AZ31镁合金钨极交流氩弧焊焊缝气孔的研究

采用金相显微镜和扫描电镜对AZ31镁合金薄板在钨极交流氩弧焊时产生的气孔进行了研究,分析了气孔的形成原因,并提出了焊缝气孔的防止措施.试验结果表明:焊前彻底清除母材坡口、表面和焊丝表面的油污及氧化膜,采用较大的焊接电流和较高的焊接速度,选用合适的氩气流量,焊前预热等措施都能有效地防止焊缝中气孔的产生.     

Exploring thermal spray gray alumina coating pore network architecture by combining stereological protocols and impedance electrochemical spectroscopy

Complex multiscale pore network architecture characterized by multimodal pore size distribution and connectivity develops during the manufacture of ceramic thermal spray coatings from intra- and interlamellar cracks generated when each lamella spreads and solidifies to globular pores resulting from lamella stacking defects. This network significantly affects the coating properties and their in-service behaviors. De Hoff stereological analysis permits quantification of the three-dimensional (3D) distribution of spheroids (i.e., pores) from the determination of their two-dimensional (2D) distribution estimated by image analysis when analyzing the coating structure from a polished plane. Electrochemical impedance spectroscopy electrochemically examines a material surface by frequency variable current and potential and analyzes the complex impedance. When a coating covers the material surface, the electrolyte percolates through the more or less connected pore network to locally passivate the substrate. The resistive and capacitive characteristics of the equivalent electrical circuit will depend upon the connected pore network architecture. Both protocols were implemented to quantify thermal spray coating structures. Al₂O₃-13TiO₂ coatings were atmospherically plasma sprayed using several sets of power parameters, are current intensity, plasma gas total flow rate, and plasma gas composition in order to determine their effects on pore network architecture. Particle characteristics upon impact, especially their related dimensionless numbers, such as Reynolds, Weber, and Sommerfeld criteria, were also determined. Analyses permitted identification of (a) the major effects of power parameters upon pore architecture and (b) the related formation mechanisms. This article was originally published inBuilding on 100 Years of Success, Proceedings of the 2006 International Thermal Spray Conference (Seattle, WA), May 15–18, 2006, B.R. Marple, M.M. Hyland, Y.-Ch. Lau, R.S. Lima, and J. Voyer, Ed., ASM International, Materials Park, OH, 2006.     

100 MN双动铝挤压机主柱塞的机械加工工艺

介绍了国内首台万吨铝挤压机关键零部件主柱塞的加工工艺 ,以及在大型卧式车床上加工大直径、高光洁度阶梯深孔、盲孔的加工方法及工艺流程和所需工装设计等。     

硬质合金大规格顶锤成型工艺的研究

研究了压制成形过程硬质合金顶锤的制备工艺及工艺参数影响抗断裂强度的规律性,分析了冷等静压可得到理想压坯密度的理论基础。提出了大制品成型方法。     

飞机压力加油系统节流孔径优化控制策略研究

基于飞机地面压力加油系统管路模型，本文采用高级遗传算法（RGA）的排序选择及随机交换算法，在满足管路最大冲击压力及满油时间差的约束条件下，经全局搜索优化策略，得到优化后适应度最佳的节流孔径，试验研究的结果验证了该方法的可行性和有效性。     

原位STM研究钢筋在模拟混凝土孔溶液中腐蚀和缓蚀动态行为

应用STM原位观察在不同氯离子浓度和pH值以及加入缓蚀剂前后的模拟混凝土孔溶液中的钢筋表面微观形貌．在pH=12．40的混凝土模拟孔溶液中，钢筋表面趋向均一，钝化膜的薄弱部分得到强化；在含3．5％NaCl，pH=10．40的混凝土模拟孔溶液中由于局部腐蚀的发生，可观察到不规则的沉积物的形成、生长；LD-2型复合缓蚀剂能消除腐蚀活性，促使表面微观缺陷消亡，增加钝化膜的耐蚀能力．研究结果说明，STM可在纳米尺度上观察表面形貌变化，可成为原位研究钢筋在模拟混凝土孔溶液中腐蚀和缓蚀的动态行为的重要手段．     

大直径卷筒螺旋车床的改造

根据大直径卷筒螺旋的特点,将普通车床进行技术改造,增加了支撑底座、动力和运动传递部分,并根据螺距要求设计了内传动链.方便地实现了大直径卷筒螺旋的加工,既降低了成本,又充分利用了闲置的设备,取得良好的效果.     

双层药皮对不锈钢焊条气孔的影响

采用平板堆焊，高速摄影，波形分析，光学金相，扫描电镜能谱分析等测试方法，研究了双层药皮对钛钙型不锈钢焊条气孔的影响。试验结果表明，焊接冶金因素对气孔倾向有重要是熔渣的碱度也有明显的影响；熔渣的组织形貌与气孔敏感性存在一定对应关系；双层药皮焊条熔滴实现了渣壁过渡形态，具有控制焊缝增硅，改善氢的逸出条件作用，可以有效防止气孔产生。     

基于支持向量机的炒作微博识别方法

微博是舆论传播的中心和渠道,同时参与舆论的形成、发展与引导过程,其自媒体发布、意见领袖参与等因素在一定程度上造成了微博谣言、虚假炒作、社会动员等现象。针对炒作微博的传播特点,分析其群体的隐蔽策划现象,挖掘出普通微博和炒作微博在传播网络结构、转发增量统计等方面的差异。通过社交网站的应用程序接口对目标微博的所有评论、转发和点赞用户进行信息获取,构建该微博的传播网络,利用社团模块度、平均最短路径和网络直径这3个属性度量该网络的紧密程度,基于支持向量机对所抽取的微博进行分类,进而识别出炒作微博。实验结果表明,该方法对微博传播用户的属性信息依赖小以及传播网络结构特征敏感,并且具有较高的炒作微博识别准确率。