基于滑模变结构的感应电动机直接转矩控制

针对感应电动机常规直接转矩控制中存在磁链、转矩脉动大,低速控制不精确等问题,在建立α-β坐标系感应电动机数学模型的基础上,提出了一种基于滑模变结构的新型直接转矩控制方法。该方法利用转速滑模变结构控制器代替常规直接转矩控制中的PI控制器,可有效减小常规直接转矩控制中的磁链和转矩脉动,增强了系统的稳定性。仿真结果证明了该方法的正确性。     

基于PR控制器的直接转矩控制策略研究

针对传统直接转矩控制中采用开关表控制造成转矩和电流脉动,以及传统调节器不能实现对交流输入信号的无静差控制等问题,基于电机空间电压矢量的转矩和磁链2个分量解耦的控制方式和PR控制器能够在静止坐标系下实现对交流输入信号的无静差控制,将PR控制器用于永磁同步电机的直接转矩控制中,并由此设计出磁链和转矩的双PR控制器。同时,在定子磁链的观测中,采用基于转子位置和定子电流的新型定子磁链估计方法。试验结果证明,将PR控制器对交流输入信号的无静差跟踪特性应用于基于空间电压矢量调制的直接转矩控制中,系统能获得优良的动态和静态响应,取得了显著的应用成效,由此验证了所提方法的正确性和可行性。     

Novel (Phenothiazinyl)Vinyl-Pyridinium Dyes and Their Potential Applications as Cellular Staining Agents

We report here the synthesis and structural characterization of novel cationic (phenothiazinyl)vinyl-pyridinium (PVP) dyes, together with optical (absorption/emission) properties and their potential applicability as fluorescent labels. Convective heating, ultrasound irradiation and mechanochemical synthesis were considered as alternative synthetic methodologies proficient for overcoming drawbacks such as long reaction time, nonsatisfactory yields or solvent requirements in the synthesis of novel dye (E)-1-(3-chloropropyl)-4-(2-(10-methyl-10H-phenothiazin-3-yl)vinyl)pyridin-1-ium bromide 3d and its N-alkyl-2-methylpyridinium precursor 1c. The trans geometry of the newly synthesized (E)-4-(2-(7-bromo-10-ethyl-10H-phenothiazin-3-yl)vinyl)-1-methylpyridin-1-ium iodide 3b and (E)-1-methyl-4-(2-(10-methyl-10H-phenothiazin-3-yl)vinyl)pyridin-1-ium tetrafluoroborate 3a′ was confirmed by single crystal X-ray diffraction. A negative solvatochromism of the dyes in polar solvents was highlighted by UV-Vis spectroscopy and explanatory insights were supported by molecular modeling which suggested a better stabilization of the lowest unoccupied molecular orbitals (LUMO). The photostability of the dye 3b was investigated by irradiation at 365 nm in different solvents, while the steady-state and time-resolved fluorescence properties of dye 3b and 3a′ in solid state were evaluated under one-photon excitation at 485 nm. The in vitro cytotoxicity of the new PVP dyes on B16-F10 melanoma cells was evaluated by WST-1 assay, while their intracellular localization was assessed by epi-fluorescence conventional microscopy imaging as well as one- and two-photon excited confocal fluorescence lifetime imaging microscopy (FLIM). PVP dyes displayed low cytotoxicity, good internalization inside melanoma cells and intense fluorescence emission inside the B16-F10 murine melanoma cells, making them suitable staining agents for imaging applications.     

STUDY ON THE VARIATION MECHANISM OF CARBON CONTENT OF LIQUID IRON IN MELTING GASIFIER

This paper studied the changing principles of carbon content in direct reduction iron (DRI) and liquid iron in the COREX melting gasifier. Under the normal working conditions of experimental equipment, liquid nitrogen was poured into the melting gasifier from its tuyere to cool down quickly. And then seven cross sections were made to study the carburization reaction and its characteristics of the solid iron and the liquid iron, and also the reaction of carbon between the slag and the metal. According to the results, the influences of the thickness of the semi-coke layer and the temperature on the carbon content of liquid iron in the COREX melting gasifier were confirmed.     

