Process conditions affect pigment quality and yield in extracts of purple sunflower hulls

Extract of purple sunflower hulls is a potential red food colorant; however, suitable process conditions must still be identified. Selected process variables were studied using bench-scale units to prepare, clarify, concentrate and spray dry extracts. Concentration by evaporation at 32°C and addition of maltodextrin to 15% (wt/dry wt) prior to drying largely eliminated pigment degradation during those steps. Relative to water extracts, extracts prepared with 5 to 15% ethanol in water generally yielded more pigment with similar levels of degradation and loss during subsequent processing. Use of 5% ethanol/2% citric acid reduced yield by about half relative to water, but gave a powder with a lower degradation index and wetting time. Percentage recovery of pigment during concentration and drying was not greatly affected by solvent type or extraction temperature.     

细长钢管内壁涂塑工艺

采用流化床和热喷涂方法喷涂直径小于２０ｍｍ的长钢管内壁。叙述了工艺过程和涂层检测方法。     

复合电镀层应用的新动向

介绍了复合电镀层应用的新动向，如电解工业用电极的制备，铝发动机气缸的应用，重点介绍Sn-Ag纳米微粒复合镀层做为无铅可焊镀层的溶液，pH值，霍氏槽及可焊性试验的结果，还介绍了具有装饰和优良憎水性的镍－聚四氟乙烯微粒复合镀层，简述了其工艺过程，溶液组成和操作条件，镀层特性及应用。     

Phosphorus seed coating increases phosphorus uptake,early growth and yield of pearl millet (Pennisetum glaucum (L.) R. Br.) grown on an acid sandy soil in Niger,West Africa

In pot and field experiments conducted in 1990 and 1991 on an acid sandy, phosphorus (P) deficient soil in Niger, West Africa, the effect of seed coating on seedling emergence, early growth and grain yield of pearl millet (Pennisetum glaucum (L.) R. Br.) was studied. Seeds of pearl millet were coated with different rates (0; 0.5; 1.0; 2.0; 5.0; 10.0 mg P seed^–1) and types of P fertilizers (single superphosphate, ammonium dihydrogen phosphate; monocalcium phosphate, sodium dihydrogen phosphate and sodium triphosphate). Seedling emergence was generally reduced at coating rates higher than 0.5 mg P seed^–1 and prevented with single superphosphate and sodium triphosphate at rates higher than 5 mg P seed^–1. No correlation was found between the pH and osmomolity of the coatings and final emergence of millet seedlings. The most favourable effect on plant growth and P content was achieved with ammonium dihydrogen phosphate (AHP) as seed coating. This was attributed to the enhancement effect of ammonium on P uptake. Compared to the untreated control dry matter production at 20 days after planting (DAP) was increased by 280%, P content per plant by 330%, total biomass at maturity by 30% and grain yield by 45%. Although seed coating with AHP may be harmful to seedlings emergence, it represents a suitable method to enhance early growth and increase yield of pearl millet.     

两种聚氨酯防水涂料的比较

对焦油型和非焦油水固化型聚氨酯防水涂料B组分的生产工艺、配方特点，施工操作工艺、固化时间、涂膜性能等方面进行了比较，指出新开发的非焦油型聚氨酯涂料生产周期短、能耗少、气味小，是环保型聚氨酯防水涂料。     

中国涂料现状及今后发展热点(一)

综述了目前中国涂料业的发展概况,并介绍了今后发展趋势和研究热点──防腐蚀涂料、卷材涂料、功能涂料、绿色木器涂料和粉末涂料等5种涂料。     

锌系工件的静电粉末涂装和工艺管理

讨论了锌系工件喷涂的相关工艺、现场管理、技术参数、质量检验和环境要求等。     

400kt／a硫酸高效电除雾器的设计参数与运行

介绍 4 0 0 kt/ a硫酸系统电除雾器总体结构及工艺设计参数 ,投入运行后 ,除雾效率低 ,介绍对存在问题的分析及解决过程 ,并介绍 2点成功经验     

铝炭制品防氧化涂料的作用机理

采用热分析等研究方法，分析了铝炭制品的氧化过程，研究了以阻断铝炭制品与氧气接触来实现防氧化的硼硅酸盐系涂料的高温特性和防氧化机理，以及不同结合剂对涂料与铝炭制品界面行为的影响。     

Formation of hydrophilic starch coatings on polyethylene films

Thin starch coatings were deposited onto polyethylene (PE) film surfaces when PE films were immersed in 1% jet cooked starch solutions and the hot solutions were allowed to cool. Normal cornstarch, waxy cornstarch, high amylose cornstarch, and solvent‐extracted normal cornstarch (to remove native lipid) were used in these experiments. Amounts of adsorbed starch varied from about 0.03–0.05 mg per cm² of PE, and these starch coatings imparted hydrophilic properties to film surfaces, as evidenced by contact angle measurements. Although starch could be removed by gently rubbing water‐wet PE surfaces, air‐dried coatings were more firmly attached, and did not separate from the PE surface when films were bent or flexed. SEM images of starch‐coated film surfaces showed that starch was deposited as particles less than 1 μm in diameter, and also as aggregates of these submicron particles. Despite the fact that some starch samples contained only very small amounts of amylose and native lipid, surface‐deposited starch in all experiments contained 90–100% amylose; and exhibited the same V_h X‐ray diffraction pattern, indicative of helical inclusion complex formation. © 2002 Wiley Periodicals, Inc. J Appl Polym Sci 84: 1781–1788, 2002; DOI 10.1002/app.10589