40Cr钢表面低温气体碳、氮、氧多元共渗层的摩擦学性能

利用低温气体多元共渗技术将碳、氮、氧元素同时渗入40Cr钢表面形成改性层。分析了保温时间对渗层厚度的影响,研究了改性层的显微组织、厚度、结构、渗层硬度及干摩擦磨损性能。结果表明：经多元共渗后表面改性层由疏松层、白亮层和过渡层组成;白亮层的硬度最高,达到850HV,多元共渗后40Cr钢表面的耐磨性能显著提高。     

电火花涂层的特性和耐磨性研究

采用电火花表面强化设备,以YS2硬质合金作为强化电极在45钢表面涂覆形成一层合金强化涂层。用扫描电镜、X射线衍射仪和显微硬度计分析了电火花表面强化层形貌、性能和组织结构。在磨损试验机上对其耐磨性进行测试,同时利用扫描电镜对试样的磨损形貌进行观察分析。结果表明,获得了冶金结合的强化层,显著提高了基体的硬度和耐磨性。     

磷酸盐-氢氧化钾溶液中镁合金微弧氧化膜层结构和性能研究

在磷酸盐-氢氧化钾电解液中,利用微弧氧化技术在AM60B镁合金表面获得了氧化膜层。截面光学显微形貌与扫描电镜照片显示,该氧化膜层为一连续的整体,氧化膜与基体存在清晰的界面,界面附近无孔洞、裂纹等缺陷,而在氧化膜表面则分布着大量的微孔,并有微裂纹存在;EDS成分分析表明,膜层主要由Mg、Al元素（来自于基体）和P、O元素（来自于电解液）组成;X-射线衍射实验证明了微弧氧化处理在镁合金表面形成了一层以MgO为主要组成的氧化膜,但未检测到P的存在,由此说明P以非晶态的形成存在于膜层中。膜层截面硬度分布曲线和耐蚀性实验表明,膜层硬度随着膜层与界面距离的增加起初增大,在距离界面10μm处达到最大值为580HV,之后逐渐降低;基体与微弧氧化膜层在w（NaCl）=3．5％NaCl溶液中的极化腐蚀电流密度分别为198A／cm^2和3．54A／cm^2,说明微弧氧化膜的生成使镁舍金的耐蚀性能明显增强。     

Influence Exerted by Microhardness of Basic Minerals of Ferruginous Quartzites on the Technological Properties

The problem on microhardness is considered as reflection of genetic strength of ferruginous quartzites of the Mikhailovsky deposit and possibility of using these data to predict ore-preparation processes.     

Fe74Cr2Mo2Sn2P10Si4B4C2非晶合金的晶化过程和硬度变化

Fe74Cr2Mo2Sn2P10Si4B4C2是一种发现不久的块体非晶合金。用旋淬法制备了该合金的非晶带材,DSC测得玻璃转化温度Tg是750K,晶化温度Tx1是786K,Tx2是805K。将带材样品分别在不同保温温度和保温时间下退火,用XRD和DSC研究晶化时的相转变。Fe74Cr2Mo2Sn2P10Si484C2非晶合金的晶化过程为Am→Am＋α-Fe-α-Fe＋Fe3P＋Cr23C6＋Fe3C＋Fe3B＋Fe2B,晶化的两个阶段分别对应淬态样品DSC曲线上的两个放热峰。测试了不同退火条件下样品的显微维氏硬度,结果表明晶化使硬度升高,二次晶化时最高,达到HV1278。     

Densification and mechanical properties of mullite-SiC nanocomposites synthesized through sol-gel coated precursors

Mullite-SiC nanocomposites are synthesized by introducing surface modified sol-gel mullite coated SiC particles in the matrix and densification and associated microstructural features of such precursor are reported. Nanosize SiC (average size 180 nm) surface was first provided with a mullite precursor coating which was characterized by the X-ray analysis and TEM. An average coating thickness of 120 nm was obtained on the SiC particles. The green compacts obtained by cold isostatic pressing were sintered in the range 1500–1700°C under pressureless sintering in the N₂ atmosphere. The percentage of the theoretical sintered density decreases with increase in SiC content. A maximum sintered density of 97% was achieved for mullite-5 vol.% SiC. The fractograph of the sintered composite showed a highly dense, fine grained microstructure with the SiC particles uniformly distributed along the grains as well as at the grain boundaries inside the mullite. The Vicker’s microhardness of mullite-5 vol.% SiC composite was measured as 1320 kg/mm² under an applied indentation load of 500 g. This value gradually decreased with an increase in SiC content.     

磨削对不同温度回火钢铁材料微观结构的影响

对淬火和不同温度回火处理的37SiMnCrNiMoV超高强度钢和60Si2Mn弹簧钢的电解抛光表面和磨削表面的X射线衍射线的半高宽和显微硬度进行测量,并通过线形分析得到了两种表面的亚晶粒尺寸和微观应变。结果表明,随着回火温度的升高,电解抛光表面的半高宽和显微硬度均逐渐减小。比起电解抛光表面,高温回火试样磨削表面的亚晶粒尺寸减小、微观应变增大,使得其半高宽和显微硬度都增大了,它说明磨削表面得到了加工硬化。而低温回火试样磨削表面的亚晶粒尺寸减小,但微观应变也减小了,其显微硬度增大,半高宽却减小了。200℃回火37SiMnCrNiMoV钢磨削表面的屈服强度比电解抛光表面的高出约400MPa。显微硬度和屈服强度的提高说明磨削也使低温回火试样磨削表面得到加工硬化,其微观应变和半高宽的减小是异常的。文中讨论了这种异常减小的机制。     

钢复合渗硼层的组织结构及显微硬度

分析并系统研究了合金元素对复合渗硼层宏观组织,相成分及显微硬度的影响,结果表明,合金元素使Ｆｅ－Ｂ相图上的共晶点移动,从而改变复合渗硼层中高硬度硼化物和低硬度共晶体的相对含量。复合渗硼层的显微硬度比渗硼层的高０．５－１倍。     

吸热式可控气氛多用炉稀土渗碳

本文首次实现了在吸热式可控气氛多用炉中进行稀土渗碳。结果表明,９００℃稀土渗碳可使渗层增加３４．８％,较原工艺（９３０℃渗碳）渗层增加１４．１％,表层组织、表面硬度及耐磨性优于原工艺。     

中镍铬无限冷硬铸铁轧辊激光表面强化

本文采用在铸铁轧辊表面上激光熔化预置的合金粉末来改善铸铁轧辊的表面性能.使用金相、扫描电镜和显微硬度计对激光熔化区的显微组织和硬度进行了测试表征.结果表明,激光熔化区与基体形成了冶金结合.由于激光的快速加热和快速冷却造成熔化区的组织细化.激光处理区的硬度由于晶粒细小和强化相的存在而得到提高.经450℃×48h高温回火处理后,激光熔化区的硬度几乎不发生改变.