Oxygen transport,thermal and electrochemical properties of NdBa0.5Sr0.5Co2O5+δ cathode for SOFCs

In this study, the crystal structure, thermal, oxygen transport, electrical conductivity and electrochemical properties of the perovskite NdBa_0.5Sr_0.5Co₂O_5+δ (NBSC55) are investigated. In the temperature range of 250 °C–350 °C, the weight loss upon heating was due to a partial loss of lattice oxygen and along with a reduction of Co⁴⁺ to Co³⁺. The tend of weight-loss slows down as temperature increased above 350 °C indicating a reduction of Co³⁺ to Co²⁺ during this stage. The oxygen migration is dominated by surface exchange process at high temperature range (650-800 °C); however, the bulk diffusion process prevails at low temperature range (500–600 °C). For long-term testing, the polarization resistance of NBSC55 increases gradually form 3.13 Ω cm² for 2 h to 3.34 Ω cm² for 96 h at 600 °C and an increasing-rate for polarization resistance is around 0.22% h^?1. The power density of the single cell with NBSC55 cathode reached 341 mW cm^?2 at 800 °C.     

Effects of corrosion in liquid fluoride salt on the tensile strength of domestic SiC fibers

The relationship between the tensile strength of corroded domestic second-generation (2ed-gen) SiC fibers at various temperatures for 500 h in 46.5LiF-11.5NaF-42.0KF (mol. %) eutectic salt and the typical microstructure was studied. Weibull theory was used to analyze the critical defects that caused the tensile fracture, and the microstructure of fibers before and after corrosion was characterized. It is concluded that the decrease of tensile strength after corrosion at 800 °C is caused by the surface injury of fibers, which led to the shift of critical defects from the internal defects of virgin fibers to surface defects. Moreover, corrosion at higher temperature accelerates the corrosion process and dissolve the surface O-contained layer thoroughly. This shifts the critical defects back to the internal defects and will be helpful for the recovery of tensile strength of corroded fibers at the higher temperature.     

Impact assessment of reservoir desiltation measures for downstream riverbed migration in climate change: A case study in northern Taiwan

Typhoon Aere in 2004 induced severe sedimentation and loss of storage capacity of the Shihmen Reservoir in northern Taiwan. The resulting dramatic increase in the turbidity of the water seriously affected the water supply. To effectively maintain the stability of the water supply and maintain the reservoir’s storage capacity, the government of Taiwan began to plan and construct a series of improvement measures, such as a sediment flushing tunnel, the JhongJhuang Bank-Side Reservoir, and the Amuping Desilting Tunnel. However, previous studies only focused on the impact of the sediment flushing tunnel and the Amuping Desilting Tunnel on the downstream riverbed, and did not consider the possibility of increasing sediment discharge after the completion of the JhongJhuang Bank-Side Reservoir. In addition, climate change will cause the intensity of extreme rainfall to increase enormously in the future. That rainfall and extra sediment flushing will challenge the existing flood prevention facilities. Therefore, this study considered that the JhongJhuang Bank-Side Reservoir will increase sediment discharge of the Shihmen Reservoir, and used dynamical downscaling extreme typhoon data of climate change under the RCP 8.5 scenario to explore the flood prevention and riverbed migration of the main channels of the Dahan and Tamsui Rivers in the future. We used the rainfall–runoff model of Hydrologic Modeling System to simulate rainfall and runoff, and used the hydraulic and sediment transport model of CCHE1D to holistically simulate flood events and consequent river scouring and deposition behaviors. Our results showed that the projected peak discharge during the late 21st century (2075 to 2099) will be at least 50% higher than that during the baseline (1979 to 2003) period. In terms of flood prevention, the potential of overbank flooding will increase in the downstream area, and the trend of long-term change in the riverbed will be dominated by degradation (-0.489 ± 0.743 m) in the future. The improvement measures will have a limited impact on riverbed migration (0.011 ± 0.094 m) in the Dahan and Tamsui Rivers. After the operation of the JhongJhuang Bank-Side Reservoir, the Shihmen Reservoir is expected to increase the sediment discharge ratio by 70% during floods, and it will not cause excessive water turbidity that may affect downstream water supply.     

Simulation studies on a rotating ring disk electrode: Effects of ionic migration with kinetic complication-disk results

In continuation to my previous work (Guha S. AIChE J. 2013;59(4):1390-1399), in this work, effects of ionic migration are evaluated for disk region of a rotating ring disk electrode system by numerically solving complex differential equations, developed for mass transfer along with kinetic complication in presence of ionic migration under limiting current condition. The system for simulation is 0.01 M Fe₂(SO₄)₃ solution with H₂SO₄ as supporting electrolyte. Simulation cases are presence and absence of ionic migration with kinetic complication (oxidation of Fe²⁺ to Fe³⁺ under O₂ pressure). Results show that concentration boundary layer thickness of reactant Fe³⁺ reduces appreciably and steady-state disk current reduces substantially in presence of migration. Simulated steady-state disk current in absence of migration case agrees well with published data. Results indicate higher Fe²⁺ concentration in presence of migration and thereby higher rate of oxidation of Fe²⁺ to Fe³⁺ at all rate constant values.     

