Investigation on interior moisture distribution inducing dielectric anisotropy of coals

Dielectric anisotropy phenomenon of coal was detectable by many dielectric measurements. The paper presented that it was attributed to coal interior moisture distribution. A new model describing interior moisture distribution was developed basing on microstructure observation of coal. In the model, coal interior moisture distribution was analyzed and simulated numerically, the relationship between interior moisture distribution and coal dielectric property was constructed, the character of the permittivity varying with moisture content had also been studied and coal dielectric anisotropy was deduced. Corresponding experiment results were well satisfied with the model analysis, demonstrating that the interior moisture content could cause coal dielectric anisotropy.     

Influence of the surface conditions on permeation in the deuterium–MANET system

The condition of the surfaces is of crucial importance for the deuterium permeation through materials. In this work a study of the surface constants for the adsorption (σk₁) and release (σk₂) of deuterium under different surface conditions on the martensitic steel DIN 1.4914 (MANET) has been carried out. The growth of an oxide surface layer (Cr₂O₃) of about 25–30 nm in a MANET sample, heat treated in an oxidizing environment, compared to the bare MANET that have a ‘natural' oxide of about 5 nm has provoked a reduction of both the permeation rate and the recombination coefficient (about 3 orders of magnitude). In addition, the permeation governing process has changed from diffusion-limited to surface-limited. The measurements of the permeation rate of deuterium were performed by a gas-phase permeation technique over the temperature range 574–746 K and for deuterium driving pressures in the range from 3 to 10⁵ Pa.     

Ultrasonic study of molecular association of poly(vinyl chloride) solution in tetrahydrofuran

Ultrasonic absorption, velocity, adiabatic compressibility, relaxation time and relaxation amplitude measurements are reported on poly(vinyl chloride) (PVC) solution in tetrahydrofuran (THF) using pulsed ultrasonic apparatus operating at 2 MHz and 313 K. Results show a linear increase of velocity. density, viscosity, absorption coefficient, relaxation time and relaxation amplitude values with the increase of PVC concentration in THF. In contrast the compressibility decreases with increasing PVC concentration. This suggests interaction between PVC and THF molecules.     

Tb0.3Dy0.7(Fe1-xAlx)1.95合金的结构、磁致伸缩性能和自旋重取向研究

本文系统研究了室温下Tb0.3Dy0.7(Fe1-xAlx)1.95(x=0,0.05,0.1,0.15,0.2,0.25,0.3,0.35)合金中金属Al替代Fe对晶体结构、磁致伸缩、内禀磁致伸缩、各向异性和自旋重取向的影响.结果发现,x＜0.4时,Tb0.3Dy0.7(Fe1-xAlx)1.95完全保持MgCl2立方Laves相结构,晶格常数a随Al含量x的增加而增大.磁致伸缩测量发现,随着替代量x的增多磁致伸缩减小,x＞0.15时超磁致伸缩效应消失;x＜0.15时磁致伸缩在低场下(H≤40kA/m)有小幅增加,高场下迅速减小,而且易趋于饱和,说明添加少量Al有助于减小磁晶各向异性.内禀磁致伸缩λ111随[111]替代量x的增加大幅度降低.穆斯堡尔效应表明,Tb0.3Dy0.7(Fe1-xAlx)1.95合金的易磁化方向随成份和温度在{110}面逐渐偏离了立方晶体的主对称轴,即自旋重取向.室温下,当x=0.15时,Tb0.3Dy0.7(Fe1-xAlx)1.95合金中出现了少量非磁性相;x＞0.15时,合金完全呈顺磁性.     

