All-printed and highly stable organic resistive switching device based on graphene quantum dots and polyvinylpyrrolidone composite

We propose all printed and highly stable organic resistive switching device (ORSD) based on graphene quantum dots (G-QDs) and polyvinylpyrrolidone (PVP) composite for non-volatile memory applications. It is fabricated by sandwiching G-QDs/PVP composite between top and bottom silver (Ag) electrodes on a flexible substrate polyethylene terephthalate (PET) at ambient conditions through a cost effective and eco-friendly electro-hydrodynamic (EHD) technique. Thickness of the active layer is measured around 97 nm. The proposed ORSD is fabricated in a 3 × 3 crossbar array. It operates switching between high resistance state (HRS) and low resistance state (LRS) with OFF/ON ratio ∼14 for more than 500 endurance cycles, and retention time for more than 30 days. The switching voltage for set/reset of the devices is ±1.8 V and the bendability down to 8 mm diameter for 1000 cycles are tested. The elemental composition and surface morphology are characterized by XPS, FE-SEM, and microscope.     

Carbon nanotube filter for heavy metal ion adsorption

This study investigated carbon nanotube filtration technology using catalyst particles supported on silicalite-1–biomorphic carbon materials (BCMs). Aqueous solutions of Mn(II), Cu(II), Cr(III), Cd(II), and Pb(II) were used to test the efficiency of heavy metal ions removal. Carbon nanotubes (CNTs) were synthesized and grown on BCMs by the chemical vapor deposition method catalyzed with the catalyst (Co, Fe, and Ni). The synthesized CNTs with Co– and Fe– nanoparticles were typically multi-walled carbon nanotubes, and they showed good crystallinity (I_D/I_G = 1.05) and yield of (11.10 and 8.86) %. The removal efficiency of Mn(II), Cu(II), Cr(III), Cd(II), and Pb(II) ions using Co-catalyzed CNT filter was 97.57%, 98.01%, 97.89%, 97.42%, and 99.99%, respectively.     

The Electron–Phonon Interaction of Low-Dimensional and Multi-Dimensional Materials from He Atom Scattering

Atom scattering is becoming recognized as a sensitive probe of the electron–phonon interaction parameter λ at metal and metal-overlayer surfaces. Here, the theory is developed, linking λ to the thermal attenuation of atom scattering spectra (in particular, the Debye–Waller factor), to conducting materials of different dimensions, from quasi-1D systems such as W(110):H(1 × 1) and Bi(114), to quasi-2D layered chalcogenides, and high-dimensional surfaces such as quasicrystalline 2ML-Ba(0001)/Cu(001) and d-AlNiCo(00001). Values of λ obtained using He atoms compare favorably with known values for the bulk materials. The corresponding analysis indicates in addition, the number of layers contributing to the electron–phonon interaction, which is measured in an atom surface collision.     

Rare-earth free sensitizer in NaLuCrF4:Er upconversion material

Upconversion phosphors are known as a material system that can convert near-infrared light into visible/ultraviolet emissions by sequentially absorbing multiple photons. The studies on upconversion materials often use two rare earth (RE) ions as a sensitizer-activator pair. We investigated the influences on luminescence intensity depending on Cr-doping content (x) of hexagonal NaLu_0.98–xCr_xF₄Er_0.02 (x = 0–0.9) upconversion material by substituting Lu³⁺ ions with Cr³⁺in the absence of Gd³⁺. The change in upconversion luminescence intensity appears with saddle-like shape. We suggest that Cr³⁺ ions play the dual role as a constituent in host lattice and a sensitizer in the upconversion process. Optimal conditions for gaining the strongest upconversion emission correspond to x = 0.3–0.5, where there are effective energy transfers between Cr³⁺ and Er³⁺ ions and CrEr dimers. Apart from these values, the emission intensity decreases rapidly which can be ascribed to the absence of multiple-photon absorption for the case of low Cr³⁺ contents, and to the coupling between Cr³⁺ and/or Er³⁺ ions for the case of high Cr³⁺ contents. Magnetization and electron-spin-resonant measurements were performed to understand the correlation between the optical and magnetic properties.     

