奥氏体化温度及冷却方式对20Mn2SiVB钢组织及性能的影响

通过各种试验手段,研究了20Mn2SiVB钢不同奥氏体化温度及不同冷却方式处理后其显微组织及其强度和塑性的变化,确定了最佳的热处理工艺。结果表明:900℃奥氏体化后风冷时钢的强塑性最好;在强塑性最佳时的微观组织是铁素体+粒状贝氏体。     

Temperature Dependence of the Magnetocrystalline Anisotropy in Nd_2Co_(14)B Compound

Easy and hard magnetization curves of Nd_2Co_(14)B compound have been measured withextracting-sample-magnetometer(μ_0H_(max)=6T)at 10～300 K.Magnetic anisotropy constants K_1 and K_2have been determined by fitting the hard magnetization curves,in which only K_1 ,K_2 and misalignment anglehave been taken as fitting parameters.The values of K_1 and K_2 at 4.2 K were derived by extrapolation.Anisotropy coefficients,x_2~° and x_4~°were derived from the anisotropy constants.The anisotropy constant K_2increases rapidly with increasing temperature when TT_(sr).The temperature depen-dence of the magnetic anisotropy coefficient x_2~° was fitted with the formula.The anisotropy coefficients x_2~°can be well described by the tenth-power law from 4.2 K to T_(sr)and by the sixth-power law from T_(sr_ to 300 K.     

Preparation and characterization of TiO2 photoelectrode codoped with aluminum and boron and its application in dye-sensitized solar cell

Nanocrystalline titania films codoped with aluminum and boron were prepared by cathodic vacuum arc deposition. In the process, titanium alloy target was used under an O2/Ar atmosphere, and sensitization of films were carried out by natural dye-sensitized complex in anhydrous ethanol. The structure, surface morphology and UV-vis spectra of titania films codoped were measured by X-ray diffraction analysis, scanning electron microscopy and ultraviolet-visible spectrometer. Theas-deposited films are found to be amorphous. The films annealed were examinedto be of anatase structure with orientation along the (101) planes, the averagecrystal size is in the range between 41 and 45 nm. SEM results show that thereare some pores in the codoped titania films, the optical properties of the dye-sensitized films were also measured which reveals that the spectral responses of films shift to the visible region. Under simulated sunlight illumination, the overall energy conversion efficiency of dye-sensitized nanocrystalline solar cell is 0.9%.     

CO2气体保护焊机操作注意事项

介绍了焊工在CO2气体保护焊机的安装、使用、维护保养及维修中的注意事项。     

含Cl^-溶液中SO4^2-对316不锈钢临界点蚀温度的影响

采用外加恒电位下腐蚀电流-温度扫描方法研究了在0．5％Cl^-溶液中，SO4^2-浓度对316不锈钢点腐蚀行为的影响．结果表明，随着SO4^2-浓度的增加，钝化电流增加，开路电位降低．当SO4^2-浓度低于0．42％时，316不锈钢的临界点蚀温度比不存在SO4^2-时的临界点蚀温度低；当SO4^2-浓度大于0．42％时，临界点蚀温度比不存在SO4^2-时的临界点蚀温度高．从离子竞争吸附的角度进行分析，对SO4^2-加速与抑制点蚀两种作用规律的形成原因进行了解释．     

基于I2C总线技术的等离子喷焊系统的研究

阐述了基于I^2C总线技术的等离子喷焊过程控制系统的设计原理，介绍了软硬件及接口设计技术。实践表明，采用I^2C总线技术，不仅使系统的芯片大大减少，系统的灵活性增强，而且提高了系统的抗干扰能力。     

Preparation and characterization of GaN films grown on Ga-diffused Si （111） substrates

Hexagonal GaN films were prepared by nitriding Ga2O3 films with flowing ammonia. Ga2O3 films were deposited on Ga-diffused Si (111) substrates by radio frequency (r.f.) magnetron sputtering. This paper have investigated the change of structural properties of GaN films nitrided in NH3 atmosphere at the temperatures of 850, 900, and 950℃ for 15 min and nitrided at the temperature of 900℃ for 10, 15, and 20 rain, respectively. X-ray diffraction (XRD), scanning electron microscopy (SEM), transmission electron microscopy (TEM) and X-ray photoelectron spectroscopy (XPS) were used to analyze the structure, surface morphology and composition of synthesized samples. The results reveal that the as-grown films are polycrystalline GaN with hexagonal wurtzite structure and GaN films with the highest crystal quality can be obtained when nitrided at 900℃ for 15 min.