庞磁电阻La0.8Sr0.2MnO3薄膜的微结构研究

利用激光分子束外延方法在(001)SrTiO3衬底上制备庞磁电阻La0.8Sr0.2MnO3薄膜.发现高密度、尺度均匀的纳米聚集物弥散地分布在La0.8Sr0.2MnO3薄膜中.Z衬度像、EDS及电子衍射综合分析表明,这些纳米聚集物的内部成分出现起伏,主要特征是富Mn贫La,Mn/La的比值在其核心处达到极大值,形成立方结构的第二相MnO.LSMO薄膜由两种正交结构的取向畴组成.MnO与畴1的取向关系为[101]LSMO,1//[100]MnO和(010)LSMO,1//(010)MnO;与畴2的关系为[101]LSMO,2//[100]MnO和(010)LSMO,2//(001)MnO.在LSMO/STO外延体系中,还观察到大量的失配位错.失配位错的类型分为刃型失配位错,位错线沿<100>方向;螺型失配位错,位错线沿<110>方向.刃型位错是基中原有位错在薄膜生长过程中沿生长表面的扩展造成的;螺型失配位错的形成与降温过程中LSMO正交结构的取向畴的形成有关.     

SiO_2:nm-Ag的制备及其结构特性

采用溶胶–凝胶法制备了掺纳米银的二氧化硅(SiO2:nm-Ag)微粉,并探讨其形成机理。用TG-DTA、XRD和TEM研究了微粉的结构特性及其影响因素。结果表明,通过控制制备条件和退火温度可以得到不同结构的SiO2:nm-Ag微粉。干凝胶研磨后在500℃退火,得到的微粉中SiO2主要以非晶硅藻土形式出现,银簇细小而均匀;在900℃退火时得到的微粉中,SiO2主要以低温方石英形式出现,银簇较大且分散。     

纳米ZnO掺杂压敏电阻电位梯度与显微组织研究

在制备ZnO压敏电阻的原料中加入纳米级ZnO粉料，研究了纳米级粉料对ZnO压敏电阻的压敏电位梯度的影响，并对其微观组织进行了分析研究，从理论上探讨了纳米ZnO影响ZnO压敏电阻压敏电位梯度与组织的机理．研究结果表明，压敏电阻中加入纳米ZnO后，其压敏电位梯度显著提高，纳米ZnO(质量分数)在0-30%的成分范围内，随着纳米ZnO含量的增加，ZnO压敏电阻的压敏电位梯度明显提高．其原因是纳米ZnO加入到ZnO压敏电阻中，使晶粒尺寸减小所致．     

纳米自组装催化剂渣油加氢脱残炭性能

根据纳米自组装机理,以γ-Al_2O_3为载体,Mo-Ni为活性组分,制备了正向胶束法和反应胶束法Mo-Ni纳米自组装催化剂。结果表明:以残炭质量分数为4.78%的渣油为原料,在Mo/Ni(质量比)为6∶1的条件下,当精制催化剂和裂化催化剂活性组分负载质量分数分别为30%,25%时,催化剂的残炭脱除效果为最佳;将正向胶束法制备的精制和裂化催化剂复配使用,在反应压力为14 MPa,体积空速为0.20 h~(-1),反应温度为350℃,氢气/原料油(体积比)为850的最佳条件下,渣油加氢脱残炭率最高达到53.82%。     

碳材料在电化学催化还原CO2领域的应用

CO2电化学催化还原反应(CERR)是一种潜在的CO2转化方法,可以将CO2还原为高附加值的化工产品和化学燃料,实现温室气体的高效清洁利用,对解决能源危机与环境问题均具有十分重要的意义。CERR中催化剂的性质是决定和控制反应活性、选择性和稳定性的主要因素。与金属催化剂相比,非金属催化剂(碳材料)由于其具有组成可控、能量效率高和稳定性优异等特点,而备受关注。笔者总结了近几年CERR杂原子掺杂碳基催化剂的研究进展,讨论了杂原子掺杂碳材料的催化性能,及其在CERR中的催化活性中心和相关机理,总结了杂原子掺杂碳基催化剂的发展方向。     