基于DD伺服传动器实现三轴联动定位的设计

直接驱动（DD）伺服是一种高性能的伺服产品，由于其特殊的构造和高精度的设计，使其在制造业、机器人领域得到广泛应用。文章结合自主设计的激光内雕机控制方案，在分析系统工作原理基础上，详述了DD伺服位置控制方法，通过整定其PID参数，实现了三轴联动系统的准确定位。     

Effects of surfactant and particle size on the microstructure and strength of Si3N4 foams with high porosity

The highly porous Si₃N₄ ceramic foams were prepared by direct foaming with mixed surfactants. The surface tension and viscosity of slurries were tailored by different carbon chain length of surfactants and different mean Si₃N₄ particle size to achieve the pore size controlling. The nearly linear relationship between the pore size and the ratio of surface tension to viscosity was observed, which indicates that the pore size could be precisely tailored by the slurry properties. Si₃N₄ ceramic foams with porosity of nearly 94%, mean pore size of 110–230 µm, and compressive strength of 1.24–3.51 MPa were obtained.     

磷石膏提质降杂实验研究

磷石膏的综合利用对保护环境、促进企业可持续健康发展具有重要意义,但是磷石膏中的磷、氟、二氧化硅等杂质影响其利用。针对云南磷石膏中二氧化硅含量高的问题,采用正浮选工艺开展了磷石膏提质降杂的实验研究。通过单因素条件实验获得了合适的工艺参数：浮选温度为15 ℃、矿浆pH为2、十二胺用量为300 g/t。在此条件下,进行了“一粗二精”的正浮选开路流程实验,获得了二水石膏（CaSO₄·2H₂O）质量分数为97.5%、二氧化硅质量分数为1.17%的精矿,所得精矿达到了GB/T 23456—2018《磷石膏》一级品指标的要求;二水石膏回收率为98.58%、二氧化硅去除率为92.23%。通过正浮选不仅成功实现了二水石膏和二氧化硅的有效分离,而且磷石膏中的水溶磷和水溶氟也得到了有效去除,从而提高了磷石膏的品质。     

SPV490钢轧后在线热处理工艺研究

研究了SPV490钢控轧后在线直接淬火、回火工艺参数与其力学性能之间的关系。分析了不同的工艺参数对钢板组织及性能的影响。结果表明:经奥氏体再结晶区和未再结晶区两阶段结合控制轧制后在线930℃直接淬火、640℃回火,钢板可获得均匀、细小的回火索氏体组织,其综合力学性能均超过标准要求。     

Al-K2ZrF6体系熔体反应法合成复合材料的微观组织和力学性能

开发了Al-K2ZrF6体系熔体反应法合成原位铝基复合材料，采用XRD，SEM和TEM分析了复合材料中相组成、微观组织和界面结构。实验结果表明：合成的增强相为Al3Zr颗粒，常规金属型铸造的复合材料中其尺寸在3μm～4μm左右，一般成聚集态分布，颗粒形貌基本为长方体状：该复合材料经重熔快淬成形后，颗粒尺寸减小，基本为粒状，并弥散分布于基体上。Al3Zr／Al复合材料的界面结构研究表明，Al3Zr颗粒与Al存在一定的晶体学位向关系：[^-2^-21]Al3Zr∥[100]Al，（012）Al3Zr∥（1^-10）Al，其点阵错位度仅为10．87％，这表明Al3Zr颗粒可作为基体Al相的形核衬底。Al3Zr／Al复合材料的力学性能测试显示，当Al3Zr颗粒体积分数为11.2％时，抗拉强度和屈服强度分别为148．7MPa和110．2MPa，而且Al3Zr／Al复合材料的抗拉强度和屈服强度均随颗粒体积分数增加显著提高。     

不同分散染料微胶囊的制备及应用

采用原位聚合法进行双层造壁，对不同结构的分散染料进行胶囊化。将分散染料高速均化后，在pH=4～6时加入TMM，65℃保温1．5小时，再滴加一定量PEHMM，在75℃时保温2.5小时进行双层造壁、C.I.分散橙30染料胶囊的粒径平均值为13．53μm，中值8．732μm；C.I．分散蓝56微胶囊粒径平均值为36.3μm，中值24.87μm。胶囊染色结果显示：这两只染料性能优于传统染料，染色后其废液的吸光度分别为0.021和0.003，比传统染色废水的1.286和0.786低很多。