同质焊缝球墨铸铁焊条的研制

研制了一种适合于球墨铸铁与球墨铸铁以及球墨铸铁与结构钢焊接的专用球墨铸铁焊条，通过试验确定了球墨铸铁焊条的合金成分并给出了比较合理的焊芯和焊条药皮化学成分。采用该焊条对球墨铸铁焊接时，可以达到同质焊缝要求。测试结果表明，焊缝金属的化学成分、金相组织均满足焊接球墨铸铁的要求，焊缝的硬度在190～230HB之间，焊缝中石墨球化稳定，焊条具有良好的焊接工艺性能。     

真空粉末绝热低温贮罐制造的部分工艺方法

在真空粉末绝热低温贮罐的制造过程中、通过吸附器分子筛的活化、夹层真空系统的处理和充装珠光砂等工艺方法的改进,可较大地缩短产品的制造周期并提高产品的质量。     

Application of High Temperature Corrosion-Resistant Materials and Coatings Under Severe Corrosive Environment in Waste-to-Energy Boilers

Corrosion-resistant materials (CRMs) and coatings are key technologies to increase power generation efficiency and reduce maintenance in waste-to-energy (WTE) plants. Corrosion environment became severe as steam temperatures have increased. The steam condition of more than 400 °C/3.9 MPa became possible in WTE boilers by using highly durable corrosion-resistant coatings, such as thermal spray of Al/80Ni20Cr alloy, HVOF-sprayed NiCrSiB alloy, Alloy 625 weld overlay for waterwall tubes and also superheater tubes. Also, the use of 310S type stainless steels and high Cr-high Mo-Ni base and high Si-Cr-Ni-Fe alloys have progressed because of a better understanding of corrosion mechanisms. Furthermore, high durability coatings using cermet and ceramic materials were applied to high temperature superheaters. This paper describes the major developments and the application of CRMs and coating technologies in the last 30 years in WTE plants, the corrosion mechanisms of alloys, the deterioration mechanisms of spray coating layers, and future subjects for the development of corrosion-resistant materials and coatings.     

焊接工艺参数对奥氏体不锈钢焊接接头腐蚀行为的影响

通过草酸腐蚀和硫酸-硫酸铁腐蚀实验，研究了奥氏体不锈钢焊接接头腐蚀与焊接热输入的关系。结果表明，随着焊接线能量的增加，其焊接接头腐蚀越严重。随着焊接线能量的增大，腐蚀率增大且有加速趋势。     

Microstructure and mechanical properties of wrought magnesium alloy AZ31B welded by laser-TIG hybrid

The laser-TIG hybrid welding was mainly used to weld the wrought magnesium alloy AZ31B. The tech-nical characteristics of laser-TIG hybrid welding process was investigated and the interactional mechanism between laser and arc was discussed, at the same time the microstructure and mechanical properties of the wrought magnesi-um alloy AZ31B using laser-TIG hybrid welding were analyzed by optical microscope, EPMA, SEM, tensile ma-chine, hardness machine. The experimental results show that the presence of laser beam boosts up the stability of the arc during high speed welding and augments the penetration of weld； the crystal grains of magnesium alloy weld are fine without porosity and cracks in the best welding criterion and the microstructure of HAZ does not become coarse obviously. The elements profile analysis reveals that Mg content in the weld is lower than that of the base metal, but Al content is higher slightly. Under this experimental condition, the wrought magnesium alloy AZ31B joint can be achieved using laser-TIG hybrid process and the tensile strength of the joint is equivalent to that of the base metal.     

锚链钢弯环内侧开裂分析原因

对锚链钢弯环的原材料和车削后热处理材料及开裂的弯环进行低倍、组织、断口检验，结果表明弯环开裂是由车削后的热处理工艺和焊接工艺控制不当造成的。     

熔池表面变形对电弧行为特征的影响

在电弧与熔池统一模型的基础上研究熔池上表面变形对电弧行为特征的影响。用本模型计算出的平坦熔池表面电流密度和热流密度的分布与试验结果显示了很好的一致性。而变形熔池表面的电流密度和热流密度分布则不再符合近似的高斯分布。这就为下一步研究电弧和熔池的工作提供了基础。     

铍的焊接缺陷及其控制技术研究

加填充材料焊接铍是防止铍焊缝开裂的技术措施之一,但加填充材料对铍进行高能束焊接可使焊缝形成钎接焊.介绍了铍焊接时生成的缺陷,主要有焊接裂纹、气孔、夹杂、未焊透和热影响区的晶粒长大等,全面系统地总结了铍焊接形成的各类缺陷,减轻和消除焊接缺陷的各种试验技术.在焊接参数试验的过程中,避开对焊接裂纹敏感的脉冲焊和深熔焊接工艺参数,可使铍的焊接缺陷（特别是焊接裂纹）明显地减少.     

压力管道焊缝含环向表面裂纹J积分估算方法

基于SC .ENG(表面裂纹工程估算 )方法的基本原理 ,建立了弯矩作用下压力管道焊接接头含有内表面、等深度及有限长度环向表面裂纹的J积分近似估算公式 ,在计算公式中考虑了焊缝非匹配因素的影响。与SC .ENG1和SC .ENG2方法相对应 ,在此分别称所推导的J积分估算方法为SC .ENG3和SC .ENG4方法。该方法建立在塑性形变理论、Ramberg -osgood本构关系和等效原则基础上 ,通过使裂纹存在时的结构柔度与壁厚局部减薄时模拟结构的柔度相等的方式建立J积分的估算公式。有限元数值解验证了上述J积分估算公式的有效性     

10CrMo910钢焊接工艺探讨

通过对大庆２００ＭＷ机组主蒸管道１０ＣｒＭｏ９１０钢的焊接性能分析,提出了一整套行之有效的焊接工艺,并在施工现场检修焊接中进行了实践,为焊接同类钢材提供了可借鉴的经验和工艺参数。