are believed to mark the transition from scrolls on one side to nested tubes on the other. On the tube side, layer spacing becomes irregular. Analysis of the helicity of the tubes shows a strong correlation between diameter and helicity. This suggests that the organizing principle for the tubes is not Van der Waals forces, as in the case of graphite or turbostratic carbon, but preservation of helicity. Based on these observations and total energy calculations, the authors speculate that graphene monolayers initially form scrolls and subsequently transform into multiwall nanotubes through the progression of defects. Scrolls and nested tubes thus coexist within a single MWNT.     

Aqueous electrochemical intercalation of bromine into graphite fibers

For the first time, graphite fibers have been electrochemically intercalated with Br⁻ that have the same structure and properties as those intercalated from vapor phase Br₂. This was accomplished by intercalating pitch-based Thornel^® K-1100 graphite fibers at low temperature (near 0 °C) and high currents (2 A) for long times (6 h). The mechanism appears to be that Br⁻ is oxidized to aqueous Br₂ which, when sufficient local concentration builds up, intercalates the fiber. This was confirmed by intercalating K-1100 fiber in a saturated aqueous Br₂ solution without passing an electrical current. The applied voltage does apparently lower the activation energy of the reaction as evidenced by the observation that P-120 and P-100 fibers will not intercalate in aqueous Br₂ unless a voltage is applied.