Effect of sintering temperature on solidification and migration of non-volatile and volatile heavy metals in glass-ceramic

Using tailings as material to prepare glass-ceramic is an excellent way to achieve the resource utilization of solid waste. However, at present, researches on the solidification and migration of heavy metals are limited. Therefore, in this study, ten groups of samples were prepared by controlling sintering temperatures. The solidification, migration, and leaching behavior of non-volatile and volatile heavy metals were studied. The research showed that, with the increase of temperature, the properties of the samples were improved. Fe participated in the phase transformation and evolved into insoluble iron pyroxenes solid solution, while Pb was homogeneously distributed in the glass matrix of glass-ceramics. The leaching concentrations of Fe and Pb in the glass-ceramics were 0.055 mg/L ～0.087 mg/L and 0.074 mg/L ～0.140 mg/L, which were far below the threshold value. The results showed that heavy metals can be effectively solidified in glass-ceramics and have good environmental benefits.     

Contribution of metal vapor mass at periphery part of pulsed arc to electromagnetic force in weld pool

The arc welding has been used in various welding methods because it is inexpensive and high in strength after welding. However, it is a problem that accidents such as collapse of the bridge occur because of the welding defects. The welding of low cost and high productivity is required without the welding defects. The pulsed TIG welding is inexpensive and capable of high‐quality welding. The electromagnetic force contributing to penetration changes because the transient response of arc temperature and iron vapor generated from anode occurs. However, the analysis of pulsed TIG welding with metal vapor has been elucidated only metal vapor concentration near anode with transient phenomenon and heat flux. Thus, the theoretical elucidation of penetration depth with control factor has not been researched. In this paper, the contribution of metal vapor mass at the periphery part of pulsed arc to the electromagnetic force in the weld pool is elucidated. As a result, the iron vapor mass at periphery part decreased with increasing the frequency. The iron vapor was stagnated at axial center within one cycle. The electromagnetic force to the penetration depth direction in weld pool increased at axial center. Therefore, the metal vapor mass at periphery part plays an important role for the electromagnetic force increment at axial center.     

Study of the effect of noble metal promotion in Ni-based catalyst for the Sabatier reaction

This paper reports the preparation and the evaluation of the performance of Ni-based powder catalysts with low nickel loading on the CO2 methanation reaction, that is an integral part of the power-to-gas (PtG) technology. CeO₂, CeZrO₄ and CeO₂/SiO₂ were selected as possible supports, and the results of this first screening pointed out that 10%Ni/CeO₂ catalyst could offer the best reaction performances because of ceria's peculiar characteristics. Moreover, the promotion of this promising formulation with the addition of a small amount of noble metals (Pt, Ru, Rh) was investigated, showing that platinum in particular can enhance the catalyst performances. A further study related to the noble metal loading pointed out that platinum and ruthenium have a different optimum loading condition: this result, together with the activity tests performed on monometallic formulations with only the noble metal, suggested that the two metals are able to catalyse two different reactions, thus promoting two different reaction mechanisms.     

Synthesis and characterization of a novel Ca-alginate-biochar composite as efficient zinc (Zn2+) adsorbent: Thermodynamics,process design,mass transfer and isotherm modeling

In this present work, Ca-alginate-biochar adsorbent has been synthesized, characterized and tested its effectiveness in the removal of aqueous phase Zn²⁺ metal. The removal efficiency was studied under various physicochemical process parameters. External mass transfer model, intraparticle diffusion model and pseudo-first-order and pseudo-second-order models were used to fit the experimental Zn²⁺ adoption kinetic results and to identify the mechanism of adsorption. The desorption studies indicate the possibilities of ion-exchange and physical–chemical adsorption of Zn^2+. The adsorption was best described by Langmuir isotherm model. Thermodynamic parameters suggested that the adsorption process becomes spontaneous, endothermic and irreversible in nature.     

Preparation of nanocrystalline nickel oxide from nickel hydroxide using spark plasma sintering and inverse Hall-Petch related densification

Nanocrystalline nickel oxide (NiO) was prepared from nickel hydroxide by Spark plasma sintering (SPS) and the mechanisms involved in the densification of NiO were studied. Reverse precipitated nickel hydroxide powders were SPS processed at 400, 600 and 700?°C with 70?MPa pressure. Pure NiO with 12?nm crystallite size formed after 400?°C sintering process. However NiO grains had grown to 18 and 38?nm after 600 and 700?°C sintering respectively. NiO pellets prepared using 600 and 700?°C SPS sintering schedules had relative densities of 83% and 94% respectively. Two displacement rate regimes were observed during densification of NiO in both 600 and 700?°C sintering processes. Decomposition of nickel hydroxide and particle sliding of NiO led to first displacement rate maximum while inverse Hall-Petch based plastic deformation facilitated densification during the constant second displacement rate regime. No densification occurred during sintering holding times indicating the limited role that diffusion played during densification.