含钡合金在钢液中的脱氧行为研究

在MoSi2炉上采用MgO质坩蜗对钢管进行了含钡合金脱氧行为的研究。实验中钡系合金主要选取SiAUBa、SiCaBa、SiAlBaCa、SiAlBeCaSr及用于钙处理的SiCa包芯线，选用Al作为对比脱氧剂，考察了钡系合金脱氧的全氧含量，脱氧产物的分布、尺寸和形貌，探讨了钡系合金脱氧和对夹杂物变性作用的机理。     

Repair of Cracked Aluminum Overhead Sign Structures with Glass Fiber Reinforced Polymer Composites

Transportation departments have been using aluminum overhead sign structures since the 1950s. It is well documented that cracks develop in the welds between diagonal and chord members due to fatigue stresses from wind-induced vibration of the slender members. The cracks propagate to complete failure of the members, which can cause collapse of the truss and inflict injuries. The original design of overhead sign structures did not consider fatigue as a limit state. In addition, field welding of aluminum structures for any possible repairs is prohibited. A repair method for the cracked aluminum welded connections between diagonals and chord members using glass fiber reinforced polymer composites (GFRPs) is proposed. The static load carrying capacity of the welded connection, and the cracked connection repaired with GFRP composites are established. The paper describes the surface preparation of the aluminum tubular members, and the architecture and application sequence of the GFRP composite to retrofit the connection. Experimental results are presented from static tests of welded aluminum connections, welded aluminum connections retrofitted with GFRP composites, and new aluminum connections that depend only on GFRP composite elements for their strength. The results from monotonic static tests carried out on cracked welded specimens from actual sign structures show that the retrofitted connection with GFRP reinforcement achieved 1.17 to 1.25 times the capacity of the welded aluminum connection without any visible cracks. This result, and the minimal traffic disruption anticipated in the actual field application, makes this retrofit method a good candidate for implementation.     

铝对W9Mo3Cr4V高速钢组织和硬度的影响

用Ｘ－射线仪，扫描电镜和透射电镜系统研究了铝对钨钼系高速钢铸态，退火以及淬回火组织的影响，铝含量超过２．０％，淬火组织中出现含析出合金的铁素体组织和晶界屈氏体，导致钢硬的降低。     

过共晶Al－Si合金共生区激光表面处理

用２ｋＷ连续ＣＯ２激光对过共晶Ａｌ－１８Ｓｉ合金以不同能量密度和扫描速度进行快速熔凝处理。用扫描电镜、电子微区分析仪分析了微观结构。从计算机对Ａｌ－Ｓｉ合金ｆ－ｎｆ系统的非平衡理论计算所得的共生区及实验结果的分析可见，当能量密度和扫描速度决定的凝固条件处于共生区中部时，过共晶Ａｌ－Ｓｉ合金激光表面处理可以得到共晶间距低于２００ｎｍ的完全共晶结构。     

过共晶铝硅合金细化初晶硅的研究

研究了ZL8604过共晶铝硅合金初晶硅细化剂和加入方式与加入量以及影响细化效果的冶铸工艺因素,实验结果达到了技术指标要求。     

Electrochemical Investigation on the Formation of Dy-Fe Alloy in Molten Chlorides

ＥｌｅｃｔｒｏｃｈｅｍｉｃａｌＩｎｖｅｓｔｉｇａｔｉｏｎｏｎｔｈｅＦｏｒｍａｔｉｏｎｏｆＤｙＦｅＡｌｏｙｉｎＭｏｌｔｅｎＣｈｌｏｒｉｄｅｓＬｉｕＧｕａｎｋｕｎ（刘冠昆），ＴｏｎｇＹｅｘｉａｎｇ（童叶翔），ＨｏｎｇＨｕｉｃｈａｎ（洪惠婵），Ｙａｎｇ...     

塑料合金用反应型相容剂

反应型相容剂含有反应基团,可与含相应基团的聚合物起化学反应,因而在混炼过程中增容。本文系统地介绍各种反应型相容剂的设计、合成、品种和应用。     

碳纤维表面处理对铝电解用硼化钛阴极涂层性能的影响

硼化钛阴极涂层是铝电解用可润湿性阴极材料中的一种，具有优良的抗钠渗透性和对铝液润湿性，可以有效地延长铝电解槽寿命。碳纤维是硼化钛涂层材料的增强剂之一．对硼化钛阴极涂层的性能影响很大。本文研究了不同工艺的液相碳纤维表面氧化处理法对硼化钛阴极涂层抗拉强度和粘接强度的影响。采用PTIR检测碳纤维处理后表面含氧基团的变化，寻找影响硼化钛阴极涂层性能的原因，从而达到最有效地提高TiB2阴极涂层抗拉强度和粘接强度的目的。结果表明，采用工艺(1)(10％HNO3，80℃、恒温5min．超声波、5min)对碳纤维进行表面处理最合理，处理后碳纤维表面含氧基团的含量最高．用其制备硼化钛阴极涂层的抗拉强度、粘接强度最大。     

GH871 合金的蠕变断裂机制

对采用AIM+ESR和VIM+ESR工艺冶炼的GH871合金在650 ℃的蠕变性能及特征的研究表明,与用AIM+ESR工艺冶炼的GH871合金相比,用VIM+ESR工艺冶炼的GH871合金在蠕变断裂过程中裂纹萌生的形式(包括裂纹形状及形成时间)和裂纹扩展至裂纹连接所需的时间均表现出明显韧化的特征.