Influence of Ti Powder Characteristics on Combustion Synthesis of Porous NiTi Alloy

Porous NiTi shape memory alloy (SMA) is a novel biomedical material used for human hard tissue implant .The influence of elemental titanium powder characteristics such as powder morphology, particle size and specific surface area( SSA) on the minimal ignition temperature ,combustion temperature and final product of porous Ni-Ti SMA fabricated by combustion synthesis method was investigated in this paper by scanning electron microscopy (SEM) and laser diffraction.The preliminary data indicated that the titanium powder characteristics had a strong effect on combustion synthesis of porous NiTi SMA.     

Thermal Expansion Behavior of La1—xSrxMn1—yCoyO3—δ Perovskites

The thermal expansion behavior of La1-xSrxMn1-yCoyO3-δ (x=0.2-0.4, y=0.1-0.3) perovskites in air has been investigated. The average linear thermal expansion coefficients increased with increasing Sr content up to 40 mole fraction or Co content up to 30 mole fraction. The expansion is generally attributed to an increase in the average cation radius as some of the cations in the perovskite are reduced in valence when oxygen ions are removed from the structure.     

刚性棒状全芳香液晶聚酯的合成及性质的研究

以溴和苯基取代的对苯二甲酰氯及2，2′-二甲基联苯-4，4′-二甲酰氯作为单体，分别与甲基、叔丁基、苯基取代的对苯二酚经熔融缩聚反应，合成一类具有刚性棒状结构的全芳香液晶聚酯。聚酯的热性质以TGA、DSC，热台偏光显微镜研究。所有的聚酯均为热致性液晶，它们具有相对较低的转变温度，在普通的有机溶剂中具有较好的溶解性质。     

赋予针织服装个性魅力的女红工艺

将富于变化的女红工艺与单调的针织服装相结合，会使针织服装由平淡变为丰富，由呆板变为活泼。文章论述了在针织服装中运用女红图案、色彩、材料、针法的原理。     

Analytic methods for modeling longitudinal data from rolling therapy groups with membership turnover.

Interventions for a variety of emotional and behavioral problems are commonly delivered in the context of treatment groups, with many using rolling admission to sustain membership (i.e., admission, dropout, and discharge from group are perpetual and ongoing). The authors present an overview of the analytic challenges inherent in rolling group data and outline commonly used (but flawed) analytic and design approaches to addressing (or sidestepping) these issues. Moreover, the authors propose use of latent class pattern mixture models (LCPMMs) as a statistically and conceptually defensible approach for modeling treatment data from rolling groups. The LCPMM approach is illustrated with rolling group data from a group-based alcoholism pilot treatment trial (N = 128). Different inferences were made with regard to treatment efficacy under LCPMM vs. the commonly used standard group-clustered latent growth model (LGM); coupled with other preliminary findings in this area, inferences from LGMs may be overly liberal when applied to data from rolling groups. Continued work on data analytic difficulties in groups with membership turnover is critical for furthering the ecological validity of research on behavioral treatments. (PsycINFO Database Record (c) 2010 APA, all rights reserved)     

A novel technique to prepare LiNbO3 at low temperature

Fresh niobium hydroxide was first precipitated from NbF₅ solution using an aqueous ammonium hydroxide under basic conditions. Then a simple procedure of mixing lithium and niobium hydroxides together and heating at a low temperature (400 °C) produced pure ultrafine single phase LiNbO₃ (LN). In the literature, this is the lowest temperature so far reported on the formation of LN. The phase content and lattice parameters are determined by X-ray diffraction (XRD). The average particle size and morphology were studied by transmission electron microscopy (TEM).     

Effect of C/Ti ratio on the laser ignited self-propagating high-temperature synthesis reaction of Al-Ti-C system for fabricating TiC/Al composites

TiC/Al composite was successfully synthesized utilizing laser ignited self-propagating high-temperature synthesis (SHS) of Al-C-Ti system with the different C/Ti molar ratio. When the molar ratio of C to Ti is below 1:1 in the starting materials, in addition to fine TiC particulates, a large amount of Al₃Ti phase was found in the composites; however, when the molar ratio of C to Ti is 1:1 in the starting materials, the Al₃Ti phase was almost completely eliminated and the distribution of TiC particulates generally appeared to be more homogeneous throughout the products synthesized.     

Formation of mushroom-like ZnO microcrystals through a solution calcination process

Mushroom-like ZnO microcrystals have been prepared via a solution calcination route, using Zn(NO₃)₂ as Zn source in the absence of any surfactants, templates or catalysts. This is the first example to prepare mushroom-like crystals as semiconductors, which are expected to show particular physical properties. The ZnO products were investigated by X-ray powder diffraction (XRD), scanning electron microscopy (SEM), Raman spectroscopy and photoluminescence (PL) spectrum measurements. A suitable concentration of Zn(NO₃)₂ solution was important for the growth of the mushroom-like products. The reported synthetic procedure is straightforward and inexpensive, and thus can be readily adopted to produce large quantities of mushroom-like ZnO microcrystals.     

Characterization of two-phase nickel aluminides produced by pressure-assisted combustion synthesis

Two-phase (B2+L1₂) nickel aluminide intermetallic compounds were synthesized by the pressure-assisted volume combustion synthesis (CS). The production and characterization of the samples containing NiAl+Ni₃Al were investigated. Aluminum (99% pure, 15 μm) and carbonyl nickel (99.8 pure, 4-7 μm) powders were used. The production of intermetallic compound was carried out at 1050 °C under 150 MPa uniaxial pressure in open air atmosphere in an electrical resistance furnace for 60 min. The formation temperature of intermetallic compound was determined by differential scanning calorimeter (DSC) analysis, and exothermic temperature of powder mixture was determined as 653 °C. The characterization of samples was confirmed by optical microscope, SEM and XRD analysis. It was observed that the structure of compound has very low porosity and the formation of NiAl was completed successfully. The relative density of test materials measured according to Archimedes’ principle was 98.04%. The microhardness of test materials was about 351 HVN₁.