On the corrosion fatigue crack initiation model and expression of metallic notched elements

In the present study, attempts are made to extend the application of the mechanical model for the fatigue crack initiation (FCI) and the FCI life formula of metallic notched elements in laboratory air to those in the corrosive environment. The test results and analysis of the corrosion FCI (CFCI) life of aluminum alloys and Ti---6A1---4V show that the expression of the CFCI life obtained by modifying the FCI life formula in laboratory air can give a good fit to the test results of the CFCI life. The salt water (3.5% NaCl) environment has no effects on the CFCI resistant coefficient compared with the FCI resistant coefficient in laboratory air. However, 3.5% NaCl environment greatly decreases the CFCI threshold of aluminum alloy, but has little effect on the CFCI threshold of Ti---6A1---4V. The loading frequency ranging from 1 Hz to 10 Hz has no appreciable effect on the CFCI life, and thus, the CFCI threshold of aluminum alloys investigated. Hence, the expression for the CFCI life of metallic notched elements proposed in this study is a better one, which reveals a correlation between the CFCI life and the governing parameters, such as, the geometry of the notched elements, the nominal stress range, the stress ratio, the tensile properties and the CFCI threshold. However, this new expression of the CFCI life needs to be verified by more test results.     

氧化铝陶瓷缺口件循环疲劳及断裂机理

用实验方法研究了Ａｌ＿２Ｏ＿３陶瓷缺口试件在循环载荷作用下的疲劳寿命。结果表明，缺口导致的应力集中效应显著降低了循环疲劳寿命；若用缺口根部最大应力为应力水平，则不同缺口半径陶瓷试件具有相同疲劳断裂规律，说明陶瓷材料的疲劳集中系数和理论应力集中系数相同。本文还分析讨论了陶瓷材料的循环疲劳寿命表达式和循环疲劳断裂机理。     

Grain Boundary Sliding in Fatigue of Pure Aluminum

The distributions of plastic strain near grain boundaries induced by fatigue loading were investigatedby the fiducial grid method in pure aluminum specimens, and the resulted grain boundary sliding(GBS) was systematically analysed. The results show that the strain field near a grain boundary isnonuniform. GBS is restricted by the junction of grain boundaries and causes discontinuities of bothdisplacement and strain. A peak value of shear strain was created in short-range area across the grainboundary. GBS plays an important role in cyclic softening and secondary hardening. The control fac-tor of GBS is the relative orientation between two grains and the macro orientation of the grainboundary rather than the ∑ value of the boundary.     

A new monitoring system for piping systems in fossil fired power plants

A CEC-funded project has been performed to tackle the problem of producing an advanced Life Monitoring System (LMS) which would calculate the creep and fatigue damage experienced by high temperature pipework components. Four areas were identified where existing Life Monitoring System technology could be improved:

1. 1. the inclusion of creep relaxation

2. 2. the inclusion of external loads on components

3. 3. a more accurate method of calculating thermal stresses due to temperature transients

4. 4. the inclusion of high cycle fatigue terms.

The creep relaxation problem was solved using stress reduction factors in an analytical in-elastic stress calculation. The stress reduction factors were produced for a number of common geometries and materials by means of non-linear finite element analysis. External loads were catered for by producing influence coefficients from in-elastic analysis of the particular piping system and using them to calculate bending moments at critical positions on the pipework from load and displacement measurements made at the convenient points at the pipework. The thermal stress problem was solved by producing a completely new solution based on Green's Function and Fast Fourier transforms. This allowed the thermal stress in a complex component to be calculated from simple non-intrusive thermocouple measurements made on the outside of the component. The high-cycle fatigue problem was dealt with precalculating the fatigue damage associated with standard transients and adding this damage to cumulative total when a transient occurred.

The site testing provided good practical experience and showed up problems which would not otherwise have been detected.     

工艺因素对金属封装外引线弯曲疲劳的影响

考察了金属封装外壳制造工艺对外引线弯曲疲劳的影响,发现电镀镍是导致外引线弯曲次数明显减少的最主要工艺步骤,且随镀镍层厚度的增加,弯曲次数减少。此外还讨论了外引线的氢含量和晶粒度对引线抗疲劳能力的影响。     

控制棒驱动机构常温通风均匀性试验研究（续篇）

本文叙述控制棒驱动机构在常温通风均匀性方面的试验。通过平顶型堆顶结构和球面型堆顶结构通风均匀性试验的比较,找出通风的阻力、风速和不均匀系数间的规律。     

引黄工程首次试通水期间泵站安全监测资料的分析

介绍了引黄工程泵站建筑物的结构特性、监测情况以及首次试通水期间 安全监测量的变化特点，指出了监测资料反映出的一些工程实际问题。通过定量分析，揭示 了建筑物承受的主要荷载以及监测量的变化规律，发现了工程问题发生和发展的原因，较为 系统、深入地从安全监测的角度研究了引水工程泵站地下洞室群的工作性态。     

重载齿轮齿面疲劳损坏及预防

点蚀和剥落是重载齿轮齿面疲劳损坏最普遍的形式.根据齿轮失效分析实例,对齿面初始点蚀、破坏性点蚀和齿面剥落等三种主要疲劳损坏的特征、发生部位及破损危害程度进行了分析研究,较系统地论述了齿轮接触疲劳破坏机理,影响因素及其产生原因,并对有关的齿面破坏提出了相应的预防措施.     

底部两层框架-抗震墙砖房抗震能力的分析方法与设计控制

提出了底部两层框架 -抗震墙砖房框剪层和砖混层的极限受剪承载力、侧移刚度、极限剪力系数计算公式 ,并基于设置不同数量抗震墙的底部两层框架 -抗震墙砖房的实例计算和弹塑性时程分析 ,给出了结构砖混过渡层与相邻框剪层的极限剪力系数比和侧移刚度比的合理取值及薄弱楼层位置判别和破坏状态评定的方法和原则。     

环形截面大偏心受压构件截面延性系数计算

延性是混凝土构件的一项重要特性 ,延性系数是构件延性的度量 ,由于沿周边均匀配筋环形截面偏心受压构件受力计算的特殊性 ,至今没有一个较精确的计算公式。本文根据沿周边均匀配筋环形截面偏心受压构件的工作特点 ,采用常用应力应变关系和基本假设 ,提出了其延性系数的计算方法。