Mn含量对Mg2Ni型合金相形成及放电性能的影响

采用按比例混合合金粉末压制成圆柱试样，然后用低温烧结和随后机械球磨的方法制备了非晶态的Mg2Ni型合金。研究了烧结和球磨对不同Mn含量的Mg2Ni型合金的相形成过程及电化学性能的影响。实验表明：在Mg2Ni中采用第三组元Mn对Mg进行适量的替代后，通过烧结及球磨方法可以获得均匀的非晶相；微量替代可有效地提高其放电容量：随替代量的增加，合金最大放电容量和高速放电能力降低，而充放电循环稳定性提高。     

Study On the Tribological Behavior of the Arc-added Glow Discharge Plasma Non-hydrogen Carburization On Titanium Alloy Surfaces

This paper introduces a new titanium alloys surface strengthening treatment by using the arc-added glow discharge plasmas non-hydrogen carburization technique. High purity and high strength graphite is selected as cooling cathode arc source for supplying carbon atoms and particle, which migrate to the titanium alloy(Ti6Al4V) surface and form modified layer. Thus, the hydrogen embrittlement is avoided while the tfibological behavior of the titanium alloy surface is improved in the respects of anti-friction and anti-wear ability.The tribological behavior of the modified layer under dry sliding against SAE52100 steel was evaluated on a ball-on-disc test rig. The results showed that the modified layer obtained a thickness of 30μm at 980℃, 30minutes. The microhardness of the Ti6Al4V alloy surface attained 936 HV, which was much larger than that of the Ti6AI4V alloy. The Ti6AI4V alloy was characterized by adhesion wear and scuffing under dry sliding against the steel, while the surface modified layer experienced much abated adhesion wear and scuffing under the same testing condition. This could be attributed to the carbon dement with different modalities exists in the modified layer.The modified layer showed good friction-reducing and fair anti-wear ability in dry sliding against the steel. Using the SEM,XRD and XPS, the phase structure and morphology of the carburization modified layer was analyzed.     

An investigation of ultrasonic-assisted electrical discharge machining in gas

This study focuses on using ultrasonic to improve the efficiency in electrical discharge machining (EDM) in gas medium. The new method is referred to as ultrasonic-assisted electrical discharge machining (UEDM). In the process of UEDM in gas, the tool electrode is a thin-walled pipe, the high-pressure gas medium is applied from inside, and the ultrasonic actuation is applied onto the workpiece. In our experiment, the workpiece material is AISI 1045 steel and the electrode material is copper. The experiment results indicate that (a) the Material Removal Rate (MRR) is increased with respect to the increase of the open voltage, the pulse duration, the amplitude of ultrasonic actuation, the discharge current, and the decrease of the wall thickness of electrode pipe; and (b) the surface roughness is increased with respect to the increase of the open voltage, the pulse duration, and the discharge current. Based on experimental results, a theoretical model to estimate the MRR and the surface roughness is developed.     

40Cr钢电火花表面强化层的磨损特性研究

分析了在大接触应力的磨损条件下,表面残余应力和硬度对40Cr电火花强化层耐磨性的影响,探讨了其磨损机理。结果表明:滚动磨损和滚、滑动磨损时,随着试样表层硬度的提高,试样的耐磨性增大;强化层中的残余压应力可以提高强化层的硬度并增强其耐磨性。滚动磨损时,电火花强化层的磨损方式主要为粘着磨损、疲劳磨损和磨粒磨损三种机制;在滚、滑动磨损时,除上述三种机制外,还发生了氧化磨损。     

混粉电火花镜面加工技术及应用

利用自行研制的混粉电火花镜面加工装置，对混粉电火花镜面加工影响因素，加工表面性能等进行了深入研究，找出了粉末特性，工件材料，粉末浓度及放电参数等对混粉电火花镜面加工的影响规律，给出了合理的混粉电火花镜面加工工艺条件，以文中确定的加工工艺条件对铸造和压铸模具进行混粉电火花镜面加工，结果表明，该技术能提高模具制造质量，降低工人劳动强度，缩短模具制造周期。     

