Analysis of Intermetallic Phases Formed on Surface Vapor Oxidized H13 Hot Work Steels in Molten Aluminum

In this paper, the author dipped surface vapor oxidized H13 steel specimens into 700℃ molten aluminum liquid for a certain period of time. Analyze the intermetallic phases formed on the H13 samples surface with optical microscope and X-ray diffraction method. The observation of immersion test sample's cross-section shows that Fe3O4 film will protect die substrate from molten aluminum erosion. The identification of the intermetallic phases reveals that they consist of 2parts, which is named as the composite layer and the compact layer. Further investigations are made in order to know the phase constituents of the 2 layers, they are Al8Fe2Si (outer composite layer), (AlCuMg) and Al5Fe2 (compact layer),respectively. The experimental results show that on the same specimen, a convex surface with bigger radius of curvature is more likely to be molten and the melting loss speed is also faster than a flat and smooth surface. The thickness of compact layer on a smooth surface is much bigger than that of the convex surface. Therefore, the author supposes the compact layer is favorable in stabilizing the die surface material from further melting loss, as their formation on the die surface, the melting loss speed will decrease.     

Diffusion bonding between nickel-base superalloy K24 and heat-resisting steel 1Cr11Ni2W2MoV

IntroductionSLlperalloyandheat-resistingsteelarenowwidelyusedasstructurematerialsinaerospace,a\-lationalldshipbuildingindustries.Nickel-basesuperalloywasfirstlyrevealedasanengineeringmaterialduringtheearly1960swhenitwasrecognizedasbeingsuitableforllledium-temperaturegasturbinel'l.Now.nickel-basesuperalloyhasbeenpracticallyusedinhigheffectiveturbinestosatisfytheincreasingdemandsforhighertemperatureenvironmentsIZI.Insomeaerospaceengines,theimpellersshouldserveattemperatureof1000C~1100C,andala…     

Zinc Coated Steel/Epoxy Adhesive Systems: Investigation of the Interfacial Zone by FTIR Spectroscopy

The present study takes advantage of the ability of Fourier Transform Infrared Spectroscopy (FTIR) for the analysis of ultrathin organic films on metals. FTIR in the reflection mode (IRRAS) is used in order to study the interaction of ultrathin films of dicyandiamide (hardener of most one-pack epoxy resins) with various substrates, model ones such as gold or zinc and industrial ones such as steel and zinc-coated steels.

Pure zinc surfaces and, to a lesser extent, zinc-coated steels are shown to react with dicyandiamide after heating at 180°C, as evidenced by the frequency shift of the absorption band (at about 2200 cm^-1) characteristic for nitrile groups. As real systems consist of thick layers of a fully formulated adhesive cured onto a metallic substrate, the direct investigation of such a buried interphase is no longer possible by FTIR and by most of the known spectroscopies. Some mechanically tested specimens are then analysed, after failure, by FTIR microspectrometry. The spectra obtained, corresponding to the fracture initiation zone which is about 100 μm in diameter, advocate for the presence of an ultrathin layer of modified polymer still covering the substrate.     

广州新白云国际机场压型钢板锌加涂装工艺

列举了业主规定的压型钢板的涂装配套及膜厚要求,介绍了锌加的涂装工艺、安全与环保、质量检验。     

钢筋阻锈剂在工业厂房中的应用

介绍了钢筋阻锈剂的基本性能、使用范围和方法。     

嵌入式二维码数据无线多点传输系统设计

设计了一种基于FreeRTOS嵌入式操作系统的二维条码无线传输系统,描述了系统的软硬件实现方法和多点数据传输的链路控制机制。系统主控芯片采用通用的MCU芯片STM32,结合二维码扫描引擎和蓝牙传输模组实现多个扫描终端与基座间的数据传输。     

原材料价格波动下钢铁生产库存多期优化模型

考虑钢铁企业钢材生产受钢材需求和生产变动成本波动的双重影响,在预测基础上,建立钢材生产库存多期动态优化模型。由于模型涉及多种钢材及多个时段,属于大规模问题,求解困难,且为了避免粒子群算法陷入局部最优,提出采用模拟退火与粒子群组合智能算法对模型进行求解。最后通过钢铁企业L的案例,结果表明算法具有较强的收敛性和适用性,模型可用于解决钢铁企业多期生产实际问题。     

骨架材料对全钢载重子午线轮胎性能的影响

讨论骨架材料的规格、结构分布及工艺控制对全钢载重子午线轮胎性能的影响。胎体帘布采用带有外缠丝的 3 + 9+ 15× 0 2 2 + 0 15规格钢丝、胎体帘线密度在 45 0～ 65 0根·m- 1 范围内 (帘线直径大于 1 2mm)以及胎体反包端点在成品外轮廓曲线的第 2或 3条装配线上等措施均有利于保证胎体强度 ;合理设计带束层结构 ,端点与胎侧肩部花纹距离取 10mm左右有利于消除应力过度集中 ;采用钢丝增强带有利于提高胎圈刚性。     

陶瓷坯体增强剂聚丙烯酸钠在艺术瓷成形过程的应用

本文合成了一系列不同相对分子质量的聚丙烯酸钠,应用于艺术瓷的坯体中,研究了聚丙烯酸钠对艺术瓷坯体强度、变形率的影响,并对聚丙烯酸钠增强机理进行了探讨。结果表明:聚丙烯酸钠可有效地提高艺术瓷坯体的成形强度,减少了坯体的变形率,当增强剂c加入的质量分数为0.6%时,坯体的干燥强度增加率达167.5%,坯体的变形率从50%降低到10%。     

碳钢贮热水箱的模拟腐蚀试验及涂层耐蚀性能研究

碳钢贮热水箱长期在30～80°C温变的热水环境中工作,易受到热水及水中杂质的腐蚀。研究了不同温度下Q235钢在自来水及含100μg/mLNaCl的自来水中的腐蚀速率。对裸钢及其涂覆相同厚度的不同涂层──酚醛环氧(自制)、钛纳米聚合物和改性聚乙烯后在70°C自来水中的极化曲线进行了比较。采用动电位扫描极化曲线测量和电化学交流阻抗谱法(EIS)分别对涂覆不同涂层的Q235钢进行了耐蚀性能研究。结果表明,3种防腐涂层均具有较佳的抗热水性,耐蚀能力较强,适宜对Q235钢贮热水箱进行防护。