Cucurbitaceae family seeds are mostly discarded as agro-industrial wastes. Gurum (Citrullus lanatus var. colocynthoide) is an underutilized wild cucurbit plant, closely related to desert watermelon, which is grown abundantly in some African countries. Gurum seeds can play a significant role in health and nutrition due to their high oil content. This review describes the nutritional composition of gurum seeds and their oil profile. Gurum seeds are a good source of oil (27–35.5%), fiber (26–31%), crude protein (15–18%), and carbohydrates (14–17%). Gurum seeds oil is extracted by supercritical CO₂ (SFE), screw press, and solvent extraction techniques. The gurum seeds oil is composed of unsaturated fatty acids with a high proportion of linoleic acid (C18:2) and oleic acid (C18:1). Gurum seeds oil contains various bioactive compounds, such as tocopherols, phytosterols, and polyphenols. It is reported that solvent extraction gives a higher yield than the screw press and SFE, but the SFE is preferred due to safety issues. More studies are required for producing better quality gurum seeds oil by using novel extraction techniques that can increase oil yield.     

NiFeAlO4载氧体制备及煤化学链燃烧反应特性

铁基载氧体是一种具有工业应用前景的载氧体,但存在氧利用率低、在高温下易烧结等问题。虽可通过制备双金属复合载氧体或添加惰性组分改进其性能,但均存在一定缺陷。若将活性组分和惰性材料融入到一个晶体结构制备尖晶石结构载氧体,则可实现利用双金属协同作用提高载氧体活性的同时,利用Al3+提高载氧体的稳定性。采用共沉淀法和溶胶凝胶法制备了具有尖晶石结构的NiFeAlO₄载氧体,考察了制备方法、载氧体与煤质量比对NiFeAlO₄载氧体化学链燃烧特性和循环稳定性的影响,并分析了载氧体对煤转化过程的作用。结果表明,溶胶凝胶法制备的NiFeAlO₄载氧体具有更好的反应性,载氧体与煤质量比为20∶1时,碳转化率为86.7%,远高于煤单独热解时的碳转化率(34%),此时CO₂体积分数为93.6%。对反应前后NiFeAlO₄载氧体晶相结构和形貌进行分析,表明循环过程中经“还原-氧化”后生成的NiO和载氧体颗粒团聚是导致载氧体活性下降的主要原因。相较于载热作用,NiFeAlO₄载氧体在煤化学链燃烧中主要起供氧作用,其不仅会促进挥发分向煤气的转化,且NiFeAlO₄载氧体与焦炭之间也存在固-固反应,利于更多CO₂的生成。     

砂岩翻砂废砂在水泥生料配料中的应用

我公司拥有2×2 500 t/d新型干法水泥生产线,在生产中逐步以废砂来替代砂岩进行生料配料,本文探讨了废砂的使用对水泥生产过程、熟料质量性能以及成本效益等方面的影响。结果表明：使用废砂替代砂岩进行水泥生料配料煅烧硅酸盐水泥熟料,未对熟料煅烧过程及熟料性能产生不良影响,烟气排放指标和熟料质量技术指标均符合国家标准要求。按我公司目前年产熟料110万t、掺加量按5.8%计算,年消耗废砂约10.0万t,每年节约成本约100万元,经济效益明显。     

铜冶炼企业产品质量控制的探索与实践

为了保持阴极铜化学成分和质量长期稳定,某铜冶炼企业对阴极铜化学成分进行监控,对铜冶炼生产系统中电解工序物料、产出后又重回本系统物料、贵金属系统中产出物料、外购原料中物料的杂质总量进行分析,提出了减少杂质对阴极铜质量影响的措施,为阴极铜质量的稳定创造了良好的生产条件,并提升了企业适应复杂原料市场的能力。     

CVD金刚石膜{100}取向在改进化学反应模型下生长的原子尺度模拟

建立了CVD金刚石膜{100}取向生长过程中的化学反应模型，表面吸附生长机制以沟槽处碳氢组元加入的机制为主，并用改进的KMC方法在原子尺度上模拟了该模型下（100）表面的生长过程，给出了衬底温度和甲基浓度等操作参数对膜质量的影响，结果表明，该化学反应模型能够较实际地揭示{100}取向CVD金刚石膜的生长。     

Magnetic and mechanical properties of FeSi alloys with high Si content

The chemical vapor（CVD） deposition-diffusion method was applied to prepare FeSi alloys with high silicon content up to 6.5%. In spite of various deposition and post-annealing, the sample remains α-Fe bcc structure. The cross section of the composition was analyzed to evaluate the Si content and distribution before and after annealing. The results show that the soft magnetic properties are improved by increasing the silicon content. For the samples containing about 6.5% Si, the coercivity decreases to 60 from 237.3 A/m of the original. It is also obtained that, in addition to the Si content, Si distribution has a large influence on the core loss due to the effect of resistivity. The micro-hardnesses were also evaluated along the cross-section after various annealings.     

TiNi形状记忆合金的线性回复行为及其稀土渗入改性

提出了TiNi形状记忆合金线性回复行为的新概念，采用稀土表面渗入化学热处理的方法，研究了对其线性回复性能的影响。实验结果表明：对TiNi形状记忆合金弹簧渗铈(Ce)或渗钐(Sm)，可以显著改善其线性回复性能。线性回复温度范围Tw从4℃拓宽到11℃，线性回复率η从54％提高到78％，线性回复程度PL从56％提高到70％，非线性回复程度Ps从44％减小至8％，但总回复程度PT有所下降。这些结果是由于TiNi合金弹簧渗层中金属问化合物的强化效果所致。     

WD615气缸体铸件材料性能的改善

WD615气缸体铸件曾发生化学成分不稳定、铸件本体组织粗大、铁素体含量偏高、硬度偏低等质量问题，为此，采取了如下措施：1）加强熔炼用材料的质量控制；2）提高冲天炉的熔炼质量；3）改进熔炼工艺（调整C,Si量，采用Cu-Cr-Sn合金化；降低浇注温度）；4）改进孕育工艺；5）采用炉前快速检测技术；6）加强铸件本体质量检测。结果表明，缸体铸件的化学成分、金相组织及力学性能均满足技术要求。     

SEBF/SLF系列重防腐涂料的特性和分析

本文介绍2种SEBF熔融结合环氧粉末涂料和2种SLF双组份液体涂料,辽宁的物理和化学性能及部分测试和评价方法.     

彩色不锈钢生产工艺及其耐蚀性的研究

采用添加了ＣＳ－１添加剂的常规的不锈钢着色液可以生产出彩色不锈钢。所获彩色膜除包括在常规的着色液中可获得的颜色外，还能着出茶色、咖啡色、古铜色等颜色。通过动电位扫描极化曲线等的测量和分析，研究了所得着色膜的耐蚀性能，并解释着色膜经硬化处理后，耐蚀性得到提高的原因。