Durability of hygrothermally aged graphite/epoxy woven composite under combined hygrothermal conditions

The objective of this study was to examine the effects of hygrothermal aging on the durability of a graphite/epoxy woven composite material system. The study was part of a larger project in which the objective was to evaluate and model the effects of moisture, temperature, and combined hygrothermal conditions on the strength and life of a graphite/epoxy woven composite material system. The results presented here represent an extension of the work by Patel and Case (Int. J. Fatigue 22 (2000) 809).

The hygrothermal aging consisted of cyclical temperature and moisture variations which were meant to simulate mission conditions for an advanced subsonic aircraft. Durability studies were carried out on the aged material system in the form of fatigue and residual strength testing under humid and elevated temperature environments. Damage mechanisms and failure modes were determined through fatigue testing, residual strength testing, and nondestructive evaluation.

Changes in physical appearance, thermal analysis results, fracture surfaces, and moisture diffusion behavior all supported the idea that the material was affected by the aging process. However, experimental testing also showed that the initial and residual tensile properties of the aged material were virtually unaffected by the imposed environmental aging (as compared to unaged material testing results), except when tested at elevated temperature. At elevated temperature, both the dynamic stiffness and residual strength were noticeably reduced from that at room temperature.     

酚醛树脂复合板在热连轧机中的应用

重点分析了现有F7机架出口导卫装置的情况。原导卫材料是由铸钢制造 ,由于摩擦和高温常常引起热连轧带钢表面划伤 ,根据现场实际情况用酚醛树脂复合板替代铸钢导卫装置。实践表明 ,这种改造即可行又可靠 ,并取得了好的效果     

用环氧厚浆涂料防混凝土碳化

介绍了针对早期建筑的混凝土桥梁碳化情况采用H52-S4环氧厚浆涂料进行封闭保护、防腐处理的施工方法及施工工艺，并提出施工中应注意的有关事项，对温度影响、表面气泡处理进行了讨论，提出合理化建议。     

环氧基的PCB对无铅组装的兼容性

综述了环氧树脂基的PCB与无铅化组装的兼容性问题。经过大量试验表明,常规的FR-4基材和双氰胺固化的高Tg基材是不能满足无铅化组装要求的,而采用酚醛固化的中等-Tg的环氧树脂基材是可能成为无铅化组装用基材的。同时,PCB制造过程也起着重要的作用。PCB设计和再(回)流焊的加热梯度也影响着无铅化的性能。     

可与氟树脂基板相匹敌的热可塑性树脂基板材料

概述了可以与氟树脂基板相匹敌的低介质特性的热可塑性树脂基板材料的开发和应用。     

Anhydrous esterification of myristic acid with propylene: Ion exchange resin and acid-treated clay as catalysts

Anhydrous esterification of myristic acid with propylene was carried out in the temperature range of 110–145°C and pressure from 190–195 psig in the presence of Amberlyst-15 (cation exchange resin) and Filtrol-24 (acid-treated clay) as catalysts. The product ester, isopropyl myristate finds use in cosmetic and topical medicinal preparations where good absorption through the skin is desired. Filtrol-24 is the catalyst of choice, and the recommended operating temperature is 130°C with a pressure of 190 psig.     

The effects of glycol methacrylate as a dehydrating agent on the dimensional changes of liver tissue

The dimensional changes of liver sections during the course of processing with glycol methacrylate (GMA) or with ethanol are described. Tissue processing with ethanol served as a control. During prolonged processing steps (24 h each), linear shrinkage of tissue specimens dehydrated with GMA at room temperature was 13.2%. Subsequent infiltration with GMA resulted in trivial swelling, and polymerization in slight shrinkage (2.3%). In comparison, processing with cold GMA resulted in shrinkage during dehydration (about 10.8%), a slight swelling in pure GMA, followed by shrinkage during polymerization (2.2%). Short routine processing schedules resulted in similar shrinkage/swelling patterns, although precise values differed slightly. In all experiments, ethanolic dehydration resulted in smaller dimensional tissue changes than did GMA dehydration. The dimensional changes of tissue sections during stretching on water, mounting and drying compensated for the major part of the shrinkage manifested during processing.     

某炼油厂一级浮床除盐系统阳床工艺特性及调整试验

论述了某厂一级除盐系统阳床工艺特性及调整试验过程，对存在问题进行分析并改进，得到了实际运行最佳方式和参数，取得良好效果。     

Phenol novolac/poly(4- hydroxyphenylmaleimide) blend hardeners for DGEBA-type epoxy resin

Phenol novolac/poly (4-hydroxyphenylmaleimide) (PHPMI) blends were used as an epoxy resin hardener. The curing behavior of the above system and the thermal and mechanical properties of the cured epoxy resin were studied. It was not necessary to use a curing accelerator for this system, because PHPMI caused acceleration of the curing reaction. The curing mechanism of this system was investigated by using model compounds. Test pieces from the neat resins and the glass fiber reinforced resins were evaluated in terms of thermal and mechanical properties, respectively. It was found that heat resistance and mechanical properties were improved by increasing the amount of PHPMI in the hardener.