STRUCTURAL DETERMINATION OF TITANIUM-OXIDE NANOPARTICLES BY X-RAY ABSORPTION SPECTROSCOPY

As a potential application of titanium-oxide nanoparticles, it is extremely important to investigate a detailed picture of the surface and interior structural properties of nanocrystalline materials, such as rutile and anatase with diameters 7.0 and 4.5nm, respectively. X-ray absorption spectroscopy has been used to identify the local Ti environment and related electronic structure. We combine the experimental results at the Ti edge in both bulk and nano-crystals to determine the lattice distortion in terms of differently characteristic preedge features and the variation in the multiple-scattering region of X-ray absorption near-edge structure (XANES) spectra. The relationship between the transition peaks and the surface-to volume ratio is also discussed.     

相对压强对白炭黑氮吸附表面积测试稳定性的影响

研究相对压强对白炭黑氮吸附表面积测试稳定性的影响。结果表明:在相同液氮纯度、脱气温度、脱气时间、氮吸附点数量条件下,与相对压强范围为0.05~0.1时相比,相对压强范围为0.05~0.2时白炭黑的氮吸附表面积测量值偏低,且差值随氮吸附表面积的增大呈增大趋势;相对压强范围较小时,氮吸附表面积测试结果的线性相关因数较大,再现性较好,测试结果较稳定。     

阻燃OMMT/WPU纳米复合材料的制备及性能研究

采用端羟基聚丁二烯（HTPB）剥离层状有机蒙脱土（OMMT）为纳米片层,并与异佛尔酮二异氰酸酯（IPDI）、二羟甲基丙酸（DMPA）等单体通过原位聚合法制备了OMMT纳米片改性的水性聚氨酯（OWPU）纳米乳液及胶膜。利用小角XRD、TEM、DLS、EDS、TGA、LOI、CONE以及SEM对样品的结构和性能进行了表征。结果表明,HTPB剥离的OMMT纳米片的衬度均匀,完整性较好;改性后OWPU的乳液粒径增大,胶膜的弹性模量、热稳定性、抗熔滴性和阻燃性能均得到明显地改善,其中弹性模量可提高59.4%,热释放速率峰值可降低36.9%;燃烧炭渣表面形貌显示,瓦片状蒙脱土相互穿插形成了具有团簇结构的蒙脱土覆盖层。     

A replacement of traditional insulation refractory brick by a waste-derived lightweight refractory castable

Lightweight insulation refractories are essential for high-temperature performance to reduce energy consumption. This study investigates a new insulation material, that is, solid waste rice husk ash (RHA) derived lightweight refractory castable, replacing traditional insulation refractory brick. The RHA is generated after the burning of rice husk as biomass fuel. The RHA is used as an aggregate and alkali-extracted silica sol from RHA as a binder to fabricate the insulation castable. The nanosilica containing (~30 wt%) sol is employed to synthesize the refractory castable by varying the sol amount (2.5-12.5 wt% silica from sol). The castable specimens are cast by a vibro-caster and fired at 900-1200°C in a muffle furnace. The physic-mechanical and thermal conductivity (κ) of the castable is investigated. At 1100°C with 10 wt% dry sol retaining sample shows an excellent apparent porosity (~65%), low bulk density (~ 0.8 g/cm³), and κ (0.136 W/m k) with sustainable compressive strength (6 MPa). The acquired results are a good match with the literature (other wastes-derived insulation materials) and industrial (silica insulation brick) obtained data. These promising outcomes may inspire the refractory industries for using RHA as an aggregate and RHA extracted sol as a binder for making insulation castable.     

磷石膏提质降杂实验研究

磷石膏的综合利用对保护环境、促进企业可持续健康发展具有重要意义,但是磷石膏中的磷、氟、二氧化硅等杂质影响其利用。针对云南磷石膏中二氧化硅含量高的问题,采用正浮选工艺开展了磷石膏提质降杂的实验研究。通过单因素条件实验获得了合适的工艺参数：浮选温度为15 ℃、矿浆pH为2、十二胺用量为300 g/t。在此条件下,进行了“一粗二精”的正浮选开路流程实验,获得了二水石膏（CaSO₄·2H₂O）质量分数为97.5%、二氧化硅质量分数为1.17%的精矿,所得精矿达到了GB/T 23456—2018《磷石膏》一级品指标的要求;二水石膏回收率为98.58%、二氧化硅去除率为92.23%。通过正浮选不仅成功实现了二水石膏和二氧化硅的有效分离,而且磷石膏中的水溶磷和水溶氟也得到了有效去除,从而提高了磷石膏的品质。     

Studies on Preparation of Onion-like Fullerenes by Vacuum Heat-treatment

Onion-like Fullerenes were produced at high-temperature in vacuum. The morphology of the carbon nano onion-like fullerenes was examined and characterized by high-resolution transmission electron microscopy (HRTEM). It can be seen that the nano-sized, onion-like fullerenes possess high degree of graphization. The results suggested that the catalyst is the main factor affecting the size and yield of the fullerenes. The method is very promising for simple mass production.     

电弧炉炼钢碳化硅白渣工艺的脱氧与脱硫

理论计算和实践表明，在电弧炉上采用碳化硅代替硅铁粉和碳粉的白渣还原工艺，可强化钢的脱氧和脱硫效果；提高电炉炼钢生产效率；降低吨钢电耗和生产成本。并指出，采用喷吹技术会进一步改善该工艺的炼钢技术经济效果。     

中频炉酸性炉衬使用寿命的探讨

通过对炉衬材料的选择,作用机理及影响石英砂炉衬材料寿命的相关因素的阐述,说明了SD-T-A石英砂干振料可提高中频炉酸性炉衬使用寿命的原因.     

在纳米压入仪上进行悬臂梁法测量弹性模量的影响因素分析

对在纳米压入仪上进行悬臂梁法测量弹性模量的主要影响因素进行了综合分析,主要包括加载系统悬置弹簧刚度、压头压入、梁沿截面宽度方向挠曲、梁支座附加挠曲等影响。在考虑这些因素的基础上,得到了悬臂梁的有效挠度,利用有效挠度与载荷之间的关系,评价悬臂梁材料的弹性模量。对单晶硅(100)悬臂梁试样进行了实验,得到其弹性模量为155GPa±9.5%GPa,与参考文献值符合较好。表明在纳米压入仪上进行悬臂梁法测量,只有综合这些影响因素后,才能获得有效、准确的弹性模量测量结果。     

纳米CaCO3的表面改性研究

本文研究了纳米CaCO3表面改性的影响因素，确定了最优改性剂和改性条件，并运用沉降实验、透射电镜（TEM）等表征手段对粉体的改性效果进行了分析。结果表明：以月桂酸钠为改性剂，用量为10％，pH值为7，改性时间为1h时，改性后的纳米CaCO3的亲油化度达到85．1％，能较好地分散于环己烷和二甲苯中。