Effect of crack-growth mechanism on the prediction of fracture load of adhesive joints

This paper presents observations regarding the cracking behavior of tensile-loaded structural adhesive joints. Experiments showed that fracture occurred by the development and propagation of a damage zone, rather than a single, sharp crack, and that the presence of the adhesive spew fillet did not affect the fracture load of the adhesive joints studied. For joints bonded with the mineral-filled epoxy Cybond 4523GB (American Cyanamid), there was approximately 5 mm of subcritical crack propagation prior to final fracture. Fracture-load predictions based on the initial uncracked geometry made in previous papers were unaffected by this small change in geometry. For joints bonded with the rubber-toughened epoxy Permabond ESP 310, approximately 50 mm of subcritical crack propagation was observed. It was again found that predictions made in previous papers on the basis of the initial geometry gave a good estimate of the final fracture load even though this subcritical crack propagation significantly altered the geometry, and thus the applied energy release rates. The effect of shear deformations of the adherends was also investigated, and it was found that shear deformations could be neglected in engineering calculations for joints subject to remote tensile loading.     

大规模集成电路浮栅ROM器件总剂量辐射效应

提出了一种大规模集成电路总剂量效应测试方法:在监测器件和电路功能参数的同时,监测器件功耗电流的变化情况,分析数据错误和器件功耗电流与辐射总剂量的关系.根据该方法利用60Co γ射线进行了浮栅ROM集成电路(AT29C256)总剂量辐照实验,研究了功耗电流和出错数量在不同γ射线剂量率辐照下的总剂量效应,以及参数失效与功能失效时间随辐射剂量率的变化关系,并利用外推实验技术预估了电路在空间低剂量率环境下的失效时间.     

胜利油田污水储罐腐蚀防护方法评价

对胜利油田纯粱采油厂A3钢制生产污水（水温约60℃）储罐使用寿命过低的原因进行了实验考察。水质分析数据表明氯离子浓度高（45-48gm）是污水腐蚀性强的主要因素。A3钢在60℃污水中的腐蚀速率，由极化曲线数据计算的值大大高于失重法测定值，敞开系统中失重法测定值又高于密闭系统中测定值，挂片上出现蚀孔，说明储罐中A3钢发生了氧存在下氟离子引起的局部腐蚀（孔蚀）。元素分析结果表明．储罐阴极保护所用的牺牲阳极铝材含铁等元素量超标。牺牲阳极密封不良，在实验污水中7天后电流效率仅为2．92％，失去阴极保护能力。处于实验污水环境中的有涂层保护的A3钢．14天后出现腐蚀极化电流，表明涂层已失去完整性。要提高该采油厂及胜利油田其他采油厂污水储罐的使用寿命，必须改用合格的牺牲阳极和保护涂层材料。图3表2参7。     

Is the Promissory Note of Personality as Vulnerability to Depression in Default? Reply to Zuroff, Mongrain, and Santor (2004).

In contrast to D. C. Zuroff, M. Mongrain, and D. A. Santor (2004), the current authors find the promissory note of dependency-sociotropy (DEP-SOC) and self-criticism-autonomy (SC-AUT) as a model of risk for depression to be in default. The authors propose reorganizing what has been cast as unitary effort into 3 distinct endeavors: a psychoanalytic clinical theory, development of a refined empirical model of risk for clinical depression, and research examining the effects of DEP-SOC and SC-AUT on interpersonal relationships in nonclinical samples. The authors identify some issues that need to be accommodated regardless of whether the assessment of Zuroff et al. (2004) or their own is accepted. DEP-SOC and SC-AUT are best construed as correlated, continuous dimensions. Future work also needs to accommodate depression as chronic recurrent condition, advances in developmental psychopathology, and more stringent criteria for positing a risk factor for clinical disorder. (PsycINFO Database Record (c) 2010 APA, all rights reserved)     

三峡工地高压供电线路故障判断方法的探讨

高压供电设备故障特别是输电线路的高压接地故障对工地的影响是相当大的。由于接地故障为隐性故障，没有明显的物理现象，且若是长期接地可能会发展成较为严重的两相或三相短路故障，使系统解列运行直至崩溃；由于工地流动人员较多，还易造成电击事故。利用高压一相接地时在线路中产生零序电压这一特性来迅速判断和切除接地的用电设备，可以保证各项施工的顺利进行。     

双头螺栓失效分析

与汽车电机装配在一起的双头螺栓在拧紧后不久便发生断裂。采用扫描电镜、化学分析、金相检验等方法对失效件进行了检测，同时又进行了氢脆试验验证。结果表明，螺栓在进行表面酸洗及电镀时，氢向金属内部扩散和富集，当氢浓度达到一定临界值后，促使氢致裂纹的产生和扩展。在外应力的作用下，即出现氢脆现象导致螺栓断裂。     

部件试验模态综合的简便方法

本文将一种基于完备模态基的模态综合技术应用于子结构的试验模态综合,获得成功。这种半试验半理论的模态综合方法是一种较为简便的、要求试验工作量较小的试验模态综合法,因为它只要求测量子结构的振动模态和频率即可。数值仿真结果表明,这种简便的试验模态综合法是行之有效的。     

有杆泵抽油系统可靠性分析

抽油机井有杆果采油装置检泵故障数据的特点在于相邻两次检泵间隔之间的时间并非总是来自同一总体，可能有某种趋势的变化。通过对故障数据的趋势性检验，可验证其对某一随机过程模型的适应性，从而判定某一口井或某一批工况大致相同油井的运行可靠性，实现对生产井运行可靠性的定量评估。还通过实例说明了有杆泵抽油系统检泵故障数据的可靠性分析方法。     

复合材料压缩破坏模式的缺陷敏感性

本文基于弹塑性分叉理论研究单向纤维增强复合材料的压缩破坏模式和压缩强度对缺陷的敏感性问题。对于常见复合材料,所得结论是:无缺陷或者小缺陷情况的破坏模式为倾斜破坏带;大缺陷情况的破坏模式为水平破坏带;形成水平破坏带的压力值小于形成倾斜破坏带的压力。     

自成像列阵共振腔的分析——Ⅰ.Talbot共振腔

利用自成像效应进行半导体列阵激光器锁相是一种重要的外腔锁相技术,所构成的共振腔可分为Talbot腔和带相位补偿板的Lau腔。我们用Fox-Li方法计算了共振模式。本文给出了Talbot腔的计算结果和分析,表明同相和反相模的损耗随腔长变化存在临界点。