Wear and Creep Characteristics of a Carbon‐Derived Si3N4/SiC Micro/Nanocomposite

In the presented work some properties of a recently developed Si₃N₄/SiC micro/nanocomposite have been investigated. The material was tested using a pin on disc configuration. Under unlubricated sliding conditions using Si₃N₄ pin at 50 % humidity, the friction coefficient was in the range of 0,6 ‐ 0,7. The reduction of humidity resulted in a lower coefficient of friction, in vacuum the coefficient of friction had a value of about 0,6. The wear resistance in vacuum was significantly lower then that in air. The wear patterns on the Si₃N₄+SiC disc revealed that mechanical fracture was the wear controlling mechanism. Creep tests were realized in four point bending configuration in the temperature interval 1200‐1400 °C at stresses 50,100 and 150 MPa and the minimal creep deformation rate was established for each stress level. The activation energy, established from the minimal creep deformation had a value of about 360 kJ/mol and the stress exponent values were in the range of 0.8‐1.28. From the achieved stress exponents it can be assumed that under the studied load/temperature conditions the diffusion creep was the most probable creep controlling mechanism.     

哈得4联合站技术改造

位于塔克拉玛干大沙漠腹地的哈得4油田,2004年成为全国最大的沙漠油田,2005年产量达到200×104t。在对联合站存在问题逐一分析的基础上,提出了技术改造的措施。现场采集的运行数据表明技术改造效果明显,增强了流程可靠性,提高了自动化水平,降低了能耗。     

Fe3O4/PSt/TiO2多层包覆电磁响应微球的制备

首先采用分散聚合法将自制的Fe3O4磁流体和苯乙烯反应合成有磁核的Fe3O4/PSt磁性聚合物微球，然后，用非均匀成核水解反应在Fe3O4/PSt微球外包覆无定形二氧化钛，获得Fe3O4/PSt/TiO2复合微粒。用红外光谱、扫描电镜和热分析对粒子的形貌和结构进行了表征。并测试了微粒的介电性能和磁性，结果表明，所制得复合微粒有良好的电、磁响应性。     

Processing and microstructure of non-oxide ceramic fibres

Research and development efforts on high-temperature, oxidation-resistant fibres have increased over the past decade due to the demand for light-weight, stiff and strong composite materials in aerospace applications. Varieties of ‘high-performance’, continuous, non-oxide fibres with low-density, high tensile strength and tensile modulus have been developed either from organic precursors or via chemical vapour deposition for fabrication of ceramic matrix composites. Fibres derived from polymer precursors (e.g. Nicalon, Tyranno, HPZ) are small in diameter (compared to CVD monofilaments) and are ideally suited for ceramic composites. Processing, microstructural stability and mechanical properties of these newly developed SiC and Si₃N₄ base fibres are briefly reviewed in this paper.     

超细Fe3O4粒子表面包覆酞菁钴性质研究

本文研究了合成载氧体的金属有机化学液相淀积法制造工艺，所得产物经ＴＥＭ、ＸＰＳ、Ｍｏｓｓ－ｂａｕｅｒ谱和Ｂ－Ｈ仪等手段，研究了它的结构和磁性能。实验表明，酞青钴以薄层形式包覆在Ｆｅ＿３Ｏ＿４的表面，封闭了Ｆｅ＿３Ｏ＿４的表面孔洞，稳定了Ｆｅ＿３Ｏ＿４的物相，增强了磁性能。     

硫化铜矿中提取铜的新方法研究

对从硫化铜矿中提取铜的溶剂进行了详细研究，提出了“过硫酸铵－氨水－Ａｇ￣＋”催化、氧化、络合的提取法。     

纳米级BaAl_2O_4微粉的制备和性质

分别用溶胶 -凝胶法、低温固相反应法 ,制得了纳米级BaAl2 O4微粉 ,用电镜观察了其形貌和粒径的大小 ,用X-射线衍射仪进行了物相分析 ,测定了其纯度与晶型 ,讨论了制备方法与粒度大小的相互影响     

Unperturbed dimension of poly(4-acetoxystyrene) measured in good and theta solvents

In order to obtain the additional data concerning the unperturbed dimension of poly-4-substituted styrene, light scattering measurements are performed on the twenty-two fractions with molecular weight of (0.91–352)·10⁴ of poly(4-acetoxystyrene) in dioxan at 25°C, from which the molecular weight obtained was found easily to be evaluated with the gel permeation chromatography using THF. Phase separation experiments for this polymer indicate that the theta state is attained in isopropyl acetate at 19.7°C and butyl acetate at 26.8°C. By making viscosity measurements at that state, the value of K_Θ is directly evaluated as 5.4·10^?4 dl g^?1. The limiting viscosity number is also obtained in good solvents, THF and dioxan, at 25°C and constants of the Mark-Houwink-Sakurada equation in each solvent are determined. Further, approximately the same K_Θ as above is obtained from these data with the Stockmayer-Fixman plot. The calculated value of steric factor, 2.37, on this polymer may be plausible, compared with those of polyvinylaromatic derivatives.     

Comparison of inward and outward grown Pt modified aluminide diffusion coatings on a Ni based single crystal superalloy

Two commercial Pt modified aluminide coatings (RT22 and MDC150L) on the same single crystal Ni-based superalloy (CMSX-4) were studied by: scanning electron microscopy; transmission electron microscopy; energy dispersive X-ray spectrometry; and gravimetry. The RT22 coating is an inward grown coating (high activity), while MDC150L is produced by outward growth (low activity). Samples were oxidised in still laboratory air at 1050 °C for various times up to 2000 h. It was found that the outward grown coating produced a slower growing oxide that was more spallation resistant. Several possible reasons for this were identified including: coating purity; coating surface topography; and ductile to brittle transition temperature. The microstructural differences between the two coatings in the as-coated condition were investigated and the development of their microstructure during heat treatment was described. A model for coating growth during heat treatment was proposed.     

激光晶体Nd:YVO4的形貌及生长缺陷

本文报道了应用环境扫描电镜（ESEM）和同步辐射X射线白光形貌术对采用提拉法生长出的Nd:YVO4晶体进行的形貌及生长缺陷的分析,获得了该晶体的开裂表面的ESEM形貌像以及取自晶体肩部和中间部位的（001）面的同步辐射白光形貌像,观察到了位错、包裹物等缺陷,可为生长高质量的Nd:YVO4晶体提供重要的启示.