热轧带肋钢筋屈服不明显原因分析与探讨

针对涟钢热轧带肋钢筋的屈服不明显现象，从金属的金相组织、人工时效、自然时效、测试方法等方面着手，寻求各因素对钢筋力学性能的影响，并阐述了该异常组织的形成机理及相关因素，指出魏氏体、粒状贝氏体等的存在是造成带肋钢筋性能异常的主要原因，同时对部分屈服不明显的带肋钢筋判定提供了较为科学的依据。     

薄板坯连铸连轧工艺对铌微合金化高强度钢组织和性能的影响

首先建立薄板坯连铸连轧工艺的试验室模拟技术，并运用该模拟技术，研究薄板坯连铸连轧工艺(CSP)和传统板坯再加热工艺(TRP)两种工艺对铌微合金化高强度钢的显微组织和力学性能的影响。研究结果表明：CSP钢的晶粒细化效果不如TRP钢，两者的平均铁素体晶粒尺寸分别为8．17μm和6．30μm。在CSP试验钢板中铌的析出量较大，特别是在铁素体中细小颗粒的铌的析出物较多，沉淀强化效果较强。CSP试验钢的σ0.5和σb分别较TRP工艺低约40MPa和约25MPa，同时其低温冲击韧性较好，FATT温度较低。     

Influence of the Preheat Treatment on the Microstructure and Properties of X37CrMoV5-1 Steel

The technological properties of the hot-work tool steels depend on their microstructural quality induced by the production process and the heat treatment. One of the frequently applied methods to improve microstructure is preheat treatment. The treatment of carbonitriding X37CrMoV5-1 steel has been investigated in fluidized bed furnaces. Thickness and phase composition have been conducted using optical microscopy Neophot 32 and scanning microscopy, JEOL 5400, after etching in nital.     

高速线材生产的弹簧钢盘卷的表面脱碳分析

从金相角度对高线生产的弹簧钢盘卷的表面脱碳进行了分析，找出相关的影响因素，并针对实际情况提出了相应的改进方法。     

化学成分和固溶温度对1Cr17Mn9Ni4N不锈钢组织和性能的影响

为提高1Crl7Mn9Ni4N钢固溶处理后的力学性能(特别是钢的强度)，研究了化学成分及固溶处理温度对其组织和性能的影响。结果表明，1000—1125℃固溶处理后，该钢的组织为单相奥氏体。在标准成分范围内，随着镍、锰含量的增加，该钢的强度降低，塑性有所改善。氮明显提高该钢的强度。根据试验结果，每增加0．01％的氮钢的室温强度可提高大约5MPa，且塑性基本上不受影响。当合金成分(质量分数，％)控制在C0．08—0．12、Crl6．5—17．5、Ni3．5—4．2、Mn8．0—9．0、N0．22—0．28时，1Crl7Mn9Ni4N钢经1050—1100℃固溶处理后强度较高、塑性好，室温强度σ0．2和σb可分别达到400MPa和800MPa。     

VN合金在大规格角钢生产中的应用研究

大规格角钢主要用于铁塔制造和建筑结构中。唐钢过去用16Mn钢生产Q345级别角钢，因供轧化学成分范围较窄，供轧率偏低。通过加入V-Fe合金及VN合金进行微合金化，设计了16Mnv(N)钢种生产角钢，使角钢综合性能有显著提高。分析比较了16Mn、16MnV及16MnV(N)角钢的性能，认为在大规格高强度角钢生产中，用VN合金进行微合金化，其效果是最佳的。     

Austenitizing treatment influence on the electrochemical corrosion behavior of 0.3C-14Cr-3Mo martensitic stainless steel

Effects of austenitizing treatment temperatures on aqueous corrosion properties of martensitic stainless steels were investigated by electrochemical tests (potentiodynamic test, potentiostatic test and electrochemical impedance spectroscopy), and surface analyses (optical microscopy and XRD). The results of potentiodynamic test revealed that the breakdown potential increased with the increased austenitizing temperature, indicating increased relative resistance to initiation of localized corrosion. EIS measurements showed that MSS3 (1030 °C) exhibits larger polarization resistance value than MSS1 (970 °C) and MSS2 (1000 °C) at passive and breakdown states. This was caused by decreasing the amount of Cr-rich M₂₃C₆ carbide which acts as preferential sites for pitting corrosion.     

单壁纳米碳管/纳米铝基复合材料的增强效果

用半连续氢电弧法和活性氢等离子蒸发法分别制备出单壁纳米碳管(SWNTs)和纳米A1粉体，然后用提纯后的SWNTs和纳米A1粉体制备出SWNTs含量(质量分数)分别为0、2．5％、5．0％、7．5％和10.0％的单壁纳米碳管／纳米铝基块体复合材料．SWNTs对高强度纳米A1基体具有显著的增强作用，当SWNTs含量小于5．0％时，材料的硬度随着SWNTs含量的提高线性上升．其中5％SWNTs和纳米A1的复合增强效果最好，其硬度可达2.89GPa，大约是粗晶A1(0．15GPa)的20倍．当SWNTs含量超过5．0％时，增强效果开始缓慢的下降．讨论了单壁纳米碳管增强纳米铝基复合材料的强化机制．     

钢带试样位向及拉伸性能的探讨

从碳素结构钢热轧钢带各向异性的事实出发 ,阐述不同试样位向导致同一钢带不同的拉伸性能 ,因而影响钢带合格与否的判定。在全面考虑钢带和焊管标准的基础上 ,提出解决钢带判定的两种方法。同时 ,还对标准中存在的缺点作了说明 ,提出改进意见 ,供标准修订时参考。     

重轨钢非铝脱氧工艺研究

介绍了攀钢重轨钢非铝脱氧工艺，在满足钢中脆性夹杂物控制的前提下，采取“预脱氧＋终脱氧”的工艺，达到钢液脱氧良好，钢轨内部质量大幅提高，钢轨T[O],[Al]及氧化物夹杂评级完全满足200km/h高速铁路钢轨标准的要求。