High cycle fatigue behaviour of Ti–6Al–4V alloy at elevated temperatures

High cycle fatigue behaviour of Ti–6Al–4V alloy was studied at 623 K and 723 K. Fatigue strength decreased at elevated temperatures compared with at ambient temperature. In the short life regime, fatigue strength was lower at 723 K than at 623 K, but in the long life regime it was nearly the same at both temperatures. At elevated temperatures, cracks were generated earlier at applied stresses below the fatigue limit at ambient temperature, indicating lowered crack initiation resistance. Small cracks grew faster at elevated temperatures than at ambient temperature, which became more noticeable with increasing temperature. After allowing for the elastic modulus, small cracks still grew faster at elevated temperatures.     

Abrasion erosion of concrete by water-borne sand

Hydraulic concrete structures frequently experience long-term abrasive erosion by water-borne sand, resulting in surface damage and eventually limiting their service life. In this study, the investigation of abrasion erosion tests on concrete with various water to cementitious material ratios (w/cm) was performed. The effects of the constituent materials on concrete structure abrasion erosion resistance were studied. The test results show that: (1) reduction in the w/cm ratio increases the tested concrete abrasion resistance; (2) the splitting tensile strength is a viable indicator for concrete abrasion resistance; (3) high permeability concrete exhibits weak abrasion resistance; and (4) concrete and low strength concrete made with coarser aggregate exhibit greater abrasion resistance.     

浅析SRT-Ⅳ裂解炉炉管弯曲及断裂原因

主要分析计算了裂解炉炉管受力情况，进而得出结论：裂解炉自身结构的相互约束力和炉管渗碳是导致炉管弯曲、断裂的主要原因，并提出了相应的解决措施。     

A203型低温氨合成催化剂使用小结

对Ａ２０３型低温氨合成催化剂的使用进行总结，介绍了该催化剂的装填，升温还原情况及使用效果。     

IMPROVEMENT ON FATIGUE LIFE OF ALLOY LY12CZ AFTER LASER RADIATION AND ITS DAMAGE EVOLUTION

The change of microstructure of fatigue specimens before and after laser radiation was studiedby transmission electron microscopy.The results show that the diameter of dislocation cell λtends to a constant at fatigue failure.Based on the principles of continuous damagemechanics,expressions of the fatigue damage criterion and processes of fatigue damage evolu-tion for L Y12CZ have been derived.     

TENSILE FRACURE IN AN Al-Li ALLOY 8090

ＴＥＮＳＩＬＥＦＲＡＣＵＲＥＩＮＡＮＡｌ－ＬｉＡＬＬＯＹ８０９０￥Ｊｉａｎｇ，Ｄａｍｉｎｇ；Ｗａｎｇ，Ｙｉｎｏｎｇ；Ｈｏｎｇ，Ｂａｎｄｅ；Ｌｅｉ，Ｔｉｎｇｑｕａｎ（ＨａｒｂｉｎＩｎｓｔｉｔｕｔｅｏｆＴｅｃｈｎｏｌｏｇｙ，Ｈａｒｂｉｎ１５００８０）Ｓｕ...     

BREAKAGE MECHANISM OF TUNGSTEN BASED ALLOY BLOCK FOR ELECTRO-HEAT UPSETTING

The breakage mechanism of W-Ni-Fe alloy in the process of electro-heat upsetting studied both theoretically and experimetnally, and also the behaviors of crack formation and propagation were analysed. Alloy suffers from corrosion and thermal-mechanical fatigue mutual function. Simultaneously, the practical ways to improve the anvil life was discussed.     

影视作品中“审丑”现象流行的原因——从王宝强的走红谈起

从王宝强走红影视圈的案例出发,讨论了当今影视作品中的"审丑"现象流行的原因。这种"丑",不涉及品德,而是单纯的外貌丑,而这种外貌丑又是相对的。认为"审丑"现象的产生主要基于观众的审美疲劳,时代导致审美趋向多元化,把审美的意义赋予丑的形象,丑星的现实生活基础等几个原因。另外指出这种类型的丑星需要对自己加以调整、提高演技才能在影视圈走得更久,否则会引起观众的"审丑疲劳",不过是昙花一现。     

减震油弹性模量及疲劳特性试验台设计与实现

油液的体积弹性模量以及疲劳特性参数是油液非常重要的物理参数,在液压系统中,直接影响系统的稳定性和动态品质.研究设计了弹性模量及疲劳特性参数测试试验台,基于弹性模量的定义对弹性模量进行测量计算,同时以专用车辆油气悬挂装置为对象,对悬挂内液压油疲劳特性参数进行测试,如:温度、粘度等.完成控制系统以及数据采集系统的设计,与上位机实时通讯,实现测试过程的自动化.     

Model test of helical angle effect on coal loading performance of shear drum

The work presented in this paper focuses on improving coal loading performance of shear drum.Employing the similarity theory,we carried out a dimensional analysis of the correlation parameters which in...