用攀枝花钛矿和云南钛矿冶炼钛渣工业试验研究

通过磁性测量和X-射线衍射研究了Gd2(Co，Al)17化合物的结构和磁晶各向异性。当x≤4时，样品具有菱方Th2znl7型结构，x=5时，具有六方CaCu5型结构。随着Al浓度增加，晶格常数和单胞体积单调增大，而居里温度和自发磁化强度近似线性地减小；在x≥l时，观察到Co亚点阵的磁晶各向异性变号，室温易磁化方向由易面转变为易轴，且易轴各向异性场和各向异性常数随Al原子浓度增加出现极大值；基于补偿温度(65K)下自由粉末颗粒的磁化曲线，导出了亚点阵间的分子场系数和Gd-co交换耦合常数，结果表明，Al原子对Gd-Co交换耦合作用的影响较小。根据Al原子在Co亚点阵4种晶位的择优占位，分析了磁晶各向异性的演变。     

NANO-MULTILAYERS WITH HIGH PERPENDICULAR ANISOTROPY FOR MAGNETIC RECORDING

(FePt/Ag)n nano-multilayers were deposited on MgO (100) single crystal with laser ablation and then subjected to annealing. FePt L1o grains with (001) texture and thus a large perpendicular magnetic anisotropy constant Ku of the order of 106 J/m3 were formed. A thick Ag layer is found to be favorable for decreasing the dispersion of the easy axis for magnetization. The measurement of time decay of magnetization gave rise to a small activation volume of the order of 10-25m3, showing the promising of being the recording medium for future high density perpendicular recording.     

Microstructures and Plastic Anisotropy of As—Cast Low Carbon Steel Strips

对比研究了低碳钢带铸材不同处理状态钢带和薄板铸坯中不同位置切片的组织特征、晶体学织构和15％工程应变条件下的塑性异向性．结果表明，带铸材试样中存在{111}与{114}特征织构，织构强度均较弱；铸坯切片中存在{111}与{001}特征织构，并且因局部凝固冷速不同存在明显的织构强度差异．两组低碳钢的法向异向性与平均晶粒尺寸的对数之间尽管均存在线性关系，但斜率明显不同．分析表明法向异向性的晶粒尺寸依存性与钢带中织构的强弱有关，由此提出了“有效织构强度比”的概念，从塑性变形理论的角度解释了微观组织对塑性异向性的影响．     

快淬非晶合金制备态磁各向异性研究SCIEI

本文详细研究了铁基、铁镍基和钴基非晶合金条带制备态的平面磁各问异性。测定了退火前后试样中各向异性的变化及各向异性常数K_(us)随温度的变化,得出K_(us)(T)∝M_s^2(T)关系,由此得出平面磁各向异性由应力各向异性和表面形状各向异性两部分组成。     

化合物TbMn6Sn6的磁性和磁相变

采用分子场理论模型对稀土-过渡族金属间化合物的磁性、自旋重取向相变和场诱导的一级磁相变进行了研究.从理论上计算了TbMn6Sn6的易磁化方向随温度的变化以及不同温度时的磁化曲线,描述了自旋重取向相变和场诱导的一级磁相变.基于单离子模型计算了Tb离子和化合物的一阶和二阶磁晶各向异性常数及其随温度的变化,得到了和实验数据基本一致的结果.结果表明:Mn次晶格和Tb次晶格磁晶各向异性能之间的相互竞争是导致自旋重取向相变的物理机制,而稀土离子的四阶晶场项对场诱导的一级磁相变产生很大的影响.     

Textures in high purity aluminum foils and AA3004 sheets

1　INTRODUCTIONWithincreasingdemandsofhighmaterials properties ,thetexturesinAlandAlalloysplaymoreandmoreimportantrole .Highpurityaluminumfoilsneedverystrongcubetexture ,whichwillfavorthe“channeletching”effectforhighvoltageelectrolyticcapacitors ,andAA30 0 4aluminumalloysheetsneedcertaincubetexturetosuppressthe 4 5°earingbehav iorresultingfromstrongrollingtexturecompo nents[1] .InAlandAlalloys ,heavycoldrollingwillresultinstrongβ fibertexturescomposedofthewellknownCu ({ 112 }〈111〉…