Adsorption of Th(Ⅳ) and Ce(Ⅳ) on Zirconium Based Metal-organic Framework Zr-CAU-24

In this paper, zirconium based metal-organic frameworks (MOFs) Zr-CAU-24 was successfully prepared by using solvothermal method, which was one kind of zirconium based MOFs. Zr-CAU-24 has nanoporous structure with BET specific surface area of 1 610 m²/g. Thermogravimetric analysis (TGA) and irradiation stability test were conducted. Taking Zr-CAU-24 as adsorbent, the adsorption characteristics of Th(Ⅳ) and Ce(Ⅳ) on Zr-CAU-24 were investigated through static adsorption experiments. The effects of contact time, initial pH on Th(Ⅳ) and Ce(Ⅳ) adsorption by Zr-CAU-24 were investigated respectively, and the kinetics and thermodynamics were investigated. The results indicate that Zr-CAU-24 has good thermal stability and irradiation stability. The quasi-second-order model provides a good explanation for the adsorption process of Th(Ⅳ) and Ce(Ⅳ) on Zr-CAU-24, which is a chemical adsorption process. The active site of Zr-CAU-24 is evenly distributed, and the adsorption is a single layer adsorption. Through the study of selective adsorption of mixed metal ions on Zr-CAU-24, it is found that Zr-CAU-24 has the adsorption selectivity for Th(Ⅳ) and Ce(Ⅳ).     

二丁基氧化锡的制备改进

用甲苯和少量四氢呋喃作溶剂 ,通过格氏反应由四氯化锡制备了四丁基锡 ,四丁基锡与四氯化锡直接反应冷却后得二丁基二氯化锡粗品 ,随后用二丁基二氯化锡粗品的乙醚溶液直接水解制备二丁基氧化锡高并反应收率均大于 90 %。     

Evaluation of microstructure and creep damage in high-Cr ferritic steel welds

11Cr-0.4Mo-2W-CuVNb steel (ASME Gr.122) is used for boiler components in ultra-supercritical (USC) thermal power plants.The creep strength of high-Cr steel welds decreases due to the formation of Type IV creep damage in the heat-affected zone (HAZ) during long-term use at high temperatures.In the present study,the processes and mechanisms of Type IV creep damage were elucidated by investigating the long-term creep strength,microstructure and damage behavior of Gr.122 steel welds.Creep tests using thick weld...     

满足国Ⅳ及以上排放共轨供油泵技术发展的思路

介绍了在满足国Ⅳ及以上排放柴油机时,共轨系统供油泵的技术发展思路,对国Ⅳ柴油机的主要技术路线和共轨系统供油泵的技术对策进行了分析,进而对共轨泵的基本结构型式和油量控制方式等关键参数的设计和选型思路进行了详细介绍。     

(S)-1-(2-氯乙酰基)吡咯烷-2-甲腈的合成与表征

探讨了合成(S)-1-(2-氯乙酰基)吡咯烷-2-甲腈的新工艺路线,即以L-脯氨酸为原料,经N-氯乙酰化、羧基氨基化和酰胺脱水反应合成目标化合物。目标化合物及各中间体的结构采用1HNMR和MS进行了确定。此外,详细研究了反应条件的影响,得到了优化的反应条件。目标产物的总收率可达42.3%。该合成路线具有原料便宜易得、操作简单、条件温和等优点,具有很好的市场应用前景。     

电流密度对不锈钢基β-二氧化铅-二氧化钛-四氧化三钴复合镀层性能的影响

研究了电流密度对不锈钢基β-PbO2-TiO2-Co3O4复合镀层的沉积速率、显微硬度、表面形貌、结合力、电催化活性等性能的影响。镀液组成和其他工艺条件为:Pb(NO3)2250g/L,HNO310g/L,NaF0.5g/L,TiO215g/L,Co3O430g/L,温度50℃,pH1～2,沉积时间4h。通过扫描电镜、能谱仪和X射线衍射仪分析了复合镀层的形貌、组成和构相。结果表明,最佳电流密度为4A/dm2。在4A/dm2下,β-PbO2-TiO2-Co3O4复合镀层的沉积速率为15.31g/(h·dm2),显微硬度为653.3HV,表面平整、致密。镀层中Ti、Co的摩尔分数分别为2.22%和4.37%,表明TiO2和Co3O4颗粒与β-PbO2镀层实现了共沉积。     

