一种新型悬臂棒条筛的设计与应用

介绍了一种新型悬臂棒条筛分机械,论述了其结构、工作原理和技术特性。从理论和实践两方面论证了它的结构、处理能力、筛分效率、返矿率都明显优于普通悬臂棒条筛分机械,可广泛应用于高炉槽下烧结矿的筛分作业。     

Flow stress of high density polyethylene and nylon 66 at high rates of strain

Measurement of the flow stress of high density polyethylene (HDPE) and nylon 66 at strain rates of 10³ s^?1 using a split Hopkinson pressure bar technique is discussed. The flow stress at a strain of 10% has been determined for both polymers at 20°C. The intrinsic errors involved in this technique are briefly reviewed. The results indicate that the flow stress of HDPE and nylon 66 were 50MPa and 150MPa, respectively, at strain rates of about 10³s^?1.     

步进梁式炉的运动研究

对国内引进的、用于粉末冶金的步进梁式炉的运动,以图解法和解析法进行了分析,并对运动参数进行了理论推导和计算。本研究结果,对解决步进粱式炉的运动故障以及进行新型设计提供了有效的理论分析和计算依据。     

Concast连铸机自控系统简介

天津钢铁有限公司引进了瑞士Concast公司6机6流方、圆坯连铸机及相关技术，文章简要介绍了Concast连铸机的自动控制系统的特点和功能。     

热轧左旋螺纹钢的开发

介绍了在轧钢厂二车间开发顾客需要的Φ18、Φ20、Φ22的热轧左旋螺纹钢。在原有Φ18、Φ20、Φ22热轧圆钢的工艺基础之上做工艺设计，经实际生产轧制，其产品质量完全符合顾客要求。     

轧后穿水冷却工艺对棒材组织性能的影响

针对轧机产量提高后冷床冷却能力不足的问题 ,研制开发了棒材轧后穿水冷却技术。通过对小规格 2 0MnSiV热轧带肋钢筋进行轧后穿水冷却 ,钢材上冷床温度降低了 90～ 110℃ ,提高了产品质量 ,改善了各项力学性能 ,抗拉强度平均提高了 3 5～ 40MPa ,钢材性能合格率由 97.5 %提高到了 99.6% ,解决了冷床冷却能力不足、制约生产的瓶颈问题。     

集中载荷作用下的套管抗挤能力分析

根据油田套管损坏情况,建立了集中载荷作用下的套管抗挤能力计算模型,利用能量法和曲杆理论,分析研究了承受180°对称分布集中载荷、90°均匀分布集中载荷和120°均匀分布集中载荷下中厚壁套管抗挤能力,得出了理想圆管抗挤强度和套管屈曲临界挤毁压力的计算公式,通过分析比较理论解与有限元解,其最大相对误差不超过1%,得出了套管抵抗局部载荷的能力低于抵抗均布载荷的结论。     

HRB400月牙型螺纹钢筋试制

本文详细介绍了包钢采用平炉冶炼工艺试制HRB400钢筋的生产过程和检验结果，对试制中出现的问题提出了改进措施，并初步研究了稀土对HRB400钢筋质量与性能的影响。结果表明，采用平炉冶炼工艺可生产出符合GBl499—1988的HRB400钢筋。本次试验研究尚未看出稀土对HRB400钢筋的质量与性能产生明显影响。     

Microstructural investigation of long-term degradation mechanisms in GFRP dowel bars for jointed concrete pavement

Steel dowel bar is used to transfer loads in concrete pavement slab. However, once the steel dowel bar corrodes, it may cause faults, such as joint freezing in concrete pavement, level differences resulting from spalling or decreased efficiency of load transfer, etc., which are the same problems experienced by typical reinforcing steel. This study evaluated the applicability of glass fiber-reinforced polymer (GFRP) dowel bar as a substitute for steel dowel bar. A microstructural analysis was conducted to examine the decrease in durability of GFRP dowel bar exposed to deterioration environments. To analyze the deterioration mechanism of GFRP dowel bar, scanning electron microscopy was employed and the porosity was measured by the gas absorption method. It was concluded that the longer the GFRP dowel bar was exposed to deterioration environments, the more the interlaminar shear stress decreased. This result was validated by the microstructural analysis. © 2008 Wiley Periodicals, Inc. J Appl Polym Sci, 2008