Phosphorus‐containing polyaryloxydiphenylsilanes with high flame retardance arising from a phosphorus–silicon synergistic effect

Polyaryloxydiphenylsilanes were prepared from phosphorus‐containing diols and diphenydichlorolsilane through solution polymerization. With a stoichiometric imbalance in feed monomers, the resulting polymers exhibited moderate melting points and good processing properties. The polymers prepared showed initial decomposition temperatures above 340 °C, excellent thermal stability, high char yields at 850 °C and very high limited oxygen index values of 56–59. The polymers' char yields and their (P + Si) contents showed linear relationships. © 2003 Society of Chemical Industry     

Wear and Creep Characteristics of a Carbon‐Derived Si3N4/SiC Micro/Nanocomposite

In the presented work some properties of a recently developed Si₃N₄/SiC micro/nanocomposite have been investigated. The material was tested using a pin on disc configuration. Under unlubricated sliding conditions using Si₃N₄ pin at 50 % humidity, the friction coefficient was in the range of 0,6 ‐ 0,7. The reduction of humidity resulted in a lower coefficient of friction, in vacuum the coefficient of friction had a value of about 0,6. The wear resistance in vacuum was significantly lower then that in air. The wear patterns on the Si₃N₄+SiC disc revealed that mechanical fracture was the wear controlling mechanism. Creep tests were realized in four point bending configuration in the temperature interval 1200‐1400 °C at stresses 50,100 and 150 MPa and the minimal creep deformation rate was established for each stress level. The activation energy, established from the minimal creep deformation had a value of about 360 kJ/mol and the stress exponent values were in the range of 0.8‐1.28. From the achieved stress exponents it can be assumed that under the studied load/temperature conditions the diffusion creep was the most probable creep controlling mechanism.     

Development of a Continuous Segmented Flow Tubular Reactor and the “Scale‐out” Concept – In Search of Perfect Powders

The synthesis of powders with controlled shape and narrow particle size distributions is still a major challenge for many industries. A continuous Segmented Flow Tubular Reactor (SFTR) has been developed to overcome homogeneity and scale‐up problems encountered when using batch reactors. Supersaturation is created by mixing the co‐reactants in a micromixer inducing precipitation; the suspension is then segmented into identical micro‐volumes by a non‐miscible fluid and sent through a tube. These micro‐volumes are more homogeneous when compared to large batch reactors leading to narrower size distributions, better particle morphology, polymorph selectivity and stoichiometry. All these features have been demonstrated on single tube SFTR for different chemical systems. To increase productivity for commercial application the SFTR is being “scaled‐out” by multiplying the number of tubes running in parallel instead of scaling‐up by increasing their size. The versatility of the multi‐tube unit will allow changes in type of precipitate with a minimum of new investment as new chemistry can be researched, developed and optimised in a single tube SFTR and then transferred to the multi‐tube unit for powder production.     

Numerical Study of Finite Element Method Based Solutions for Propagation of Wetting Fronts in Unsaturated Soil

The accurate prediction of the propagation of a wetting front in an unsaturated soil subjected to surficial infiltration is of practical importance to many geotechnical and geoenvironmental problems. The finite element method is the most common solution technique as the hydraulic soil properties are highly nonlinear. Two important issues are often found to create difficulties in such analyses. First, numerical oscillations are usually observed in the calculated pore pressures at the wetting front. Second, when a reasonable mesh size and time step are used, the elevation of the wetting front may be seriously overpredicted. This paper is focused on the second issue. The under-relaxation (UR) technique used in the iterative process within each time step is found to have a serious impact on rate of convergence with refinement in mesh size and time step. Two different techniques are typically used; the first evaluates the hydraulic conductivity using an average of heads calculated from the preceding time node and the most recent iteration of the current time node (UR1), and the second evaluates the hydraulic conductivity using the average of heads calculated from the two most recent iterations of the current time nodes (UR2). The study shows that UR1, which is adopted in programs such as SEEP/W, ensures that the solution converges rapidly to a stable solution within a time step, but may converge to the wrong wetting front at a given elapsed time unless a sufficiently refined mesh is used. UR2 converges much more slowly within a time step, but the error in the wetting front is smaller than that generated by UR1.     