Evolution of Local Structural Ordering and Chemical Distribution upon Delithiation of a Rock Salt–Structured Li1.3Ta0.3Mn0.4O2 Cathode

Lithium‐rich disordered rock‐salt oxides have attracted great interest owing to their promising performance as Li‐ion battery cathodes. While experimental and theoretical efforts are critical in advancing this class of materials, a fundamental understanding of key property changes upon Li extraction is largely missing. In the present study, single‐crystal synthesis of a new disordered rock‐salt cathode material, Li_1.3Ta_0.3Mn_0.4O₂ (LTMO), and its use as a model compound to investigate Li concentration–driven evolution of local cationic ordering, charge compensation, and chemical distribution are reported. Through the combined use of 2D and 3D X‐ray nanotomography, it is shown that Li removal accompanied by oxygen oxidation is correlated with the development of morphological defects such as particle cracking. Chemical heterogeneity, quantified by subparticle level distribution of Mn valence state, is minimal during Mn redox, which drastically increases upon the formation of cracks during oxygen redox. Density functional theory and bond valence sum mismatch calculations reveal the presence of local short‐range ordering in the pristine oxide, which gradually disappears along with the extraction of Li. The study suggests that with cycling the transformation into true cation–disordered state can be expected, which likely impacts the voltage profile and obtainable energy density of the oxide cathodes.     

钡盐法处理六价铬电镀废水及最优工艺参数研究

使用钡盐法对铬废水处理,对p H值在废水中的初值、反映温度计量结果、重铬酸钾的浓度等,在回收六价铬的影响效果进行了分析。对废水中的六价铬使用了源自吸收的分光光度法回收。经过处理后,废水中的p H为8~9的时候,六价铬的回收在9%。废水中的六价铬随着其浓度不断上升增加。超过10℃的时候,六价铬的反应没有非常大的影响,但是当温度降低到10℃以下的时候,回收率就逐步下降了。经过处理之后,六价铬的浓度达到了0.276 7 mg/L,达到了相关规定的标准。     

Molten salt synthesis of MAX phases in the Ti-Al-C system

The molten salt method was used to synthesise the MAX phase compounds Ti₂AlC and Ti₃AlC₂ from elemental powders. Between 900–1000?°C, Ti₂AlC was formed alongside ancillary phases TiC and TiAl, which decreased in abundance with increasing synthesis temperature. Changing the stoichiometry and increasing the synthesis temperature to 1300?°C resulted in formation of Ti₃AlC₂ alongside Ti₂AlC and TiC. The type of salt flux used had little effect on the product formation. The reaction pathway for Ti₂AlC was determined to be the initial formation of TiC_1-x templating on the graphite and titanium aluminides.     

Chloride migration in concrete with superabsorbent polymers

Superabsorbent polymers (SAP) can be used as a means for internal curing of concrete. In the present study, the development of transport properties of concrete with SAP is investigated. The chloride migration coefficient according to NT BUILD 492 is used as a measure of this. Twenty concrete mixtures are tested 7, 14, and 28 days after casting. The development of degree of hydration is followed for 20 corresponding paste mixtures.Both when SAP is added with extra water to compensate the SAP water absorption in fresh concrete and without extra water, the internal curing water held by SAP may contribute to increase the degree of hydration. No matter if SAP is added with or without extra water, it appears that the so-called gel space ratio can be used as a key parameter to link age and mixture proportions (water-to-cement ratio and SAP dosage) to the resulting chloride migration coefficient; the higher the volume of gel solid relative to the space available for it, the lower the chloride migration coefficient, because the pore system becomes more tortuous and the porosity becomes less.     

Formation and properties of high entropy oxides in Co-Cr-Fe-Mg-Mn-Ni-O system: Novel (Cr,Fe,Mg,Mn,Ni)3O4 and (Co,Cr,Fe,Mg,Mn)3O4 high entropy spinels

Possibility of formation of quinary and senary equimolar high entropy oxides from the Co-Cr-Fe-Mg-Mn-Ni-O system is presented. Different proposed compositions are synthesized using the solid-state reaction route at high temperatures (900−1100 °C) and quenched to room temperature. Phase composition of the samples is studied, showing tendency toward formation of two main phases: rock salt-structured Fm-3 m and spinel-structured Fd-3 m. It is documented that the annealing temperature has a profound effect on stability of both structures, and at 1100 °C usually the highest content of Fm-3 m phase is usually observed. Three different oxides, namely, (Co,Cr,Fe,Mn,Ni)₃O₄, (Co,Cr,Fe,Mg,Mn)₃O₄ and (Cr,Fe,Mg,Mn,Ni)₃O₄ are obtained as single-phase materials, which structure can be described as the high entropy Fd-3 m spinel one. The latter two compounds have not been previously reported in the literature. Activated character of the electrical conductivity dependence on temperature is observed, with relatively high total conductivity at high temperatures and corresponding high absolute values of Seebeck coefficient.