(K0.45Na0.55)0.98Li0.02Nb0.77Ta0.18Sb0.05O3-Co0.85Cu0.15Fe2O4复合陶瓷的磁电性能研究

以压电体(K0.45Na0.55)0.98Li0.02Nb0.77Ta0.18Sb0.05O3和压磁体Co0.85Cu0.15Fe2O4为原料,通过传统的固相反应法制备了(1-x)[(K0.45Na0.55)0.98Li0.02Nb0.77Ta0.18Sb0.05O3]-xCo0.85Cu0.15Fe2O4多铁性复合陶瓷,并使用X射线衍射仪、扫描电子显微镜、压电测试仪、铁电测试仪和磁电耦合测试仪对物相、显微结构、压电、铁电、磁电耦合性能进行了分析。结果表明,复合陶瓷的相结构保持为(K0.45Na0.55)0.98Li0.02Nb0.77Ta0.18Sb0.05O3和Co0.85Cu0.15Fe2O4两种物相,但两者之间发生了轻微的化学反应。随着Co0.85Cu0.15Fe2O4压磁相含量的增加,复合陶瓷的压电系数从56pC/N减小到21pC/N,剩余极化强度略有降低。在压磁相含量为0.2时可获得4.3mV·cm-1·Oe-1的最佳磁电耦合系数。     

柠檬酸根对纳米Fe_3O_4/PVA磁性复合膜性能的影响

采用化学共沉淀法制备了添加柠檬酸根前后的纳米Fe_3O_4粉体材料,用流延成膜法制备了添加柠檬酸根前后的Fe_3O_4/聚乙烯醇(PVA)复合膜。用红外光谱分析仪、古埃磁天平法、振动样品磁强计、自制磁致变形设备、发射扫描电子显微镜对添加柠檬酸根前后的纳米Fe_3O_4/PVA复合膜的结构及性能进行了表征和分析。结果表明:添加柠檬酸根纳米Fe_3O_4制备的Fe_3O_4/PVA复合膜磁化率更大、磁性能更好、磁致变形性能更大、分散性好。     

Fe_3O_4@MgO纳米复合材料的制备及其对Pb~(2+)的吸附性能

采用两步化学沉淀法制备了Fe_3O_4@MgO纳米复合材料,研究了纳米复合材料对Pb~(2+)的吸附性能。结果表明,所制备的复合材料具有较高的顺磁性和稳定性,其饱和磁化强度为58.07 emu/g,初始氧化增重温度为125℃,对Pb~(2+)有较好的吸附能力,在50 min内可以达到吸附平衡,最大吸附量为711.5 mg/g,其吸附过程符合准二级动力学模型和Langmuir等温吸附模型。     

Personalized Cancer Immunotherapy via Transporting Endogenous Tumor Antigens to Lymph Nodes Mediated by Nano Fe3O4

While immunotherapy has a tremendous clinical potential to combat cancer, immune responses generated by conventional cancer immunotherapy remain not enough to completely eliminate tumors, mainly due to the tumor's immunosuppressive microenvironment and heterogeneity of tumor immunogenicity. To improve antitumor immune responses and realize personalized immunotherapy, in this report, endogenous tumor antigens (ETAs) that dynamically present on tumor cells are transported to lymph nodes (LNs). Based on the hypothesis that nano Fe₃O₄ (≈10 nm) could serve as the nanocarrier for transporting ETAs from the tumor to LNs, we wondrously find that Fe₃O₄ has a tremendous potential to improve cancer immunotherapy, because of its excellent protein‐captured efficiency and LNs‐targeted ability. To ensure the optimal ETAs‐bound efficiency of Fe₃O₄, a core–shell formulation (denoted as Ce6/Fe₃O₄‐L) is developed and specific release of Fe₃O₄ in tumor is enabled. These findings provide a simple and general strategy for boosting cytotoxic T‐cell response and realizing personalized cancer immunotherapy simultaneously.     

Polypyrrole functionalized with FePcTSA for NO2 sensor application

The nitrogen dioxide (NO₂) sensing capability of polypyrrole (PPy) was enhanced dramatically after functionalized with iron(III)phthalocyanine-4,4′,4″,4-tetrasulfonic acid monosodium salt (FePcTSA). The incorporated phthalocyanine was confirmed by different characterization techniques such as UV–vis spectroscopy, FTIR, GFAAS, EDAX, etc. The resistance of the functionalized PPy decreased spontaneously during exposure to NO₂ gas at room temperature. This material exhibited excellent stability, reversibility, and reproducibility. The lowest response time (t₅₀) thus obtained is 47 s with a highest response factor (ΔR/R₀ × 100) of 50.25.     

NdFeB废料中钴的回收研究

在NdFeB废料经硫酸溶解回收稀土后的高铁、低钴硫酸溶液中，采用添加铁屑、硫化钠、硫磺的硫化沉淀法回收钴，取得了较好的效果，钴的沉淀率大于99％，且沉淀物中钴含量可达8％（质量分数）。该法的最佳工艺条件是：Fe：Co=1．5，Na2S：Co=2，S：Co=0．5，t=70℃、pH=2，反应及沉淀时间为1h。     

由中间相沥青制备泡沫炭:Fe(NO3)3的影响

以中间相沥青为前驱体制备高性能泡沫炭，在考察中间相沥青、Fe（NO3）3及其混合物热分解行为的基础上，着重研究了Fe（NO3）3对制备中间相沥青基泡沫炭的影响，揭示了Fe（NO3）3对泡沫炭孔泡结构的影响规律及其作用机制，初步研究了在泡沫炭炭化过程中形成的Fe／C之物相结构及其石墨化行为。结果表明，在不同的炭化温度下，Fe在泡沫炭中的存在形态各异；Fe物种的存在有利于提高泡沫炭的石墨化程度。     

添加Fe3+对二氧化钛薄膜吸收光谱及光催化活性的影响

用阳极氧化法制备多孔状的纳米晶二氧化钛薄膜,通过往阳极氧化的电解液中添加Fe3 ,使其进入二氧化钛薄膜中,研究了掺杂Fe3 对二氧化钛薄膜吸收光谱和光催化活性的影响.在阳性氧化时通过往电解液中添加不同含量的Fe3 可以制得掺杂Fe3 浓度不同的薄膜,研究了掺杂Fe3 浓度不同对薄膜吸收光谱和光催化活性的影响.用X射线衍射、扫描电子显微镜、紫外-可见吸收光谱仪和X光电子能谱对薄膜进行了表征.实验发现掺杂Fe3 使二氧化钛薄膜对入射光的吸收带边发生红移,讨论了其作用机制.