Synthesis of heterocyclic metal complexes and their evaluation as marine antifoulants

4-Amino-3-thio-1,24-triazolidine (L₁) and 4-amino-5-thio-1,3,4-thiadiazole (L_II) as well as their metal complexes of the general formulae ML_I·2H₂O and ML_IICl (M; Pb(II), Cd(II) and Zn(II)) were prepared. With Sn(II), we obtained Sn(L_I)₂·2H₂O and SnL_IICl, respectively. The structures of the compounds were identified through elemental analysis, and IR and UV spectra measurements, in addition to thermal analysis in case of the metal complexes. The antifouling properties of the compounds were tested by their incorporation into paint formulations which were applied to PVC substrates and tested in water from Alexandria western harbour. When the compounds were added at 17·5% by volume, the coated panels were fouled after 3 months of immersion. The addition of 6·7% by volume of tributyltin oxide to 15·8% of the prepared compounds in one formulation elevated the paint efficiency and prevented fouling for 11 months. Paint containing solely tributyltin oxide at the same concentration was inactive against algae.     

Polymer networks based on α,ω-methacrylate-terminated poly(1,3-dioxolane)

α,ω-Methacrylate-terminated poly(1,3-dioxolane)s (polyDXL) were synthesized by cationic ring-opening polymerization of DXL in the presence of methylene-bis(oxyethylmethacrylate) as transfer agent. If the initiator concentration is small compared with the transfer agent concentration, the molecular weights of the polymers are governed by the ratio of the reacted monomer to the reacted transfer agent. The α,ω-methacrylate-terminated polyDXLs obtained undergo free radical polymerization with formation of polyacetal networks. The properties of the networks as function of the molecular weight of the corresponding prepolymers are reported.     

Effects of hydrolysis on the physical properties of short glass-fibre reinforced poly(ethylene terephthalate)

The mechanical fracture strength and toughness of short-fibre composites, injection moulded from compounds of poly(ethylene terephthalate) (PET) containing 10 and 30% (by weight) (w/o) glass, have been investigated and the dependence upon matrix hydrolytic stability determined. Mouldings have been characterised by several physical techniques to evaluate molecular weight, degradation rates, crystallinity and morphology, whilst time-dependent gravimetric data were derived to quantify sorption kinetics and allow comparisons with theoretical reaction rates to be made. During melt processing, PET is hydrolysed extremely rapidly by traces of moisture (<0.02w/o). yet the inherent strength of moulded composites declines significantly only below an apparently critical molecular weight. However, on long-term humid ageing in hot water, impact behaviour especially is rendered more complex by simultaneous crystallisation, molecular reorder and losses of interfacial bond strength.     

Modeling and assimilation of root zone soil moisture using remote sensing observations in Walnut Gulch Watershed during SMEX04

Soil moisture status in the root zone is an important component of the water cycle at all spatial scales (e.g., point, field, catchment, watershed, and region). In this study, the spatio-temporal evolution of root zone soil moisture of the Walnut Gulch Experimental Watershed (WGEW) in Arizona was investigated during the Soil Moisture Experiment 2004 (SMEX04). Root zone soil moisture was estimated via assimilation of aircraft-based remotely sensed surface soil moisture into a distributed Soil-Water-Atmosphere-Plant (SWAP) model. An ensemble square root filter (EnSRF) based on a Kalman filtering scheme was used for assimilating the aircraft-based soil moisture observations at a spatial resolution of 800 m × 800 m. The SWAP model inputs were derived from the SSURGO soil database, LAI (Leaf Area Index) data from SMEX04 database, and data from meteorological stations/rain gauges at the WGEW. Model predictions are presented in terms of temporal evolution of soil moisture probability density function at various depths across the WGEW. The assimilation of the remotely sensed surface soil moisture observations had limited influence on the profile soil moisture. More specifically, root zone soil moisture depended mostly on the soil type. Modeled soil moisture profile estimates were compared to field measurements made periodically during the experiment at the ground based soil moisture stations in the watershed. Comparisons showed that the ground-based soil moisture observations at various depths were within ± 1 standard deviation of the modeled profile soil moisture. Density plots of root zone soil moisture at various depths in the WGEW exhibited multi-modal variations due to the uneven distribution of precipitation and the heterogeneity of soil types and soil layers across the watershed.