Effects of a Nd—Fe—B magnetic filler on the crystallization of poly(phenylene sulfide)

The crystallization of poly(phenylene sulfide) (PPS) in a polymer–magnetic Nd—Fe—B powder suspension was studied. Isothermal crystallization behavior was analyzed by way of differential scanning calorimetry, and the kinetics were described via the Avrami equation. The Avrami parameters and the crystallization times were strongly affected by both the particle size and the presence of a coupling agent coated on the filler particles. The small Nd—Fe—B particles exhibited long induction and half‐times, whereas the large particles tended to have short crystallization times. Particles ranging from 38 to 150 μ appeared to have similar crystallization times and to have no significant change in the value of Avrami index with melt crystallization temperature. As a result of these analyses, the dynamic mechanical properties were determined to correlate the fundamental polymer crystallization characteristics and the physical properties of the PPS binder. The enhancement of the wetting of the filler to the binder was promoted through the coupling agent, as confirmed by dynamic mechanical testing performed on the samples. The storage modulus typically decreased because of the presence of the uncoated small particles. Conversely, the loss modulus was enhanced because of the presence of the coated small particles in the PPS binder. © 2002 Wiley Periodicals, Inc. J Appl Polym Sci 83: 1091–1102, 2002     

机械合金化Fe50Ti50非晶的形成及球磨强度对它的影响

本文通过电子扫描和Ｘ衍射对机械合金人Ｆｅ５０Ｔｉ５０非晶粉末形成做了研究。研究发现：机械合金非晶形成可以大致地分为二个阶段－粉末的破碎阶段和非晶的形成阶段。另外，对球磨强度对非晶形成的影响进行了研究。结果表明：强度低时粉末需要较长的时间才能形成非晶，强度高时粉末形成非晶的时间大大缩短，但在随后的球磨中，粉末会重新晶化形成新相。     

Kinetic model for water/oil absorption of mesquite gum (Prosopis juliflora) and gum arabic (Acacia senegal)

The water and oil uptake of mesquite and arabic gums in powdered form was studied at temperatures of 23, 35 and 45°C. A previously proposed equation to predict osmotic equilibrium was tested using the experimental data with both gums and a good statistical fit was obtained. Mesquite gum showed the highest water and oil absorption at all temperatures studied. Temperature dependence of the reciprocal of the S₁ and WL_∞ were determined using an Arrhenius equation. The activation energy for water and oil absorption for gum arabic was 21.98 and 39.57 kJ mol⁻¹, compared to that of mesquite gum having values of 15.79 and 46.16 kJ mol⁻¹, respectively. A second order kinetic model was obtained for water and oil absorption for both gums.     

Ti-6-22-22S合金步进轧制工艺加工棒材研究

采用步进轧制工艺制备了Ti-6-22-22S合金Ф50mm棒材，对加工、热处理、组织与性能的关系进行了分析。结果表明：在两相区上部温度960℃轧制获得细网篮组织，棒材性能较好且数据均匀；热处理后，得到双态组织，强度．塑性达到优良组合，而片层状组织强度较高，但塑性稍低。     

Microstructure and Mechanical Properties of Heat-treated GeSb_2Te_4 Thin Films

The effect of annealing on microstructure,adhesive and frictional properties of GeSb 2 Te 4 films were experimentally studied.The GeSb 2 Te 4 films were prepared by radio frequency(RF)magnetron sputtering,and annealed at 200℃and 340℃under vacuum circumstance,respectively.The adhesion and friction experiments were mainly conducted with a lateral force microscope(LFM)for the GeSb 2 Te 4 thin films before and after annealing.Their morphology and phase structure were analyzed by using atomic force microscopy(AFM)and X-ray Diffraction(XRD)techniques,and the nanoindention was employed to evaluate their hardness values.Moreover,an electric force microscope(EFM)was used to measure the surface potential. It is found that the deposited GeSb 2 Te 4 thin film undergoes an amorphous-to-fcc and fcc-to-hex structure transition;the adhesion has a weaker dependence on the surface roughness,but a certain correlation with the surface potential of GeSb 2 Te 4 thin films.And the friction behavior of GeSb 2 Te 4 thin films follows their adhesion behavior under a lower applied load.However,such a relation is replaced by the mechanical behavior when the load is relatively higher.Moreover,the GeSb 2 Te 4 thin film annealed at 340℃presents a lubricative property.     

Effect of carbon black composite (CBC) support properties on hydrodesulfurization performance of sulfided Mo and Co, and carburized Mo, catalysts

Carbon black composites (CBCs) have been prepared by pyrolyzing mixture of a carbon black with polyfurfuryl alcohol and then pretreated by oxidation with nitric acid, gasification with water steam or ammoxidation. The effects of the chemical character of the carrier surface, nature of the active metal phase and pH value of the impregnation solution on the catalytic activity towards the hydrodesulfurization (HDS) of thiophene of the CBC supported Mo (Co) catalysts were determined. It was stated that the catalytic properties of the CBC supported sulfides of Mo or Co and of Mo carbides are affected by the chemical character of the carrier surface. Generally, catalysts supported over basic surface CBC exhibit higher activity than those ones supported over CBC possessing acidic surface character. Co catalysts supported on acidic surface show lower activity (per mol of active metal) than Mo based ones supported on the same carrier. In the case of catalysts supported on basic CBC, Co exhibits distinctly higher activity than Mo. At the experimental conditions adopted for this study, CBC surface properties, active phase nature, and catalyst impregnation pH were found to exert a relatively small influence on both HDS and hydrogenation activities.     

Growth and optical property of zinc oxide thornballs

A new microstructure, thornball, of zinc oxide (ZnO) was synthesized by a very simple solid vapor deposition process under lead oxide (PbO) atmosphere. The microthornballs consist of numerous needles, which extend outwards in all directions symmetrically. They have dimensions of 120 μm in diameter, while the average diameter of the needles is about 100-200 nm. The needles on the balls grow along the 〈0 0 0 1〉 orientation and have gradient compositions along radial. Control experiments proved that PbO played an important role in the growth. Additionally, photoluminescence property was observed and provided the evidence that PbO did not deteriorate the optical properties of ZnO thornballs. This kind of microstructures has potential applications in the field of photochemical catalysis.     

织物树脂层压复合材料抗弹性能研究

针对防弹织物树脂层压复合材料的研制，考察了层压复合材料面密度，纤维类型，树脂体系，铺层混杂方式及纤维混杂分数，织物铺层，预置分层等因素对层压复合材料靶板弹道冲击性能的影响。