使用热反应型水溶性聚氨酯F-2840E提高纯棉织物"三防"效果

通过试验验证了热反应型水溶性聚氨酯F-2840E可提高“三防”（拒水、拒油、拒污）助剂TG-410H的使用性能，可提高TG-410H等部分有机氟系“三防”整理剂的耐洗性和“三防”效果，减少了“三防”助剂的用量．     

注入剖面五参数组合测井仪的改进

文章介绍了注入剖面五参数组合测井仪及对该仪器的改进与完善，特别是对流量计的结构进行了改进。流量计下端采用水阻尼和机械弹簧两种保护措施，有效地保护了涡轮；过芯加重改成通用加重下挂到涡轮流量计上，有效地减少了涡轮粘污，提高了组合测井仪的测井成功率。改进后测井成功率从60％提高到90％。同时。对数据处理与传输电路也进行了改进，新开发研制了PPM码数据传输体系，使组合仪耐温指标提高到175℃。     

Study on Preparation and Application of Ti／Si Complex Zeolite

A Ti/Si complex zeolite has been prepared. X-ray diffraction and infrared spectrometry study has shown that two structures, namely the ZSM-5 and MCM-41, exist in the sample. BET tests have revealed that the complex zeolite contains regular mesopores of 2.6 nm. Ultraviolet spectrometry analysis has shown that the Ti species exist in the zeolite skeleton in the form of tetra-coordinate valence. The Ti/Si complex zeolite (TS-1/Ti-MCM-41) has apparently improved catalytic activity with respect to the macromolecular organic compound oxidation as compared to individual components of either Ti or Si containing zeolites (TS-1 and Ti-MCM-41).     

长庆油田陕北区原油破乳剂的筛选和复配

实验考察了8种市售水溶性破乳荆对长庆油田陕北区有代表性的宝塔区、安塞和子长原油(均为低硫中间基-石蜡基原油)的脱水效果(加量100mg／L，脱水温度55℃，时间3h)。目前长庆采油一厂使用的YT-100和延炼集团使用的GT-940对这3种原油的脱水效果均较好，但对子长原油的脱水率不高，分别为69．7％和58．9％。在由所选性能较好的破乳刺组成的4种二元复配物中，GT-940 HQ96-1对3种原油的脱水效果均高于单剂，最佳配比分别为4：1，4：1，3：2；其余3种复配物则对原油有选择性，其中GT-940 YT-100相近(97．5％)；YT-100 HQ96-1仅能改善子长原油的脱水效果，配比为4：1时脱水率最高(76．4％)；SP-169 HQ96-1仅能改善宝塔区原油的脱水效果．配比3：2和2：3时脱水率最高(92．9％)。表5参6。     

Fabrication of Ormocer Containing Eu3＋ Ion and Their Optical Spectra

Eu3 ions were incorporated in sol and gel by a sol-gel processing using 3-glycidoxypropyltrimethoxysilane(CH2OCHCH2O(CH2)3Si(OCH3)3, GPTMS) and ethyl silicate (TEOS) as precursors. The basic chemical-physical properties such as DTA curve, FF-IR spectra and specific surface area were recorded. The characteristics of their optical spectra were measured and investigated. The results indicate that the emission intensity of Eu3 ion in ormocer is much higher and the global line width is wider than those in SiO2 gel. The relationship between the composition and structure of gels and the fluorescence intensity and width were discussed. The obtained ormocer shows good mechanical strength, which can be cut and polished in machine without broken.     

海洋钻井液有机物添加剂生物降解性评价

随着海洋石油的勘探开发，钻井液有机添加剂不可避免地进入海洋．因此在海洋勘探开发过程中应选择环保性能好，即生物降解性能好的有机物添加剂。用累计耗氧量法测定了海洋钻井液有机添加剂的生物降解性，研究评价了有机添加剂的生物降解规律和机理，探讨了有机物生物降解性同其化学结构的内在联系，为海洋勘探开发过程中选择环保性能好的有机物添加剂提供理论依据。总结实验结果发现：淀粉类(如DFD-140和FI-E1等)最容易生物降解；其次是纤维素类(如MV-CMC等)和烯类单体聚合物(如PAM和PHP)；而沥青类、两性离子类则难以生物降解，有的甚至对生物降解起抑制作用。     

剖析全板电镀镍金发白现象

简要介绍了全板电镀镍金加工过程中镀金面发白现象及改善措施。特别是针对高位发白(或粗糙)的产生原因和处理过程进行较为详细的描述,并对工艺在此处理过程中存在问题进行了简要剖析。     

The Fabrication and Characterization of Single‐Component Polymeric White‐Light‐Emitting Diodes

By using Ni⁰‐mediated polymerization, we have systematically synthesized a series of fluorene‐based copolymers composed of blue‐, green‐, and red‐light‐emitting comonomers with a view to producing polymers with white‐light emission. 2,7‐Dibromo‐9,9‐dihexylfluorene, {4‐(2‐[2,5‐dibromo‐4‐{2‐(4‐diphenylamino‐phenyl)‐vinyl}‐phenyl]‐vinyl)‐phenyl}‐diphenylamine (DTPA), and 2‐{2‐(2‐[4‐{bis(4‐bromo‐phenyl)amino}‐phenyl]‐vinyl)‐6‐tert‐butyl‐pyran‐4‐ylidene}‐malononitrile (TPDCM) were used as the blue‐, green‐, and red‐light‐emitting comonomers, respectively. It was found that the emission spectra of the resulting copolymers could easily be tuned by varying their DTPA and TPDCM content. Thus with the appropriate red/green/blue (RGB) unit ratio, we were able to obtain white‐light emission from these copolymers. A white‐light‐emitting diode using the polyfluorene copolymer containing 3 % green‐emitting DTPA and 2 % red‐emitting TPDCM (PG3R2) with a structure of indium tin oxide/poly(3,4‐ethylenedioxythiophene):poly(styrene sulfonic acid)/PG3R2/Ca/Al was found to exhibit a maximum brightness of 820 cd m^–2 at 11 V with Commission Internationale de L'Eclairage (CIE) coordinates of (0.33,0.35), which are close to the standard CIE coordinates for white‐light emission (0.33,0.33).