Reviews the book, Qualité de vie et drogues. Place aux jeunes (1986). In this volume, the author shares his initiatives in the plan of therapeutic and preventive intervention. This book discusses drug use and quality of life in young people. (PsycINFO Database Record (c) 2010 APA, all rights reserved)     

Thermal—Mechanical Fatigue Behavior and Life Analysis of Cast Ni—base Superalloy K417

In-phase(IP) and out-of-phase(OP)thermal-mechanical fatigue(TMF) behavior of cast Ni-base superalloy K417 was studied.All experiments were carried out under total strain control with temperature cycling between 400-850℃.Both in-phase and out-of-phase TMF specimens exhibited cyclic hardening followed by cyclic softening at the minimum temperature.Besides,they cyclically hardened in the early stage of life followed by cyclic softening at the minimum temperature.Besides,they cyclically hardened in the early stage of life followed by cyclic softening at the maximum temperature.OP TMF life was longer than of IP TMF.Various damage mechanisms operating in different controlled strain ranges and phasing were discussed.A few life prediction methods for isothermal fatigue were used to handle TMF fatigue and their applicability to superalloy K417 was evaluated.The SEM analysis of the fracture surface showed that transgranular fracture was the principal cracking mode for both IP and OP TMF.Oxidation was the main damage mechanism in causing shorter fatigue life for IP TMF compared with OP TMF.     

提高连续油管使用寿命的方法

从采用软件跟踪疲劳寿命 ,截断法 ,变径连续油管 ,反转使用连续油管 ,防止连续油管损伤 ,合理配置设备 6个方面讨论了控制管串疲劳 ,提高连续油管使用寿命的方法 ,并得出结论 :控制管串疲劳的方法中 ,最有效的方法是实际作业截断法。指出要尽量减少连续油管在带内压下工作 ,也要研究开发降阻性能好的工作液 ,以延长连续油管使用寿命、降低作业风险。     

盛钢桶铝锆碳滑板的研究与生产

通过研究,在盛钢桶用铝锆碳滑板的生产过程中,调整了ZrO2的加入量,添加了复合抗氧化剂,使滑板具用较高的强度和抗氧化性能,提高了滑板的使用寿命.     

Crack growth in aluminium alloy sheet material under flight-simulation loading

Crack propagation tests were carried out on 2024-T3 sheet specimens to study the effects of omitting low-amplitude cycles from the gust-dominated TWIST load sequence (MiniTWIST) and the removal of small load ranges from the manoeuvre-dominated FALSTAFF load sequence (short FALSTAFF). In other tests high-amplitude loads of TWIST and MiniTWIST were truncated at different levels. The results are compared with data from similar test programmes, including crack initiation. Attention is paid to unstationary crack growth retardation and a transient retardation during initial crack growth started by an artificial crack.     

Microstructure-related fracture toughness and fatigue crack growth behaviour in toughened, anhydride-cured epoxy resins

Fracture toughness and fatigue crack propagation (FCP) of plain and modified anhydride-cured epoxy resin (EP) were studied at ambient temperature. Liquid carboxyl-terminated acrylonitrile-butadiene (CTBN) and silicon (SI) rubber dispersions were used as tougheners for the EP. The morphology of the modified EP was characterized by dynamic mechanical analysis (DMA) and by scanning electron microscopy (SEM). The fracture toughness, K_c, of the compositions decreased with increasing deformation rate. K_c of the EP was slightly improved by CTBN addition and practically unaffected by incorporation of the SI dispersion when tests were performed at low cross-head speed, v. Both modifiers improved K_c at high v, and also the resistance to FCP, by shifting the curves to higher stress intensity factor ranges, ΔK, by comparison with the plain EP. It was established that both fracture and fatigue performance rely on the compliance, J_R, at the rubbery plateau, and thus on the apparent molecular mass between crosslinks, M_c. The failure mechanisms were less dependent upon the loading mode (fracture, fatigue), but differed basically for the various modifiers. Rubber-induced cavitation and shear yielding of the EP were dominant for CTBN, whereas crack bifurcation and branching controlled the cracking in SI-modified EP. The simultaneous use of both modifiers resulted in a synergistic effect for both the fracture toughness at high deformation rate and the FCP behavior.     

国产核电厂蒸汽发生器下封头接管区模拟装置承受循环载荷能力的试验

国产核电厂蒸汽发生器下封头群孔接管区具有应力分布复杂、焊接施工条件差的特点。为考核其承受循环载荷的能力，设计制造了与实物相似的模拟试验装置，根据核电厂运行寿命期内的载荷特点，确定了模拟试验装置的试验载荷与试验循环数。循环加载试验的结果表明，蒸汽发生器下封头群孔接管区承受循环载荷的能力在寿命期内是符合要求的。     

Predicting posttraumatic growth in breast cancer survivors.

Wide variability exists with respect to how breast cancer survivors respond to common psychological and psychosocial challenges of their disease, ranging from posttraumatic stress disorder to posttraumatic growth. This cross-sectional study examined contextual, disease-related, and intraindividual predictors of posttraumatic growth in 224 randomly selected breast cancer survivors. A series of hierarchical regression analyses found that age at diagnosis, marital status, employment, education, perceived intensity of disease, and active coping accounted for 34%, 35%, and 28% of the variance in growth in relationships with others, new possibilities, and appreciation for life. These findings suggest that a more comprehensive model of growth will be helpful in understanding the various factors that play a role in breast cancer survivors' perception of psychological and psychosocial growth. (PsycINFO Database Record (c) 2010 APA, all rights reserved)     

真丝绸产品的清洁生产与生态设计

通过对真丝绸整个产品生命过程的分析，对其进行了生命周期评价，说明了丝绸与其产地环境之间的联系和影响，尝试寻求两者之间的和谐关系，提出了清洁生产工艺的规划和各种行之有效的对策和措施，尝试了对环境友好的丝绸印染工艺的生态设计。     

Ermüdungsverhalten und Dauerfestigkeit von Graphit und Aluminium – infiltriertem Graphit

Fatigue behaviour and endurance limit of graphite and of aluminium‐infiltrated graphite Fatigue properties of polycrystalline, isotropic graphite FU2590 and of FU2590 infiltrated with AlSi7Mg (FU2590/AlSi7Mg) were investigated in reversed bending tests at 25 Hz at numbers of cycles below 10⁷ and in tension‐compression tests at 20 kHz below 10⁹ cycles. The open porosity of Graphite (10‐11 Vol.‐%) was infiltrated with the aluminium alloy using the squeeze casting infiltration method, which led to an increase of the bending strength by 50 %, increase of tensile strength by 30 % and increase of stiffness by 15 %. Fully reversed tension‐compression loading of FU2590 delivers a mean endurance limit at 10⁹ cycles at the normalized maximum stresses (i.e. maximum tension stress of a cycle divided by the static strength) of 0,65±0,03. Mean numbers of cycles to failure of 10⁴ were found in fully reversed bending tests at the normalized maximum stress of 0,78. The infiltrated material shows approximately 30 % higher cyclic strength in reversed bending tests, and the mean endurance limit under tension compression loading increases by 15 %. The increased endurance limit of the infiltrated material is caused by the increased stiffness. The increased toughness of graphite due to the infiltration with aluminium is of additional beneficial influence at the higher cyclic stresses investigated in reversed bending tests and in static tests.