Reduced basis approximation and a posteriori error estimation for stress intensity factors

We develop reduced basis approximations, rigorous a posteriori error bounds, and offline–online computational procedures for the accurate, fast, and reliable prediction of stress intensity factors or strain energy release rates for ‘Mode I’ linear elastic crack problems relevant to fracture mechanics. We demonstrate the efficiency and rigor of our numerical method in several examples. Copyright © 2007 John Wiley & Sons, Ltd.     

钇铝榴石晶体的超高温强度和流变性

在温度高达２０２３Ｋ，可控氧分和不同应变速率条件下，对钇铝榴石晶体进行了蠕变实验，研究表明，钇铝榴石晶体的脆－延性转变温度高达１８３３Ｋ，在温度低于２０２３Ｋ和应变速率大于１０＾－５．ｓ＾－１的条件下，其蠕变流动强度高于３０００ＭＰｑ对钇铝榴石晶体蠕变机制的研究表明，其高温塑性变形起因于晶体的位错滑移，晶体在高温下的高强度与其很高的Ｐｅｉｅｒｉｓ力相关，钇铝榴石晶体在高温晶体稳定性和超高强度使其菜     

Short-term creep and strength of fibrous polypropylene structures

The short-term creep and strength of fibrous polypropylene structures are investigated. On the basis of these characteristics, we develop the models of linear and nonlinear viscoelastic deformation of materials, specify the fields of their applicability, and study criteria used for the evaluation of the static strength and durability of these composites. __________ Translated from Problemy Prochnosti, No. 6, pp. 77–90, November–December, 2007.     

钢骨混凝土短柱在长期轴向荷载作用下的试验研究

钢骨混凝土柱结构在过去几十年间已得到广泛的运用。但是目前关于这种柱结构在长期荷载作用下由于徐变和收缩引起的与时间相关的力学性能研究还开展得很少。该文开展了钢骨混凝土短柱的长期轴向荷载试验研究,还进行了这些柱的极限承载力破坏试验。试验监测了由徐变和收缩引起的柱的轴向长期变形。基于该实测曲线的分析表明,采用ACI 209R-92的收缩模型和CEB-FIP90的徐变模型,利用龄期调整有效模量法可以较好地模拟钢骨混凝土柱在长期轴向荷载作用下的变形发展。经历了长期加载后的试验柱的极限承载力破坏试验还表明,长期轴向荷载对柱的轴压承载力没有显著影响。     

圆弧型柔性球铰柔度设计计算

 通过研究圆弧型柔性球铰的柔度性能,使该柔性球铰可代替传统的双轴柔性铰链应用于空间多自由度柔顺机构.根据《材料力学》中的卡氏第二定理,圆弧型柔性球铰柔度的解析公式被推导出,然后利用ANSYS12.0软件对其进行有限元分析, 结果表明有限元分析与解析式的计算结果基本一致.通过改变圆弧型柔性球铰的各结构参数来分析其性能,得出各结构参数对其柔度的影响大小依次为：最小截面直径 t、圆弧的圆心角θ^_m、圆弧半径R、杨氏模量E. 此设计计算和特性分析为柔性球铰在柔顺机构的应用提供了依据.     

高层框架考虑施工过程和徐变收缩影响的受力分析

位移法分析超静定结构徐变收缩效应的关键是求单元的徐变收缩固端力。首先根据力法和虚功原理,推导出杆件单元徐变固端力和收缩固端力的计算公式。然后给出了高层框架结构分析中考虑施工过程和徐变收缩影响的方法,并列出了位移法方程。用FORTRAN语言编制了高层结构徐变收缩分析的计算机程序,并对一个高层框架进行结构分析。结果表明,施工过程和徐变收缩对高层框架的受力和变形影响都较大,实际工程设计中应该考虑这些因素对结构的影响。     

升温速率对2219铝合金蠕变时效行为的影响

研究2219铝合金在蠕变时效成形过程中,升温速率对其蠕变行为及力学性能的影响规律。实验模拟构件在热压罐中的升温条件,降低材料的升温速率(0.75℃/min),延长其升温时间至4h(某典型构件真实蠕变时效升温时间),分别在0,150,210MPa 3种应力条件及不同的时效时间下进行蠕变实验,并对材料拉伸力学性能和微观组织(TEM)进行分析。结果表明:对比在材料尺度下0.5h的升温条件(5.5℃/min),升温速率的降低,在一定程度上提高了材料的力学性能,并且延长了材料强度达到峰值的时间;铝合金析出相的形状因子随着时效时间呈现先增长,到达峰值后下降的趋势;降低升温速率,材料在升温阶段即已发生了显著蠕变形变,在150MPa和210MPa应力条件下升温阶段的蠕变量分别占总蠕变量的29.28%和21.56%,且蠕变变形量和稳态蠕变速率会随着应力的升高而增加;由此,基于材料尺度(标准蠕变试样)的蠕变时效研究,用于表征构件尺度蠕变时效行为时,须进一步考虑升温速率对其成形及性能演变的影响。     

High temperature stability of 2.25Cr-1Mo steel during creep

The creep rapture behaviour of 2.25Cr—1Mo steel in air and in a salt mixture was studied. The salt coating, which can form a liquid phase at the test temperatures, increased the creep rate and reduced the rupture life of the material. The coating reduced the available cross-section of the material by removing the surface layers, thereby resulting in a reduction of the rupture life. Cross-sections of coated samples showed an outer oxide layer comprising oxide of the metal and precipitates of sulphide at the metal/oxide interface. This subsurface penetration of the corrodants was responsible for the early failure of the coated samples. This is typical of hot corrosion mechanisms. The formation of various carbides like M₂₃C₆ and M₆C, as observed by transmission electron microscopy, during creep reduced the creep strength of the material both in air and in the coated state. Increasing temperature enhanced the formation of these carbides with a consequent decrease in creep strength. Applied stress did not seem to play much of a role in the degree of carbide precipitation.     

Low-cycle fatigue properties of eutectic solders at high temperatures

This paper details the deformation mechanism and low‐cycle fatigue life of eutectic solder alloys at high temperature (around 0.8T_m). Grain boundary sliding generally nucleates a wedge‐type cavity that reduces the low‐cycle fatigue life of metals. In this study, grain boundary sliding has promoted intergranular failure contributing to the reduction in fatigue life of Sn–Ag–Cu alloy. However, grain boundary sliding has exerted no deleterious effects on fatigue resistance of eutectic Pb–Sn and Bi–Sn alloys. The phase boundary sliding with very fine microstructure induces exceptional ductility in these alloys leading to superior low‐cycle fatigue endurance for theses eutectic Pb–Sn and Bi–Sn alloys.     

镍基单晶高温合金的再结晶

镍基单晶高温合金作为先进发动机叶片的主要用材,其再结晶问题日益受到重视.本文综述了热处理温度、热处理时间、变形程度及合金成分等多种因素对镍基单晶高温合金再结晶的影响规律,分析了镍基单晶高温合金再结晶对其蠕变和疲劳性能的影响,并讨论了回复处理及浸蚀直接去除表面变形层、渗碳和表面涂层等控制再结晶的方法.最后,指出了镍基单晶...