Shear strength and aging characteristics of 63Sn−37Pb solder bumps with various solder ball and pad sizes

The shear strength and aging characteristics of 63Sn–37Pb solder bumps were characterized with variation in solder ball and UBM pad sizes. The shear strength increased with shorter effective crack size,a _effs which was determined with the solder ball and pad sizes. The shear strength of the solder bumps on Au/Ni/Cu and Ni/Cu did not change significantly with reflow time. Substantial decrease in the shear strength occurred for the solder bumps formed on Au/Ni/Cu with aging treatment, and the shear strength after aging was also related to the bump shape which was determined with the solder ball and pad sizes.     

Effect of ultrasonic power and bonding force on the bonding strength of copper ball bonds

Copper wire, serving as a cost-saving alternative to gold wire, has been used in many high-end thermosonic ball bonding applications. In this paper, the bond shear force, bond shear strength, and the ball bond diameter are adopted to evaluate the bonding quality. It is concluded that the ef/~cient ultrasonic power is needed to soften the ball to form the copper bonds with high bonding strength. However, excessive ultrasonic power would serve as a fatigue loading to weaken the bonding. Excessive or less bonding force would cause cratering in the silicon.     

剪切变形方向特征对高纯铝箔轧制织构的影响

运用取向分布函数(ODF)研究了每个轧制道次的剪切变形特征对高纯铝箔轧制织构的影响.提出用中性角的相对大小来量化轧制剪切变形作用方向改变的位置,运用Taylor晶体塑性变形理论模拟计算了中性角的相对大小对轧制织构演变的影响.实测与模拟的轧制织构特征表明:中性角靠近轧制变形区的中心位置有利于形成{001}<110>剪切织构,从而证实了除剪切变形的程度外,剪切变形方向改变的位置也是影响高纯铝箔轧制织构的重要因素.     

高层住宅结构设计

主要介绍长沙梦泽园高层住宅从基础到上部楼层各部位的结构设计,以及在设计、施工过程中所考虑的一些问题及处理方法。     

Adhesion Mechanisms of Polyurethanes to Glass Surfaces I. Structure-Property Relationships in Polyurethanes and Their Effects on Adhesion to Glass

Polyurethanes were prepared from toluene diisocyanate (TDI), 1-4-butane diol (BDO) and polycaprolactone-based triols with varying molecular weights. Among each molecular weight triol-based urethane, hard segment content was varied from 20% to 70%. Differential scanning calorimetry, tensile testing, and Iosipescu shear testing were done on all the various urethanes prepared. Thermal characterization data revealed the dependence of phase separation on hard segment content as well as on the triol molecular weight. Tensile data and Iosipescu shear data further confirmed the observations made from the DSC data. The data further indicated that phase separation can greatly improve the modulus of cross-linked segmented urethanes. Adhesion of these urethanes to glass surface was evaluated using soda-lime float glass plate. Urethane samples were cast on the air side of the glass plates and adhesion was measured in shear mode. Adhesion data indicated that in addition to hard segment content, modulus, cross-link density, and molecular weight of the triols, phase separation seems to be a major factor in controlling adhesion. Surfaces of the failed adhesion samples were also analyzed and the failure mode was found to be cohesive, in varying degree, with the different urethane systems.     

一种耐超高温、耐酸聚合物的制备及性能测试

摘要：为解决常规聚合物无法满足超高温深井酸化压裂的技术要求，本文分别以丙烯酰胺（AM） 甲基丙烯酰氧乙基三甲基氯化铵（DMC）、AM DMC SMA（十八烷基甲基丙烯酸酯）为原料，通过自由基聚合制备出两种耐酸聚合物SY-1和SY-2，并对其结构进行表征及性能测试。结果表明：SY-2红外谱图中720 cm-1为—(CH2)n—的弯曲振动吸收峰，单体成功接枝到聚丙烯酰胺分子链上；热重分析表明，SY-1升温至600℃失重比为98%，SY-2失重比86%，热稳定性得到改善；质量分数为20%盐酸中，SY-2质量分数0.8%：180℃，170s-1流变性能测试，SY-2剪切终点黏度56mPa?s，90℃、120℃、150℃剪切1h，黏度为83.6mPa?s、43.5mPa?s、27.8mPa?s，剪切稳定性分别为85.66%、74.45%、52.01%； 180℃、3MPa条件下，静态酸岩反应速率为8.94?10-5(g/cm2?s)，较常规SY-1反应速率1.69?10-4(g/cm2?s)减小一个量级。且与缓蚀剂、铁离子稳定剂配伍性良好，克服高温酸化压裂技术的应用瓶颈。     

Preadhesion Laser Treatment of Aluminum Surfaces

An excimer laser may be used for preadhesion treatment of aluminum alloys. This method presents an alternative to the use of ecologically unfriendly chemicals involved in conventional anodizing pretreatments.

Experimental results indicate that preadhesion laser surface treatment significantly improved the shear strength of modified-epoxy bonded aluminum specimens compared with untreated and anodized substrates. The best results were obtained with laser energy of about 0.2 J/Pulse/cm² where single lap shear strength was improved by 600-700% compared with that of untreated Al alloy, and by 40% compared with chromic acid anodizing pretreatment.

The mode of failure changed from adhesive to cohesive as the number of laser pulses increased during treatment. The latter phenomenon has been correlated with morphology changes as revealed by electron microscopy, and chemical modification as indicated by Auger and infrared spectroscopy.

It can be concluded that the excimer laser has potential as a precise, clean and simple preadhesion treatment of Al alloys.     

POWER CONSUMPTION WITH ANCHOR MIXERS EFFECT OF BOTTOM CLEARANCE

The effect of bottom clearance on power draw for anchors is investigated. The results suggest that power input decreases as the bottom clearance ratio b/D increases. A new correlation is proposed in which both bottom and wall clearance effects on power input are considered. The dependence of power input on these effects is additive rather than multiplicative. Thus, the total power consumption is the sum of the power inputs generated by the wall and bottom clearance. Power results from 3D-CFD numerical simulations are also presented. These results confirm fairly well the experimental points.     

环氧-聚酰胺体系中增韧剂的研究

在环氧-聚酰胺体系中分别加入“海岛结构”QS-1、聚硫橡胶、液体丁腈橡胶增韧改性,通过对固化物剪切强度、弯曲弹性模量及断裂强度的对比,“海岛结构”QS-1增韧综合性能较好.     

金属闪光外墙乳胶漆的研制及性能研究

以丙烯酸酯及有机硅单体为原料合成了核-壳型硅丙乳液,用自制分散剂将闪光铝粉分散成水性闪光铝粉浆,并成功分散于硅丙乳液中,加入进口助剂,配制成水性金属闪光外墙乳胶漆.讨论了基料的玻璃化温度、单体的加入方式、引发剂、乳化剂、反应温度、聚合工艺和pH等对乳胶漆性能的影响.