日产1000t水泥熟料生产线的提产措施

通过对五级旋风筒下料管、回转窑转速、配料方案、物料稳定等四方面进行改进,达到提产目的。     

磁性旋转编码传感器的研制

本文介绍的两相输出磁性旋转编码器输出电压V_(p-p)=41mV(V_(cc)=5V),灵敏度为6.3μV/(A·m~(-1)),分辨率为400p/r.实验证明,磁鼓与磁阻传感器之间存在最佳间隙,当间距为1mm时,输出最大.     

运用高压旋喷建造土坝坝基灌浆盖板技术

地坝坝基进行帷幕灌浆时，由于坝基无混凝土盖板，不能进行裂隙冲洗，灌浆压力受到限制，因而灌浆效果有限。采用高压旋喷在坝基建造灌浆盖板，改善了灌浆条件，取得了良好的灌浆效果，并且有效地截断坝基表层的渗漏，减少了坝基的接触冲刷破坏，温缺口水库大坝灌浆试验的成功为坝基无混凝土盖板条件下灌浆和坝基防渗加固处理探索了一条新路子。     

提高φ139.7 mm套管开窗侧钻固井质量的途径

断块油气田区块碎、连片性差、死油区多,套管损坏严重,利用开窗侧钻技术可解决油田开发中套管损坏的难题.研究开窗侧钻井固井质量,对提高油气开发效果、延长油井的使用寿命、降低成本,具有重要意义.通过改进完井液及水泥浆性能并优选配方、采取套管扶正技术、尾管柱优化设计、环空加回压技术、裸眼段扩孔技术、套管旋转固井技术等,解决φ139.7 mm套管开窗侧钻固井质量问题.中原油田自2000年全面实施套管开窗侧钻技术以来,完井固井工艺得到了完善,取得了较好的效果,累计施工267口井,成功率98.5%,井身质量和固井质量优良率均超过80%.累计增油约16×104t,经济效益显著.     

回转窑中心线偏差动态测量新法

针对现有回转窑动态测量方法存在测量基准不可靠,测量误差大等问题,提出建立横梁实体水平基准,动态测量水泥回转窑筒体中心线偏差的新方法。采用新方法设计的测量系统由全站仪、在线直径测量组件、托架组件、标定过的水平标尺和数据采集器等软硬件组成。通过架设水平基准横梁,由左、右托轮中心和轮带中心建立三角形模型,用全站仪间接测得回转窑中心线的水平和竖直偏差。经现场实地测量调试:新方法研制的测量系统稳定可靠,精度达到0.5 mm以内,测量数据与现场窑体运转状态反映一致。     

贵州天柱重晶石回转窑还原焙烧生产工艺研究

中国重晶石资源储量丰富,为科学合理利用,避免重晶石开发过程中浪费,采用?3.2 m×60 m回转窑还原焙烧处理贵州天柱重晶石,考察了焙烧温度、抛煤对重晶石还原效果的影响。结果表明,当高温区温度为1 050~1 200 ℃、窑尾温度为500~600 ℃、窑头温度为750~850 ℃、回转窑转速为0.20~0.40 r/min、处理量为15~20 t/h、吨矿耗煤为191.64 kg时,获得粗钡中硫化钡质量分数为70.5%、粗钡浸出率为91.3%的良好指标,焙烧矿石及浸出考核指标均合格,对合理利用中国储量巨大的重晶石矿资源具有重要的现实意义。     

Ti-26高强钛合金斜轧穿孔工艺研究

研究了Ti-26高强钛合金斜轧穿孔制备管坯工艺。测试了穿制的Ti-26合金管坯的力学性能，用金相显微镜观察了管坯的显微组织，用扫描电镜分析了拉伸断口的形貌。结果表明，采用斜轧穿孔方式完全可以制备Ti-26高强钛合金管坯；在1050℃下，选择合适的轧辊转速和前进角可顺利穿制Ti-26高强钛合金管坯，其管坯的强度为815MPa，延伸率达到13％，断面收缩率达到45％，晶粒度按ASTME标准为6级，比穿孔前细化，断口呈明显的塑性断口，加工管材无需热处理可以直接进行轧制，道次加工率可达45．8％。     

回转窑窑壁非稳态传热模型及窑皮厚度优化

烟气、料床、窑壁是回转窑传热过程的三要素,在确定这三要素之间传热量的基础上,建立了回转窑窑壁非稳态传热数学模型。对中铝河南分公司2号窑窑壁的非稳态传热过程进行了数值计算。结果表明:窑体旋转一周,烧成带窑壁内表面温度将在1 232~1 334℃变化,这易导致窑壁热疲劳破坏;窑皮越厚,窑壁的径向温度梯度越小,热应力越低;将烧成带窑皮厚度控制在252 mm,可使烧成带窑壁外表面温度维持在200℃。     

AI-Li/SiCp composites and Ti-AI alloy powders and coatings prepared by a plasma spray atomization (PSA) technique

There has been increasing use of Al-Li alloys in the aerospace industry, due mainly to the low density and high elastic modulus of this material. However, the problem of low ductility and fracture toughness of this material has limited its present application to only weight- and stiffness-critical components. Development of Al-Li/ceramic composites is currently being investigated to enhance the service capabilities of this material. The Ti-Al alloy is also of interest to aerospace-type applications, engine components in particular, due to its attractive high-temperature properties. Preparation of fine powders by plasma melting of composite feedstock and coatings formed by plasma spraying was carried out to examine the effect of spray parameters on the microstructure and properties of these materials. Characterization of the powders and coatings was performed using the scanning electron microscope and image analyzer. Examination of the plasma-sprayed powders and coatings has shown that in the Al-Li/SiC composite there is melting of both materials to form a single composite particle. The SiC reinforcement was in the submicron range and contributed to additional strengthening of the composite body, which was formed by a cold isostatic press and consolidated by hot extrusion or hot forging processes. The plasma-sprayed Ti-Al powder showed four categories of microstructures: featureless, dendritic, cellular, and martensite-like.     

回转窑传热模型与数值模拟

对回转窑内传热过程进行了分析 ,在已有研究基础上归纳了各项换热系数的关联式 ,尤其结合热渗透模型完善了回转壁面与料床之间传热机制的研究 ,并提出通用的计算关联式。进而提出了内热式炉型的一维轴向传热模型 ,并根据已发表的试验数据验证了该模型和各换热系数的适用性。计算表明在窑内低温段 ,物料的受热主要来自其覆盖的回转壁面对其加热 ;而在高温段 ,气体的辐射热量成为加热料床的主要热源。此外 ,由物料进口端沿轴向窑壁散热增大 ,在窑内高温段窑壁的散热甚至高于物料吸热量 ,因此在回转反应器的设计中应充分考虑窑壁散热造成的热效率降低并采取相应措施。