泡沫陶瓷的研制

泡沫陶瓷是一种新型的功能陶瓷材料。它具有独特的结构和性能，在工业中有着广泛的应用前景。泡沫陶瓷具有密度小、透气性高、耐高温、抗化学腐蚀等特性。本研究对用颗粒强化的氧化铝骨架合成泡沫陶瓷进行了分析。这种材料比其它多孔陶瓷材料具有更好的热化学性质。这种材料可以用有机海绵浸浆获得，然后烧去海绵，留下多孔陶瓷网。这种方法的优点是它包含了过程参数和陶瓷结构，同时合成物的烧结情况及其它条件的影响在文中也有阐述。     

负载型光催化剂降解有机废水的研究进展

光催化技术应用于有机废水处理具有广阔的前景，负载型光催化剂以其独特的优点日益受到人们的关注，因此，在简述普通未负载光催化剂降解有机废水的基础上，重点讨论负载型TiO2光催化剂的制备及应用。     

Preparation of solar selective absorbing CuO coating for medium temperature application

A new method of preparing CuO solar selective absorbing coating for medium temperature is presented. After pretreatment, brass was overlaid with CuO by chemical plating. The effects of reactant concentration, reaction temperature and reaction time on the absorptivity of CuO coating were investigated. The optimized condition of preparing CuO coating was obtained. The CuO coating was analyzed with X-ray photoelectron spectroscopy (XPS) and scanning electron microscopy (SEM). In order to prolong the period of use, the CuO coating was protected by TiO₂. The experiment shows that the TiO₂/CuO coating is more heat-resistant, acid-resistant, and wear resistant than CuO coating, without losing absorptivity markedly. The TiO₂ coating can reduce emissivity and protect the CuO coating. Translated from Journal of Tianjin University, 2006, 39(12): 1485–1489 [译自: 天津大学学报]     

低截留分子质量新型聚芳醚腈酮超滤膜的研制

以新型聚芳醚腈酮为膜材料 ,以N -甲基 - 2 -吡咯烷酮 (NMP)为溶剂 ,研究了聚合物浓度、添加剂种类及含量、凝胶浴温度等对超滤膜性能的影响。结果表明 ,聚合物质量分数以 1 2 %～ 1 3 %为合适的制膜浓度 ,以聚乙二醇PEG - 4 0 0为添加剂时获得了高截留率和高水通量的超滤膜。随着凝胶浴温度的升高 ,水通量明显增大 ,而截留率有所下降 ,而共聚物的浓度增加则有相反的效果。制得的超滤膜具有较低的截留分子量 (PEG- 2 0 0 0 ) ,将制得的超滤膜用于达旦黄、黄X-G等染料的分离 ,截留率均达 90 %以上     

纳米复相陶瓷的制备及性能研究进展综述

本文综述了纳米复相陶瓷的研究进展。介绍了纳米复相陶瓷的分类及制备技术,详细地阐述了纳米复相陶瓷的力学性能和微观结构,分析了提高其断裂强度、断裂韧性及抗蠕变性等性能的机理。     

PVC助剂的新进展

介绍了近年来聚氯乙烯助剂的研制、开发的现状和趋势。     

氯化聚氯乙烯的特性、制备及应用

氯化聚氯乙烯作为聚氯乙烯的化学改性产物，具有的特殊性能使其发展前景较为广阔。主要叙述了氯化聚氯乙烯所具备的优良性能、制备技术及应用领域。     

云母钛珠光颜料的研制

对钛盐的沉析特性、云母精制、颜料制备进行了探讨。研制出云母－钛珠光颜料，即二氧化钛包覆云母，包覆层明显，珠光效果显著。     

Au/ZnO and Au/Fe2O3 catalysts for CO oxidation at ambient temperature: comments on the effect of synthesis conditions on the preparation of high activity catalysts prepared by coprecipitation

The preparation of Au/ZnO and Au/Fe₂O₃ catalysts using two coprecipitation methods is investigated to determine the important factors that control the synthesis of high activity catalysts for the oxidation of carbon monoxide at ambient temperature. In particular, the factors involved in the preparation of catalysts that are active without the need for a calcination step are evaluated. The two preparation methods differ in the manner in which the pH is controlled during the precipitation, either constant pH throughout or variable pH in which the pH is raised from an initial low value to a defined end point. Non-calcined Au/ZnO catalysts prepared using both methods are very sensitive to pH and ageing time, and catalysts prepared at a maximum pH = 5 with a short ageing time (ca. 0–3 h) exhibit high activity. Catalysts prepared at higher pH give lower activity. However, all catalysts require a short operation period during which the oxidation activity increases. In contrast, the calcined catalysts are not particularly sensitive to the preparation conditions. Non-calcined Au/Fe₂O₃ catalysts exhibit high activity when prepared at pH ≥ 5. Calcined Au/Fe₂O₃ prepared using the controlled pH method retain high activity, whereas calcined catalysts prepared using the variable pH method are inactive. The study shows the immense sensitivity of the catalyst performance to the preparation methods. It is therefore not surprising that marked differences in the performance of supported Au catalysts for CO oxidation that are apparent in the extensive literature on this subject, particularly the effect of calcination, can be expected if the preparation parameters are not carefully controlled and reported.