Oxidation and Fracture Strength of High-Purity Reaction-Bonded Silicon Nitride

Reaction-bonded Si₃N₄ (RBSN) made from high-purity Si powder is unusually resistant to degradation caused by exposures to air for up to 50 h at temperatures up to 1400°C. The weight gain during oxidation of this SiH₄-originating RBSN is approximately 10 times less than conventional RBSN. Contrary to normally observed strength degradations, room-temperature strengths of this high-purity, oxidized RBSN (avg = 435 MPa, max. = 668 MPa) remained at their unusually high, as-processed levels after 1000° and 1400°C oxidizing exposures. Fracture toughness values were unaffected by oxidation ( K _IC= 2.3 to 2.4 MPa · m^1/2). This superior oxidation resistance results from the high purity and the small diameter pore channels (0.01 to 0.06 μm) achieved in this SiH₄-originating RBSN.     

高功率移相器粘接工艺初探

主要介绍了粘接技术在高功率铁氧体移相器上的应用。通过对其工艺途径及关键工序的控制，提出了采用粘接技术完成高功率移相器铁氧体的连接，不仅可以大量地缩短工作时间，而且可以使制造成本大幅度降低。     

基于模型缩聚的θ指标损伤识别方法

为实现大型三维空间结构的损伤检测,提出了一种基于模型缩聚技术的检测方法。该方法利用有限数量的加速度传感器,得到大型三维桁架结构的自振频率和模态振型,以完成损伤的识别。数值仿真结果表明：该方法在损伤的定位识别和定量识别上能达到预期的适用性和可靠性。     

圆锯片的有限元模态分析

针对金属冷热锯机锯片在锯切轧件过程中出现的振动问题 ,利用 MSC/ NASTRAN有限元软件 ,计算分析了各种参数对锯片模态的影响。从而为锯片的设计及其制造工艺的确定提供了可靠的参考依据 ,为最终解决生产中的实际问题发挥了重要作用     

轧机机架强度和刚度的研究

本文对轧机机架的强度和刚度进行了研究。研究结果表明,增加机架横梁的高度是改善轧机机架刚度最有效也是最经济合理的方法。     

制镁还原罐的研制

从含镁的矿石中提炼金属镁的方法已不仅仅是电解法 ,还有目前广泛采用的真空还原法 (皮江法 ) ,但其所用的还原罐寿命短、价格高一直是困扰着国内、国外生产的难题。用研制出新的材料和改革后的铸造工艺生产出的还原罐 ,较好地解决了上述问题 ;并达到国内、国外先进水平。     

工程机械用800MPa低合金高强度钢焊接接头断裂韧性评价

对调质状态800MPa低合金高强度钢及其焊接接头进行了系列温度的断裂韧性测试,讨论不同焊接方法对焊接接头断裂韧性的影响。发现板材的轧制方向对断裂韧性影响显著,LT方向试件的断裂韧性远超过TL方向试件的断裂韧性。在-60℃以上,母材处于上平台延性断裂范畴。在-80℃,裂纹扩展过程中有延脆断裂模式的转变。焊条电弧焊焊缝的断裂韧性与气体保护焊焊缝的断裂韧性相当。尽管常温下焊缝金属的断裂韧性甚至优于母材,但随着试验温度的降低,焊缝金属的断裂韧性迅速下降。在-20℃已发生断裂模式转变,这在结构服役时要引起重视。本研究为大型工程机械的断裂安全评定奠定了基础。     

A Finite Element Simulation of the Electroplating Process

This paper describes the development, comparison and validation of both 2-D and 3-D models of the electroplating process in which the current density distribution, generated using the Finite Element Method (FEM), is used together with Faraday's law of electrolysis to determine the local plating depth. Prior to work on industrial components, a preliminary investigation was undertaken on the electroplating of a square copper cathode (work piece) with a parallel lead anode of identical shape. The results described here show good agreement, particularly in 3-D and are considered to validate the model sufficiently for it to be used for electroplating tooling design.     

Modelling of Material Side Flow in Hard Turning

In this paper an attempt has been made to model the material side flow generated during hard turning operation. A three dimensional thermo elasto-viscoplastic finite element model is presented. The model incorporates cutting tools with different nose radii and cutting conditions. The model was also used to investigate the effect of different process parameters on the extent of material side flow. The predicted results revealed that more side flow is generated when higher nose radius is used. A similar observation is noted when lower feed is used. The simulated results agreed well with the experimentally examined machined surface, viewed with a scanning electron microscope.