P92钢焊接接头Ⅳ型蠕变断裂特性

在600-650℃,100-240 MPa对用埋弧自动焊工艺制备的P92钢焊接接头进行高温蠕变实验,采用OM,SEM和TEM等研究焊接接头的Ⅳ型蠕变断裂特性.结果表明,P92钢焊接接头的Ⅳ型断裂发生在高温和低应力条件下,存在一个临界Larson-Miller参数LMP和临界应力,它们的值分别约为35.5和120 MPa;Ⅳ型断裂部位的变形很小,位于靠近临界热影响区的细晶区,即加热峰值温度在Ac₃附近,该部位显微结构退化为铁素体等轴晶及蠕变过程中Laves相在晶界析出和长大是影响Ⅳ型断裂的主要因素,M₂₃C₆粗化的影响较小;焊接接头Ⅳ型断裂是一种晶界孔洞聚集型蠕变断裂,孔洞在粗大Laves相附近形核,可用损伤晶界上孔洞面积分数f或孔洞面积分数a作为发生Ⅳ型断裂的微观判据,它们在650℃时的临界值分别约为0.5%和1.2%.     

Ti表面构建Ⅳ型胶原/肝素生物层提高细胞相容性的研究

支架表面内皮化成为最终实现支架与血液及组织长期相容的良好途径,内皮祖细胞在材料表面的集聚、生长与增殖使快速内皮化成为可能。利用静电结合作用将抗凝血药物肝素和内皮细胞基膜中重要组成的Ⅳ型胶原结合到Ti表面,使其具有良好的细胞相容性。Ti通过碱活化和硅烷化处理后,形成带正电荷的氨基表面,与有残留负电荷的肝素/Ⅳ型胶原复合物静电结合,形成生物化层。通过傅立叶红外掠射检测了材料表面特征基团的变化,通过水接触角的测定和扫描电子显微镜跟踪表面亲疏水性能以及表面形貌的变化。通过免疫荧光染色法对Ⅳ型胶原进行定性表征。结果显示仿生层构建成功,修饰后的表面较Ti表面能够粘附更多的内皮祖细胞,细胞生长与增殖较快,且细胞形态良好,细胞相容性得到明显改善。Ⅳ型胶原的引入对于心血管植入器械的表面改性有重要参考价值。     

邻氯苯基荧光酮光度法测定钢样中的钛

研究以邻氯苯基荧光酮-十六烷基三甲基溴化铵为显色体系,在表面活性剂十六烷基三甲基溴化铵存在下,钛(Ⅳ)和邻氯苯基荧光酮所形成橙红色的络合物,实验结果表明,在酸性介质中最大吸收波长位于560nm,钛((Ⅳ)含量在0～12μg/25mL范围内符合比尔定律,其表观摩尔吸光系数ε_(560)=1.2×10~5L/mol/cm。钢样的人工合成样中钛((Ⅳ)的平均回收率为103.3%,相对标准偏差为2.0%。采用抗坏血酸掩蔽剂消除被测样中干扰离子的影响,实验结果表明:38~#和45~#钢样中钛((Ⅳ)的含量分别为0.08%和0.05%,其加标平均回收率分别为101.3%和98.9%。相对标准偏差分别为2.34%、1.34%。本方法选择性及准确性好、灵敏度高、简便易行。     

骨粉对放射性废水中钍的吸附行为研究

以骨粉为吸附材料,对水溶液中的Th(Ⅳ)进行吸附研究。采用X射线衍射(XRD)、红外光谱(FT-IR)和扫描电镜(SEM)表征了骨粉的理化性质。考察了溶液pH值、钍溶液浓度、接触时间、温度等对骨粉吸附钍的影响,并对骨粉吸附钍的吸附机理进行了探讨。结果表明,骨粉在pH=3时有最大吸附容量。等温吸附实验及动力学研究表明,骨粉对钍的吸附行为符合准二级动力学模型和Langmuir等温吸附模型,单分子层饱和吸附容量为482.50mg/g。热力学研究表明,骨粉对钍的吸附是自发的吸热过程。