涂层材料的断裂分析(英文)

和基体厚度相比,涂层很薄,因此细观力学模型可把基体作为半无限弹性体。由于涂层和基体材料的膨胀系数及弹性系数不匹配,涂层材料中残余热应力的解析解为 E_c/(1-γ_c)·(α_s-α_c)△T。用有限元法校核,该应力和解析解吻合得好。通过对涂层产生裂纹驱动力和断裂韧性的讨论,提出了抗裂涂层厚度公式。     

Effects of crack size and weld metal mismatch on the has cleavage toughness of wide plates

The heat affect zone (HAZ) is in many cases considered to be the most critical part of a weldment. In this paper, the effect of crack size and weld metal mismatch on the HAZ cleavage toughness of wide plate specimens with X-groove has been investigated by the J-Q-M theories and a simple micromechanism for cleavage fracture. Two crack sizes have been studied (a/w = 0.1 and 0.3). In the analyses, the HAZ yield strength is assumed to be higher than the base metal. For each crack size, weld metal local overmatch and local evenmatch with respect to the HAZ are considered. For a given global strain, the results indicate that weld metal overmatch and evenmatch yield the same crack tip loading in terms of J-integral for a/w = 0.3. For a/w = 0.1, overmatch gives lower crack tip loading than evenmatch. For a given crack tip loading, weld metal local evenmatch in general results in less effective crack tip loading than the overmatch. Overmatch is detrimental to HAZ toughness, but this detrimental effect becomes less significant when the crack size decreases.     

氢/空气火焰在半开口有障碍管道中的传播特性

针对氢／空气混合物，通过实验研究了其预混火焰在半开口管道中的火焰传播加速现象。结果表明，火焰传播状态随着氢气当量比的变化而发生改变。当氢／空气混合物被点燃后，由于障碍物的扰动，火焰在管道中不断加速传播，并最终到达一准稳态传播。在氢气当量比0．34附近时，火焰速度发生跃变。当氢气当量比足够大时，火焰传播由爆燃态转变为爆轰态。在本实验条件下，爆燃转准爆轰的临界条件是d/λ=2.6(d是圆环形障碍物内径，λ是爆轰格胞尺度）。障碍物阻塞比的变化对最大火焰速度和压力提升的影响不明显。     

航空齿轮表面硬化层断裂性能研究

按照航空齿轮的具体工艺过程，对材料12Cr2Ni4A的拉伸试样和断裂试样进行设计和加工，通过三点弯曲实验，重点研究了齿轮材料硬化层的硬度分布，硬化试样拉伸力学性能参数和断裂性能参数，实验结果表明，所采用试样的加工工艺方案是可行的，所获得的Kc基本反映我国航空硬化齿轮材料的断裂性能特征，为定量预测航空硬化齿轮疲劳寿命提供实验和理论分析的依据。     

Cohesive stresses and size effect in quasi-brittle materials

A novel approach to the derivation of Bažant’s size effect law is presented. Contrarily to the original Lagrangian derivation which hinged on energetic consideration, a Newtonian approach based on local stress intensity factors is presented. Through this approach, it is shown that Bažant’s size effect law is the first (and dominant) term in a series expansion for the nominal stress. Furthermore, analytical expressions forB are derived for selected specimen geometries.     

岩石龟裂系数法在火山岩裂缝储集层预测中的应用

 本文针对辽河东部凹陷油燕沟中生界火山岩的具体特征，采用纵波波速的比值——“龟裂系数”裂缝分析法［1,2,3］，研究了火山岩裂隙发育程度。综合龟裂系数裂缝分析及其他方法发现，该区中生界火山岩有效储集层的测井相特征主要表现为低密度、低中子、高声波时差和高伽马值等特征。此法的关键在于根据不同火山岩的岩性，选用合适的岩石骨架参数，在此基础上利用测井约束地震反演计算火山岩的层速度，进而计算出龟裂系数，然后根据已钻至火山岩井孔的测井相特征编制出火山岩预测厚度图。     

轴齿轮断齿失效分析

通过对轴齿轮断口形貌、硬度测试及金相组织等试验进行分析表明，齿根处没有进行硬化处理造成齿根处抗疲劳性能不足是导致轴齿轮疲劳断裂的主要原因，另外齿根过渡处倒角过小，且存在纵向刀痕引起了较大应力集中也是导致轴齿轮疲劳断裂的原因。     

40Cr钢复合热处理强韧化

用光学及电子显微镜(SEM.TEM)观察不同热处理的40Cr 钢的冲击及断裂韧性断口、及金相组织,阐明其间相互关系;断口结构可反映断裂特征,组织情况;细化晶粒提高强度、塑性和冲击韧性,但却减少脆断的特性距离 l 因而降低 K_(1c)模;减少碳(杂质)偏聚而使其呈较均匀地分布,从而减少可诱发塑坑的较粗大的碳(杂质)化合物的析出,即增加塑坑的间距 di 以及增加塑断组成物。从而都可增加断裂临界应变 ef,都可以提高 K_(1c)40Cr 复合热处理既靠先超高温淬、回火以减少碳(杂质)偏聚,改善其分布,以反增加位错马氏体从而提高 K_(1c),也靠后淬、回火细化晶粒而提高强度、塑性和冲击韧性,各自发挥长处达到强韧化。     

拉盖尔-高斯光束通过有硬边光阑光学系统的传输

采用将硬边光阑展为有限个复高斯函数之和的方法,得到了拉盖尔-高斯光束通过有硬边光阑近轴ABCD光学系统中传输的近似解析公式,作了数值计算以说明传输公式的应用,并对使用该式的误差作了讨论。     

油泵柱塞和轴承外套失效分析

对断裂的油泵柱塞、轴承外套从成分、组织、工艺等方面进行了检验分析。结果表明，柱塞首先断裂，断裂后的柱塞碎片卡住了轴承外套，使轴承外套过载脆断。而柱塞的断裂是由于热处理不当，造成淬火加热温度过高，使柱塞的显微组织出现粗大的针状马氏体，并引起淬火裂纹，导致柱塞的韧性下降，脆性增大，随着载荷作用和液压油的渗入，裂纹进一步扩展，当裂纹扩展笃柱塞有效载面积承受不了全部工作应力时，发生脆性断裂。