Relating catalyst structure and composition to the water–gas shift activity of Cu–Zn-based mixed-oxide catalysts

In order to investigate the effect of cerium oxide on Cu–Zn-based mixed-oxide catalysts four catalyst samples were characterized by means of XRD, in situ XANES and thermogravimetric analysis. The activity of the catalyst samples was tested for the forward water–gas shift reaction. Cerium oxide was found to increase the crystallinity of the ZnO phase indicating a segregation of the Cu and ZnO phases. The TOF of the water–gas shift reaction based on chemisorption data was found to be independent of composition and preparation conditions of the four catalyst samples. In contrast, the catalyst stability depends on composition and preparation conditions. Cerium oxide impregnated before calcination of the hydrotalcite-based Cu–Zn precursors leads to a more stable water–gas shift catalyst.     

锌电积的节电探讨

分析厂影响锌电积电能消耗的因素，提出了锌电积的节电对策与展望。     

锌精矿制粒沸腾焙烧新工艺的应用与改进

介绍了锌精矿制粒沸腾焙烧新工艺的工业化生产应用与技术改进情况 ,阐述了取得的成果及存在的问题     

Ionothermal synthesis of a three-dimensional zinc phosphate with DFT topology using unstable deep-eutectic solvent as template-delivery agent

A three-dimensional zinc phosphate compound with DFT topology, designated as ZnPO₄-EU1, has been synthesized by an ionothermal approach from the system HF-ZnO–P₂O₅-choline chloride-imidazolidone. Ethylenediamine, derived from decomposition of the imidazolidone component of the deep-eutectic solvent (DES) itself, is delivered to the synthesis and serves as an appropriate template for ZnPO₄-EU1. Experiments in which the synthesis conditions were varied showed that ZnPO₄-EU1 may be prepared over a wide molar ratio of P/Zn = 0.55–13.0. Powder X-ray diffraction patterns have been obtained at intervals to track the crystallization process of this material. The experimental data show that Zn₃(PO₄)₂ · 4H₂O (a dense phase) was first isolated from the DES after reaction for 1 h. Subsequently, the pure phase of ZnPO₄-EU1 was obtained with increasing crystallization time from 12 h to 72 h. The experimental results show that the nucleation and crystallization take place with relatively low levels of solvent degradation, demonstrating that zinc phosphate with a three-dimensional framework can be synthesized by in situ generation of an appropriate template using an unstable DES at high temperatures (150–200 °C).     

介孔氧化铁对正辛醇乙氧基化反应的催化性能

以十二烷基磺酸钠为模板剂、乙二胺为碱性介质,将水热法合成的氧化铁/十二烷基磺酸钠复合中孔材料在550℃、空气气氛中煅烧10h,除去模板剂,得到介孔氧化铁。通过X射线衍射、氮气吸附-脱附方法对介孔氧化铁的晶体结构和表面物性进行表征。表征结果显示,煅烧后的介孔氧化铁具有典型的六方介孔的结构特征,平均孔径为5.4nm。将介孔氧化铁用于催化正辛醇乙氧基化反应,研究结果表明,升高反应温度和初始压力、增加催化剂用量,可加快环氧乙烷的反应速率,同时产物的相对分子质量分布较窄。当平均聚合度为6.5时,正辛醇聚氧乙烯醚相对分子质量分布的选择性系数达到21.1。     

Formation and electronic structure of interface

In the present work the formation of the interface between polycrystalline silver and thin films of titanium oxide was studied with photoelectron spectroscopy (XPS, UPS) and time-of-flight secondary ion mass spectrometry (TOF-SIMS). Titanium oxide was deposited stepwise on 100 nm thick silver films by reactive magnetron sputtering allowing to study the evolution of the interface formation process. The process involves two steps: formation of thin layer of silver oxide and subsequent growth of the TiO₂ film. For better understanding of the silver oxidation process, pure silver films were exposed to a low temperature Ar/O plasma for different time intervals providing a possibility to investigate early stages of the oxide film growth.     

Preparation and Properties of Rare Earth Modified Carbon Black/Natural Rubber Composites

The oxides Eu, Ho, Er and Dy were used to prepare the hydroxides of rare earth modified carbon black. Then natural rubber latex （NRL） was added into the reactor. The system reacted at 85 ℃ with stirring for 1 h to prepare powdered HAF-Ln（OH）3/NR composites. The effects of the kind and content of Ln on the particle size distribution of P [ NR/HAF-Ln （OH）3 ] and mechanical properties of its vulcanizate were studied respectively. It is found that rare earth can help to get the powder of the composite, the product particle with a diameter less than 0.9mm will be get when the composites containing the compound of Ho, Er and Dy with dosage of 1.0, 1.0, O. 5 percent, respectively. The adding of Ln can improve the tensile strength and tear strength of the vulcanizate effectively, what＇s more, Er and Dy can decrease the permanent set of vulcanizate significantly. The SEM studies shows that P[ NR/HAF-Dy （OH）3 ] vulcanizate shows superior mechanical properties that depend primarily on the absence of free carbon black, the fine dispersion of carbon black in the rubber matrix and better polymer-filler interaction.     

降低气体悬浮焙烧炉焙烧过程中Al_2O_3粒度破损的措施

为了降低气体悬浮焙烧炉焙烧过程中Al_2O_3粒度的破损,对气体悬浮焙烧炉焙烧过程中氧化铝粒度的影响因素进行了分析,提出了降低粒度破损的一些措施。     

Study on Oxygen Isotope Fractionation in RE Oxide Minerals

ＳｔｕｄｙｏｎＯｘｙｇｅｎＩｓｏｔｏｐｅＦｒａｃｔｉｏｎａｔｉｏｎｉｎＲＥＯｘｉｄｅＭｉｎｅｒａｌｓＦａｎｇＴａｏ（方涛），ＱｉｕＹｕｚｈｕｏ（裘愉卓）（ＩｎｓｔｉｔｕｔｅｏｆＧｅｏｃｈｅｍｉｓｔｒｙ，ＡｃａｄｅｍｉａＳｉｎｉｃａ，Ｇｕｉｙａｎｇ５...