采用厚为５０μｍ的Ｐｄ／Ａｇ（２３）合金膜进行了氢气渗透系数的测定和Ｈ＿２／Ｎ＿２混和气分离的研究，得出温度、压力、膜厚、进料气流量、膜的预处理和再活化及膜表面中毒等因素对氢气渗透的影响。分离Ｈ＿２／Ｎ＿２混和气可获得高纯氢气。     

A Thermo-Mechanical Study of Some Epoxy Adhesives Subjected to Combined Dynamic and Static Stresses

The object of the present study was to investigate the effect of superimposed dynamic and static stresses on mechanical and thermal properties of some epoxy adhesives. It was found that combinations of shear creep and torsional oscillations, applied simultaneously to adhesive joints at temperatures within the glassy range of the adhesive, led to strengthening of the joints in shear and to an increase in the glass transition temperature of the adhesive. Similar loading stresses applied at temperatures close to the T_g of the adhesive, led to opposite effects on the above mentioned properties of the joints. The width of the glassy-rubbery transition of the adhesives increased, in the whole range of temperatures used in this study and for all epoxy compositions, as a result of subjecting the joints to superimposed dynamic and static stresses. The broadening of the glass transition was interpreted as a result of the stiffening of polymer network during the combined stressing experiments. A linear relationship was found between the area of endothermal peaks in the first DSC scan of specimens subjected prior to test to superimposed dynamic and static stresses at temperatures below T_g, and the shear strength of the joints. In agreement with this observation and with literature data, a linear relationship was revealed also between the glass transition temperature of the resins (measured in the first DSC scan) and the shear strength of the joints. Based on experimental observations and on some literature information, it was suggested that the strengthening of the joint, as well as the changes in thermal properties of the adhesives, are mainly due to physical processes, such as short-range orientation of network chains and an increase in intermolecular interaction between highly polar sites of the network. The possibility that superimposed stressing led to changes in chemical crosslinking was discussed but it seems that no such reactions occurred.     

Efficiency of mineral admixtures in mortars: Quantification of the physical and chemical effects of fine admixtures in relation with compressive strength

This work is the fourth part of an overall project the aim of which was the development of general mix design rules for concrete containing different kinds of mineral admixtures. The two first parts presented the separation and quantification, by means of an empirical model based on semi-adiabatic calorimetry measurements, of the different physical effects responsible for changes in cement hydration (short terms) when chemically inert quartz powders were used in mortars. Part three dealt with an intensive experimental program, presenting and commenting more than 2000 compressive strength measurements. This program concerned 1 day to 6 months old mortars containing up to 75% of inert and pozzolanic admixtures. All these compressive strength results are analyzed in this fourth part and the influence of three effects, namely dilution, heterogeneous nucleation and the pozzolanic effect, are discriminated and quantitatively evaluated. An efficiency concept is proposed in order to take into account the effect of mineral admixture in mortars from both the physical and chemical points of view. It uses an efficiency function ξ(p) that has notable properties: it is independent of time, independent of fineness and independent of the type of mineral admixture.     

Synthesis and characterization of poly(urethane‐ester)s based on calcium salt of mono(hydroxybutyl)phthalate

Calcium‐containing poly(urethane‐ester)s (PUEs) were prepared by reacting diisocyanate (HMDI or TDI) with a mixture of calcium salt of mono(hydroxybutyl)phthalate [Ca(HBP)₂] and hydroxyl‐terminated poly(1,4‐butylene glutarate) [HTPBG₁₀₀₀], using di‐n‐butyltin‐dilaurate as catalyst. About six calcium‐containing PUEs having different composition were synthesized by taking the mole ratio of Ca(HBP)₂:HTPBG₁₀₀₀:diisocyanate (HMDI or TDI) as 3:1:4, 2:2:4, and 1:3:4. Two blank PUEs were synthesized by the reaction of HTPBG₁₀₀₀ with diisocyanate (HMDI or TDI). The polymers were characterized by IR, ¹H NMR, Solid state ¹³C‐CP‐MAS NMR, TGA, DSC, XRD, solubility, and viscosity studies. The T_g value of PUEs increases with increase in the calcium content and decreases with increase in soft segment content. The viscosity of the calcium‐containing PUEs increases with increase in the soft segment content and decreases with increase in the calcium content. X‐ray diffraction patterns of the polymers show that the HMDI‐based polymers are partially crystalline and TDI‐based polymers are amorphous in nature. The dynamic mechanical analysis of the calcium‐containing PUEs based on HMDI shows that with increase in the calcium content of polymer, modulus (g′ and g″) increases at any given temperature. © 2006 Wiley Periodicals, Inc. J Appl Polym Sci 100: 1720–1727, 2006     

高功率移相器粘接工艺初探

主要介绍了粘接技术在高功率铁氧体移相器上的应用。通过对其工艺途径及关键工序的控制，提出了采用粘接技术完成高功率移相器铁氧体的连接，不仅可以大量地缩短工作时间，而且可以使制造成本大幅度降低。     

The Torque Transmission Capabilities of the Adhesively-Bonded Tubular Single Lap Joint and the Double Lap Joint

With the wide application of fiber-reinforced composite materials in aircraft, space structures and robot arms, the design and manufacture of composite joints have become a very important research area because they are often the weakest areas in composite structures.

In this paper, the stress and torque transmission capabilities of the adhesively-bonded tubular single lap joint and the double lap joint were experimentally tested. In order to compare the experimental results with the calculated results, the stress and torque transmission capabilities were analyzed by the 3-dimensional finite element method taking into consideration the nonlinear properties of the adhesive.

From the experiments it was found that the torque transmission capabilities of the adhesively-bonded double lap joint was 2.7 times as large as that of the single lap joint. Also, it was found that the fatigue limit of the double lap joint was 16 times as large as that of the single lap joint.     

超微细改性Al(OH)3填充LDPE/EVA的研究

Al(OH）3是LDPE／EVA主要的阻燃，消烟填充剂。研究了不同粒度，表面处理及填充量的Al(OH）3对LDPE／EVA的氧指数（OI），烟密度等级（SDR）和物理机械性能的影响。     

ER－892高分散松香胶的制备和应用研究

介绍了高浓度、高分散松香胶的制备和应用方法．研究结果表明：该胶游离松香含量高，乳液粒径细，施胶能力强，可减少松香和硫酸铝用量５０％～６０％，克服夏季施胶障碍，提高纸张理化性能．     

The Effect of Temperature on the Strength of Adhesively-Bonded Composite-Aluminium Joints

Different materials have different coefficients of thermal expansion, which is a measure of the change in length for a given change in temperature. When different materials are combined structurally, as in a bonded joint, a temperature change leads to stresses being set up. These stresses are present even in an unloaded joint which has been cured at say 150°C and cooled to room temperature. Further stresses result from operations at even lower temperatures.

In addition to temperature-induced stresses, account also has to be taken of changes in adhesive properties. Low temperatures cause the adhesive to become more brittle (reduced strain to failure), while high temperatures cause the adhesive to become more ductile, but make it less strong and more liable to creep.

Theoretical predictions are made of the strength of a series of aluminium/CFRP joints using three different adhesives at 20°C and 55°C. Various failure criteria are used to show good correlation with experimental results.