纳米t-ZrO_2的制备及交联胍胶压裂液的研究

以油水界面法合成纳米二氧化锆交联剂,采用SEM、FTIR和紫外-可见漫反射光谱对合成的纳米二氧化锆进行表征,通过单因素实验考察了温度、时间等因素对纳米四方型二氧化锆(t-ZrO_2)合成的影响,将合成的纳米二氧化锆配成1.5%(w)分散液,按1.5%(φ)的体积比交联0.6%(w)羟丙基胍胶形成交联冻胶,对形成的交联冻胶进行表征及性能测试。实验结果表明,纳米t-ZrO_2的最佳制备条件为100℃、24 h、十二烷基硫酸钠为表面活性剂、环己烷为油相、矿化剂为4 mol/L氢氧化钠溶液;制得纳米二氧化锆为t-ZrO_2,表面具有大量的羟基;形成的交联冻胶具有良好的挑挂性和耐温耐性,在100℃,170 s~-1)的条件下剪切120 min,冻胶压裂液体系黏度保持在100 mPa·s左右,破胶性、残渣含量和悬砂性均满足工作要求。     

The roles of nitrogen,phosphorus and Potassium in the production of sugarcane in South Africa

The amounts of N and K fertilizers used in the South African sugar industry have increased dramatically in the past four decades, due partly to an increase in the area under sugarcane but also to large increases in the amounts of N and K fertilizers applied per hectare. There has also been an increase in the amount of P fertilizer used but this has been more gradual. The main fertilizer carriers for cane and their relative efficiency are discussed. During this period there has been considerable research into the nutrient requirements of sugarcane. Correlations established between soil and leaf analysis and crop responses to N, P and K fertilizers, and their effects on cane quality, are reviewed. While fertilizer recommendations based on soil and leaf analysis have provided a useful guide for determining the nutrient requirements of cane, they are continually being modified in the light of current research.     

纳米燃速催化剂的研究进展

燃速催化剂是固体推进剂的必备部分,用来调节弹道性能,提高燃烧性能,为增加推进剂的能量水平、降低特征信号,利用纳米技术提高燃速催化剂的催化效率并减少其用量是近年来燃速催化剂领域的主要研究方向之一。综述了近年来纳米燃速催化剂在制备方法及应用方面的研究进展,指出存在的问题和改进措施,并对其应用前景进行展望。     

SnO2纳米材料制备技术的研究进展

综述了SnO2纳米材料制备技术的研究进展,报道了一种制备纳米纤维的新方法——热爆形变合成法,讨论了用该方法制备纳米纤维的基本条件。采用该方法制备出了SnO2纳米纤维,并进行了SEM和XRD分析。结果表明,SnO2纤维的直径约20-100nm,其X-射线衍射谱与标准的SnO2衍射谱完全一致。与其它方法相比,热爆形变合成法具有设备简单、操作方便、生产率高、产物无团聚等优点,稍加研磨就可获得长度不同的短纤维。但是,反应过程难以控制,这是热爆形变合成法的主要缺点。     

纳米复合含能材料的研究进展

对纳米复合材料的研究进展进行了综述,例举多种纳米复合材料的制备方法： sol-gel法、溶剂/非溶剂法、高能研磨法、多孔金属/填充物复合法.对这些制备方法及制品的性能进行了分析,认为纳米复合材料提供了研究含能材料的新角度,改进了纳米粉体含能材料储存使用过程的安全性,减轻了粒子团聚现象,有利于充分发挥材料的纳米特性.纳米复合含能材料的制备技术、制备工艺参数及制品结构对其性能的影响规律研究还处在探索阶段,今后还需理论和实践两个方面进行更加深入地分析、探讨.