核孔膜生产线膜微孔制备工艺实验研究

本文介绍核孔膜生产线,重点描述了膜微孔制备工艺的实验研究。对于PC和PES膜,已得到32种工况下的扩孔公式,其形式为D=A+Bt,其中D——孔径,t——扩孔时间,A,B为特定工艺参数下的常数值.通过实验。得到了膜孔密度N与300~#核反应堆功率P、热柱辐照位置L的经验公式,即N=6.97×10~5×10~3×101~(1.18L).在本生产线上可生产最大幅面为3 140mm×240mm,孔径为0.04～10 μm的多系列多规格的核孔膜产品。     

化学镀SiCp／Ni－P复合镀层与基体结合强度及其影响因素

论述了ＳｉＣｐ／Ｎｉ－Ｐ复合镀层与钢基体的结合强度及其影响因素。复合镀层中离界面５μｍ厚度以内区域的组成及应力状态对镀层／基体的界面结合有决定性作用，在该区域以外ＳｉＣ粒径变化不影响镀层的结合强度。适当的热处理可提高界面结合力。     

Analysis of adhesive bonded composite lap joints with transverse stitching

The effect of transverse stitching on the stresses in the adhesive is investigated using an adhesive sandwich model with nonlinear adhesive properties and a transverse stitching model for adhesive bonded composite single-lap and double-lap joints. Numerical results indicate that, among all stitching parameters, thread pretension and stitch density have significant effect on the peel stresses in the adhesive; increase in the thread pretension and the stitch density leads to a decrease in peel stress in the adhesive, while an increase in other parameters generally results in a negligible reduction in peel stress. The effect of stitching was found to be negligible on the shear stresses in the adhesive. Thus it is concluded that stitching is effective for the joints where peel stresses are critical and ineffective for those where shear stresses are critical.     

ANALYSIS ON ROOM TEMPERATURE TENSILE STRENGTH OF δ-Al_2O_3, FIBER / Al-12Si COMPOSITE

对δ－Ａｌ２Ｏ３纤维／Ａｌ－１２Ｓｉ复合材料室温拉伸强度的分析表明，在实验条件下该复合材料存在δ－Ａｌ２Ｏ３纤维的最小体积分数Ｖｍｉｎ和临界体积分数Ｖｃｒｉｔ，并求出其基体强度δｍ和室温强度σｃ－δ－Ａｌ２Ｏ３纤维体积分数Ｖｆ直线方程及纤维的临界长度ｌｃ和复合材料的剪切应力τＰ确定复合材料的ＲＯＭ预测曲线，应首先判断σｍ是否等于未增强合金的强度σｕｍ才能得出正确的结论。     

用于多种组装技术的厚膜导体复合结构

厚膜导体Ｐｄ－Ａｇ／Ａｕ、Ｐｔ－Ｐｄ－Ａｕ／Ａｕ平面复合结构，Ｐｄ－Ａｇ／Ａｕ立体复合结构可使多种组装技术相互兼容。立体复合结构还可有效地降低导体线电阻，减少线损耗。而且，其超声键合性尤佳     

Use of inverse gas chromatography to quantify interactions in amine cured epoxy resins

Flory–Huggins interaction parameters, λ, were determined for a series of probes in an amine cured epoxy resin matrix (433–493 K) and its precursors (324–363 K) by inverse gas chromatography (IGC). Hildebrand–Scatchard theory was combined with Flory–Huggins theory in order to estimate infinte dilution solubility parameters (δ₂) for the matrix and its precursors at 298 K. It was shown that the value of the solubility parameter for the cured resin matrix lies between those of its precursors. Compared to the majority of published work, an unusual aspect of this application of IGC is that solubility parameters have been determined when the stationery phases are (i) small molecules and (ii) a highly crosslinked polymer. Moreover, all possible attempts have been made to ensure equilibrium conditions between probe and stationary phase, and compensation for asymmetry of peak profile has been applied in determining δ₂. The solubility parameters estimated by IGC are in good agreement with those calculated by other methods.     

Asymmetric alumina membranes electrochemically formed in oxalic acid solution

Alumina membranes were fabricated by anodizing aluminium metal in 0.15 M oxalic acid. The growth kinetics of the porous layer were investigated in the temperature range –1 to 16 °C using linear potential scans up to 70 V. The faradaic efficiencies of metal oxidation and of porous layer formation, determined by applying Faraday's law, were found to be independent of both temperature and electrical charge. SEM analysis of the metal-side and solution-side surfaces revealed different morphologies. After dissolution of the barrier layer in phosphoric acid, the metal-side surface showed circular pores whose size of about 90 nm was found to be uniform and independent of temperature. The pore population was also practically independent of temperature and a value of about 4 × 10¹³ pores m^–2 was determined. On the solution-side surface the presence of a deposit partially occluding the mouths of pores was observed. This coating could be removed by chemical etching in NaOH or thermal treatment at 870 °C, where decomposition of oxalate occurs. This supports the hypothesis that the deposit consists of an aluminium salt containing oxalate anions precipitated from the solution. The results show that it is possible to control the morphological characteristics of the anodic alumina membranes by careful choice of experimental conditions.     

n-Al2O3/Ni复合镀层的组织与滑动磨损性能研究

用电刷镀技术制得了镍基n-Al2O3复合镀层，并对镀层的滑动磨损性能进行了试验研究。纳米复合镀层的表面形貌比较细腻，镀层中纳米粒子分布均匀，与基质金属结合紧密。镀层显微硬度达到HV700，比快速镍镀层提高约40％。滑动磨损试验结果表明，随着纳米粒子含量的增大，镀层的耐磨性提高，摩擦系数也呈增大趋势；但当镀层中n-Al2O3粒子的超过2.56%(质量分数）时，镀层的耐磨性显著下降。纳米复合镀层的磨损机制以疲劳磨损为主，而快速镍底层以粘着磨损为主。     

混凝土芯砂石桩复合地基加固堤防软基试验研究

介绍了一种新型的地基处理方法——混凝土芯砂石桩复合地基法及其在水利防洪堤软基加固工程中的应用情况。通过现场原位观测和试验,研究了混凝土芯砂石桩复合地基固结变形、孔压消散、桩土应力分担及承载力特性,结果表明混凝土芯砂石桩强度高,排水固结能力强,能迅速提高桩间土强度和承载力,应用于水利堤防工程既能控制堤防深厚软基的工后沉降,又能提高堤防边坡的稳定性,推广应用前景良好。     

Development of sealing compositions with nanostructure iron-based fillers

The possibility of utilizing nanopowders of iron and Fe-Co-Ni produced bu a thermochemical method in the fabrication of sealing composition materials is investigated. It is established that such hermetic sealing composition materials function reliably under extremal conditions and guarantee elevated strength of adhesion to the surface of the metal and high corrosion and temperature stability. __________ Translated from Poroshkaya Metallurgiya, Nos. 3–4(448), pp. 112–117, March–April, 2006.