纳米技术在涂料中的产业化应用

介绍了国内外纳米涂料的现状及其产业化进展。     

钛掺杂硅胶块体吸附剂

以陶瓷纤维纸片为基材,顺次经水玻璃、酸性钛盐溶液浸渍共沉淀制得新型陶瓷基钛掺杂硅胶块体吸附剂.多孔介质表面分析显示:掺杂硅胶孔径在0.5～6 nm范围,以中孔为主.Fourier变换红外谱在波数954 cm 1处的特征吸收峰表明吸附剂中形成了Si-O-Ti键.根据掺杂前后固体魔角核磁共振硅谱中硅原子化学位移的变化(向高场方向移动)及X射线光电子能谱中各原子结合能的变化(Ti2p3/2的结合能随钛含量的增加而增加,而Si2p,O1s的结合能则呈相反趋势)进一步表明:钛原子替代硅原子进入硅胶网络.热重分析及烧结实验结果显示:钛掺杂吸附剂具有更好的热稳定性.新型吸附剂优异的吸附性能除了与其高的比表面积相关外,还与Ti-O键对水分子的亲合力紧密相关,其耐热性能增强与形成高热稳定性Ti-O Si键及材料表面导热性能提高有关.     

Synthesis and property of nanosized palladium catalysts protected by chitosan/silica

A chitosan (CTN)/silica‐supported nanosized palladium catalyst was obtained from a silica‐supported chitosan palladium complex through a complex transition method. An adsorption model was employed to simplify the structure of the di‐supporter. It was indicated that when the polymer coil adsorbed on the silica surface with even a monolayer the catalytic activity would reach an optimum value, and different situations of the, nanosized palladium particles would cause a different catalysis. The molar ratio of the chitosan structure unit to the palladium would affect the metal's size, which therefore influenced its catalytic activity. The experimental results corresponded with the inferences. © 2002 Wiley Periodicals, Inc. J Appl Polym Sci 85: 989–994, 2002     

有机溶剂热生长技术制备硫族化合物及其光学特性的研究

以有机溶剂热生长技术(solvothermaltechnique)制备了半导体硫族化合物(CdS、ZnS、MoS2)等纳米颗粒,采用XRD、TEM等技术对其结构进行表征.以ITO导电玻璃以及导电聚合物(PANI、PPY)膜为基底,将纳米颗粒涂布其上并以PL法研究其光学特性,实验结果表明:经修饰后,材料的荧光发射位置发生显著的变化.     

超声波对沉淀二氧化硅的分散解聚研究

研究了超声波对沉淀二氧化硅的分散解聚效果，实验证明，当频率为40kHz，功率密度达到1．8W/cm^2时，沉淀二氧化硅浆料可以获得极佳的分解效果，二氧化硅聚集体小于77．6nm的颗粒数量达98．9％。     

纳米TiO2复合铁钛防锈颜料的研制及产业化进展

介绍了纳米TiO2复合铁钛防锈颜料的制备原理、工艺、技术指标;描述了铁钛防锈涂料的配方、性能检验和产业化进展情况.     

聚酰亚胺/二氧化硅杂化膜的制备与介电性能的研究

采用溶胶-凝胶法制备了BTDA-ODA聚酰亚胺/SiO2杂化膜,利用红外分光光度计（FTIR）、热重分析仪（TGA）和透射电镜（TEM）研究了杂化膜的微观结构和热性能,并对杂化膜的介电常数（e）和介电损耗（tand）随SiO2粒子含量和电场频率的变化进行了分析和讨论。结果表明：杂化膜的介电常数和介电损耗随SiO2粒子含量的增加而增大,随电场频率的升高而逐渐降低,用考虑到粒子的形状因素和两相间相互作用的EMT模型可以预测聚酰亚胺/SiO2杂化膜的介电常数。     

Solubility of Si3N4 in Liquid SiO2

The nitrogen solubility in the SiO₂-rich liquid in the metastable binary SiO₂-Si₃N₄ system has been determined by analytical TEM to be 1%–4% of N/(O + N) at 1973–2223 K. Analysis of the near edge structure of the electron energy loss peak indicates that nitrogen is incorporated into the silicate network rather than being present as molecular N₂. A regular solution model with a positive enthalpy of mixing for the liquid was used to match the data for the metastable solubility of N in the presence of crystalline Si₃N₄ and to adjust the computed phase diagram. The solubility of Si₃N₄ in fused SiO₂ is far less than reported in liquid silicates also containing Al, Mg, and/or Y. Apparently, these cations act as modifiers that break anion bridges in the silicate network and, thereby, allow further incorporation of Si₃N₄ without prohibitive amounts of network cross-linking. Finally, indications emerged regarding the diffuse nature of the Si₃N₄-SiO₂ interface that leads to amorphous regions of higher N content.     

高效乙烯聚合催化剂的制备——I．催化剂的制备规律

研究了新型含镁络合物的结构、性质及其用于制备高效乙烯聚合催化剂的制备规律。结果表明：将镁、有机醇以及不与镁发生“格式反应”的卤代烷相互作用可迅速发生反应形成新型含镁络合物溶液。该络合物在溶液中可析出结晶。具有特定的化学结构．可以均匀承载于多孔硅胶的孔隙中，负载TiCl4后制备出形态良好的球形高效乙烯集合催化剂。     

改性压实水泥抗压强度影响因素的研究

采用ＤＳＰ原理和压实技术相结合，掺加硅灰和ＣａＣＯ３等细颗粒矿物外加剂改变压实水泥材料基质。研究了成型压力、细粉掺量、养护制度等因素对压实水泥强度的影响。结果表明，掺加适量硅灰和提高成型压力可显著提高压实水泥的抗压强度，掺加ＣａＣＯ３对强度无明显影响；压实水泥存在最佳养护龄期，超过此龄期强度倒缩。