反应温度对聚苯胺薄膜生长的影响

在不同反应温度条件下采用原位聚合法在石英基片上制备了聚苯胺薄膜．对薄膜样品进行了紫外光谱、SEM、电性能表征。实验结果表明，过高的合成温度会加速聚合反应过程，抑制膜厚的增长，引起薄膜的热降解，进而对样品的导电性产生不良影响。根据生长速率与合成温度的依赖关系，估算了聚合反应的活化能Ea=34.4kJ/mol。     

Nanoscale Hybrid Langmuir－Blodgett Films Based on Cerium－Substituted Heteropolymolybdate and Polyquinoline

Nanoscale hybrid organic/inorganic Langmuir-Blodgett films of cerium-substituted heteropolymolybdates (CeHPMo) and π-conjugated macromolecule poly(1,2-dihydro-2,2,4-trimethyl) quinoline (PQ) were obtained with auxiliary film-forming material stearic acid(SA) or octadecylamine(ODA). The surface pressure-area isotherms illuminate the formation of the hybrid LB films of PQ/ODA/Ce-HPMo and PQ/SA/Ce-HPMo. The different film-forming mechanism was discussed when the different auxiliary film-forming materials were used in the system. The absorption spectra indicate that the molecules of PQ and Ce-HPMo are incorporated into the LB films. Tapping-mode AFM image reveals a granular surface texture of nanosized Ce-substituted heteropolymolybdate. STM image shows that the conductivity is greatly improved after Ce-substituted heteropolymolybdates are incorporated in the films.     

Creep Crack Growth in Polypropylene Film with Various Crack Lengths at Diverse Stresses and Temperatures

Creep crack growth rates were measured using centrally cracked tension specimens of thin polypropylene film with different crack lengths at various stresses and temperatures. The creep crack growth rates were correlated with the stress intensity factor. There was the region of the minimum constant crack growth rate which occupied more than 70% of the total creep failure life. This constant creep crack growth rate characteristics were analyzed on the basis of the stress-dependent Arrhenius type thermally activated process.     

掺铝氧化锌(AZO)导电薄膜的研究进展

综述透明导电薄膜的性能、种类、制备工艺、研究及应用状况,重点讨论掺铝氧化锌(AZO)薄膜的结构、导电机理、光电性能和当前的研究焦点。并指出,为了进一步提高透明导电薄膜的性能,应从以材料选择、制备工艺、多层膜光学设计等方面深入研发,以满足尖端技术的需要。     

溶液温度对电化学沉积氧化亚铜薄膜相成分和显微结构的影响

用电化学方法在不锈钢基体上沉积多晶Ｃｕ２Ｏ薄膜并用Ｘ射线衍射和扫描电进行了分析研究了溶液温度对薄膜相组成、晶粒尺寸和择优取向的影响，当溶液的ＰＨ＝９，温度低于５０℃时得到的是Ｃｕ２Ｏ／Ｃｕ复相薄膜，纯Ｃｕ２Ｏ薄膜可在溶液温度高于５０℃时获得，纯Ｃｕ２Ｏ薄膜具有（１００）择优取向，实验发现薄膜的晶粒尺寸随溶液温度的增加从０．１２μｍ增加到０．６５μｍ。     

铜硅取代的酞青材料LB膜气敏传感器的研究

采用ＬＢ膜技术对沉积在石英晶振的铜硅取代的酞青材料的气体敏感性进行了系统研究，结果表明，该方法所获得的敏感膜敏感度高，反应迅速，稳定性较好。     

4F0.06AC树脂吹塑薄膜技术的探讨

在加工应用试验的基础上。探讨了加工温度、吹胀比、超想线高度及设备对４Ｆ０．０６ＡＣ薄膜适宜的加工条件。     

DDI法测薄膜光学常数

双光束双波长激光干涉（ＤＤＩ）法采用自行设计的可调双波长氦氖激光器作光源，可在同一光路中通过两次测量获得薄膜样品两个波长（０．６３３μｍ，３．３９μｍ）下的光学常数，即折射率、消光系数和厚度。论述了测量原理、测量装置和测量结果。     

热分解法制备钛酸铅镧薄膜及其电性能研究

本文研究了用金属有机物热发解法制备ＰＬＴ８薄膜的工艺过程和基片对薄膜结构的影响，并且给出了铁电性能的测量结果。     

LB技术制备大面积超薄PMMA抗蚀层的研究

采用自行研制的ＬＢ自动提膜装置，制备出大面积（１０×８ｃｍ２）、高质量的ＰＭＭＡ超薄抗蚀剂膜，并将其用于高分辨率铬掩模版的研制。通过电子束曝光，湿法蚀刻，制作了分辨率优于０．５μｍ，特征线宽０．３８μｍ的４（１００ｍｍ）铬掩模版。