汽轮发电机运行过程中,转子轴颈磨损拉伤的情况较为普遍,采用微弧冷焊技术可以实现对损伤部位的修复。针对25Cr2Ni4MoV材料转子,通过焊接工艺试验和试样性能检测,得到一种可靠的微弧冷焊工艺;并通过对焊缝无损检测标准和焊后尺寸恢复工艺的研究,形成了一套完善的轴颈损伤修复工艺方案。     

铝-锂合金腐蚀性能研究综述

综述了铝-锂合金孔蚀、晶间腐蚀、应力腐蚀断裂(SCC)及剥蚀的研究现状。阐述了加工状态、热处理、显徽组织及腐蚀介质对一些铝-锂合金孔蚀及晶间腐蚀行为与SCC敏感性的影响及其影响机制．同时报道了一些研究铝-锂合金剥蚀的新方法，并提出了进一步研究的方向．     

Hydrogen embrittlement of high strength steel electroplated with zinc-cobalt alloys

Slow strain rate tests were performed on quenched and tempered AISI 4340 steel to measure the extent of hydrogen embrittlement caused by electroplating with zinc-cobalt alloys. The effects of bath composition and pH were studied and compared with results for electrodeposited cadmium and zinc-10%nickel. It was found that zinc-1%cobalt alloy coatings caused serious hydrogen embrittlement (EI 0.63); almost as severe as that of cadmium (EI 0.78). Baking cadmium plated steel for 24 h at 200 °C gave full recovery of mechanical properties but specimens plated with zinc-1%cobalt and then baked still failed in 89% of the time of unplated controls. It was shown that hydrogen uptake and embrittlement could be controlled by depositing thin layers of cobalt or nickel at the steel/coating interface. For example, the least embrittlement was caused by zinc-10%nickel (EI 0.037) due to a nickel rich layer with very low hydrogen diffusion coefficient that formed during the initial stages of electroplating. Similarly, a 0.5 μm nickel layer was effective in lowering the embrittlement caused by zinc-1%cobalt to that of zinc-10%nickel. Furthermore, a 0.5 μm cobalt layer deposited before a zinc-1%cobalt coating gave virtually 100% recovery of mechanical properties after baking.     

静磁场对ZK60镁合金组织的影响

试验发现在镁合金的凝固过程中施加静态磁场能有效细化晶粒，减小晶界化合物的厚度，同时，出现了大量细小块状化合物，这有利于提高镁合金的成形性能。     

An electrochemical method for the preparation of Mg–Li alloys at low temperature molten salt system

Mg–Li alloys have been prepared by electrolysis in a molten salt electrolyte of 50% LiCl–50% KCl (mass%) at low temperature of 420–510 °C. The effects of electrolytic temperature and cathodic current density on alloy formation rate and current efficiency were studied. For the deposition of metallic lithium on the cathode consisting of solid Mg and liquid Mg–Li, both electrolytic temperature and cathodic current density have no obvious influence on current efficiency; while for the deposition of metallic lithium on the solid magnesium cathode, both electrolytic temperature and cathodic current density greatly affect alloy formation rate and current efficiency. The optimum electrolysis condition is—molten salt mixture, LiCl:KCl = 1:1 (mass%), electrolytic temperature: 480 °C, cathode current density: 1.13 A cm⁻². Mg–Li alloys with low lithium content (about 25 wt% Li) were prepared via electrolysis at low temperature following by thermal treatment at higher temperature.     

机械合金化Al—12Ti—6Nb合金的热稳定性

将机械合金化（ＭＡ）Ａｌ－１２Ｔｉ－６Ｎｂ合金在５５０℃下空气中长时间暴露后，用光学显微镜和电子探针对其组织结构变化进行了观察与分析，测定了维氏硬度。结果表明，ＭＡＡｌ－１２Ｔｉ－６Ｎｂ表现出良好的热稳定性，在５５０℃下暴露２００ｈ后，Ａｌ３Ｔｉ中的亚稳的α－Ｔｉ核才全部转变为Ａｌ３Ｔｉ，Ａｌ３Ｔｉ颗粒随之粗化，饼状的Ａｌ３Ｔｉ变成椭球体；Ａｌ３Ｔｉ颗粒的粗化是通过Ｔｉ，Ａｌ原子扩散所控制的α－Ｔ     

锆基块体非晶合金的力学性能研究进展

本文叙述了锆基块体非晶合金的制备方法，优异的性能，特别是对其力学性能研究领域的最新进展进行了综述。并与传统晶态合金作了适当的对比，锆基块体非晶合金具有优异的力学性能，如弹性比功、超塑性、断裂韧性等，此类合金的应用将不断拓宽。     

Investigation of the titanium–indium system

The phase diagram of the Ti–In system was determined using DTA, XRD and EDX analyses. The existence of the phases Ti₂In₅ [Mn₂Hg₅ type structure, space group P4/mbm, a=0.99995(3), c=0.29960(2) nm] and Ti₃In [Ni₃Sn type structure, space group P6₃/mmc, a=0.5978(1), c=0.4812(1) nm] was confirmed. The phase previously labeled Ti₃In₂ was found to exist in a narrow homogeneity region near Ti₅₆In₄₄. Rietveld refinement of the XRD powder pattern yielded solutions compatible with a Cu₃Au-type or a BiIn-type crystal structure, but not with a CuAu-type crystal structure. Furthermore, at 38.5 at.% In, a new phase was observed having a γ-brass related crystal structure [Ti₈In₅, space group , a=0.99578(6) nm]. The intermetallic phases were formed by a cascade of peritectic reactions ending in a eutectic at >99 at.% indium between Ti₂In₅ and (In) at 0.4 K below the melting temperature of pure indium.     

基于消失模铸造的AZ91镁合金组织改性研究

研究了机械振动处理技术对AZ91合金在消失模铸造条件下的组织形貌的影响,以及该铸态组织在半固态等温热处理过程中的组织演变,并探讨了振动细化机理和组织演变机理。结果表明:机械振动能显著地细化AZ91合金的铸态组织;在液固相区570℃等温处理时,其铸态组织都能由枝晶转变为球状晶组织,而且振动处理可获得更加细小并且均匀的球状组织。等温处理时间过长时,两种组织都会发生合并长大。