PBSZT系大功率压电陶瓷极化工艺的研究

为探索大功率低损耗压电陶瓷材料的最佳制备工艺,对改性锆钛酸铅压电陶瓷Pb0.9Ba0.05Sr0.05(Sn1/3Nb2/3)0.06(Zn1/3Nb2/3)0.06Ti0.44Zr0.44O3 0.5wt%MnO2 0.5wt%Sb2O3的极化工艺进行研究。结果表明,该体系的最佳极化电场为4Kv/mm,极化温度120℃左右,此时得到的陶瓷性能较佳。     

用WKB方法讨论透射系数和反射系数

本文用WKB近似方法讨论了势垒贯穿问题系数T和其透射反射系数R之和恒等为1,即满足恒等式T R=1,并进一步得出这一结论不仅适用于一般势垒贯穿而且在方势垒贯穿中也成立,最后讨论了势垒贯穿的几种极限情况,例如,h→0(即经典情况),势垒高度v→∞、v→0,势垒宽度a→∞、a→0,等几种特殊情况下的T及R的取值问题。     

微波介质陶瓷的界面特性及其对介电性能的影响

详细地总结了界面的偏析、扩散和润湿性对微波介电性能的影响机理。并评述了粉末的初始状态、烧结工艺、添加剂(掺杂)和烧结方法等因素对材料界面特性的影响，进而影响到材料介电性能的研究进展。最后指出了在微波介质陶瓷界面研究领域面临的问题及今后的发展方向。     

Unique Dielectric Behavior of 0.6Pb(Ni1/2W1/2)O3·0.4PbTiO3 Derived from Mechanical Activation

0.6Pb(Ni_1/2W_1/2)O₃·0.4PbTiO₃(0.6PNW·0.4PT) of complex perovskite structure is successfully synthesized by mechanical activation of mixed oxide composition, followed by sintering at 950°C. It exhibits a considerably stable temperature dependence of dielectric constant over the wide temperature range of −120° to 20°C, although there occurs a dielectric peak at around 74°C. Raman spectroscopic studies show the coexistence of tetragonal and pseudocubic perovskite phases on sintering at 950°C, which are attributed to the inhomogeneous distribution of PbTiO₃ arising from mechanical activation. The dielectric behavior can be fine tuned by thermal annealing at 750°C, leading to phase redistribution in PNW-PT.     

Diluent effects on carbonate mobility in bisphenol-A polycarbonate in the solid state

The effect of miscible low molecular weight additives on the mobility of the carbonate group in bisphenol-A polycarbonate (BPAPC) has been studied using n.m.r. and dielectric relaxation experiments in the solid state. Proton-enhanced dipolar-decoupled carbon-13 n.m.r. spectra of BPAPC, isotopically enriched at the carbonate position, are obtained without magic-angle sample spinning. The resolved chemical shift anisotropy allows study of nuclear spin relaxation for the carbonate groups in the polymer that have different orientations relative to the static magnetic field in the laboratory frame. The spin-lattice relaxation time in the rotating frame (T_1?) is measured at a motional-probe frequency of 50 kHz for the undiluted polymer and for BPAPC-diluent blends containing either dibutylphthalate or dinitrobiphenyl. The T_1? exhibits some dependence on orientation in all systems studied. In the blend containing dibutylphthalate (DBP), T_1? is decreased by a factor of two for all orientations of the carbonate group. This implies that DBP substantially increases the spectral density of 50 kHz motions in the carbonate region of the polymer at ambient temperature. In contrast, dinitrobiphenyl does not significantly alter the Fourier component of thermal fluctuations at 50 kHz. Dielectric relaxation measurements at 10 kHz reveal that the primary (T_g) and secondary (β) motional processes in BPAPC are affected by low molecular weight additives. An intermediate relaxation process appears in the temperature interval between the glass transition temperature (T_g) and the sub-T_g β-relaxation (T_β) in the polymer-diluent blends. The n.m.r. spin-lattice relaxation rate in the rotating frame, T^?1_1?, correlates well with the relative magnitude of the dielectric dissipation factor (tan δ_ε) between T_g and T_β.