介绍了针对早期建筑的混凝土桥梁碳化情况采用H52-S4环氧厚浆涂料进行封闭保护、防腐处理的施工方法及施工工艺，并提出施工中应注意的有关事项，对温度影响、表面气泡处理进行了讨论，提出合理化建议。     

环氧基的PCB对无铅组装的兼容性

综述了环氧树脂基的PCB与无铅化组装的兼容性问题。经过大量试验表明,常规的FR-4基材和双氰胺固化的高Tg基材是不能满足无铅化组装要求的,而采用酚醛固化的中等-Tg的环氧树脂基材是可能成为无铅化组装用基材的。同时,PCB制造过程也起着重要的作用。PCB设计和再(回)流焊的加热梯度也影响着无铅化的性能。     

Decreasing miscibility with greater heterogeneity in ternary polymer blend: poly(cyclohexyl methacrylate), poly(α‐methyl styrene) and poly(4‐methyl styrene)

A ternary blend system comprising poly(cyclohexyl methacrylate) (PCHMA), poly(α‐methyl styrene) (PαMS) and poly(4‐methyl styrene) (P4MS) was investigated by thermal analysis, optical and scanning electron microscopy. Ternary phase behaviour was compared with the behaviour for the three constituent binary pairs. This study showed that the ternary blends of PCHMA/PαMS/P4MS in most compositions were miscible, with an apparent glass transition temperature (T_g) and distinct cloud‐point transitions, which were located at lower temperatures than their binary counterparts. However, in a closed‐loop range of compositions roughly near the centre of the triangular phase diagram, some ternary blends displayed phase separation with heterogeneity domains of about 1 µm. Therefore, it is properly concluded that ternary PCHMA/PαMS/P4M is partially miscible with a small closed‐loop immisciblity range, even though all the constituent binary pairs are fully miscible. Thermodynamic backgrounds leading to decreased miscibility and greater heterogeneity in a ternary polymer system in comparison with the binary counterparts are discussed. © 2003 Society of Chemical Industry     

Schubspannungsbomben in Faserverbunden

Shear Bombs in Fibre Composites Despite an optimum external shape non‐load adapted internal fibre orientation can lead to the formation of shear cracks where crossing tension‐compression principal stress trajectories create localized shear peaks. Trees are subject to those failure because they cannot re‐arrange their fibres after wood formation. Bones can adjust their micro‐structure to changing load conditions and in this way can better control shear failure. The engineer working with fibre composites should be alert to avoid fibre arrangements not following the force flow. Localized shear zones may also form near notches similar to normal notch stresses, however they are not always situated at the contour line of the notch.     

Possibilities and extension of XRD material response analysis in failure research for the advanced evaluation of the damage level of Hertzian loaded components

Due to clearly distinguishable damage symptoms, it is differentiated between the surface and sub‐surface failure mode of rolling bearings. Material states red out by X‐ray diffraction (XRD) residual stress measurements point to a variety of loading conditions especially at raceway surfaces that are associated with several competing failure mechanisms. The corresponding lifetime reduction can range from the lower fatigue strength region to material ratcheting in extreme cases. Relevant position of the microstructural changes and nature of the failure mechanisms are characterized. The time alteration of the XRD material parameters measured at or near the surface and at the depth of the maximum equivalent stress correlates, in a different manner, with the statistical parameter of the 10 % bearing life. Both failure modes are illustrated by concrete examples. Contaminated lubricant and boundary lubrication, which represent practically important surface‐induced failures, are discussed in more detail. Gray staining, i.e. shallow pitting, often occurs without distinct indication of global material aging by means of XRD characteristics. Here, scanning electron microscopy observations and electron microprobe analyses point to corrosion fatigue as acting surface failure mechanism. The interaction between material and lubricant under complex loading regimes particularly of mixed friction and corrosion opens further failure research areas in the field of tribology.     

Phenol novolac/poly(4- hydroxyphenylmaleimide) blend hardeners for DGEBA-type epoxy resin

Phenol novolac/poly (4-hydroxyphenylmaleimide) (PHPMI) blends were used as an epoxy resin hardener. The curing behavior of the above system and the thermal and mechanical properties of the cured epoxy resin were studied. It was not necessary to use a curing accelerator for this system, because PHPMI caused acceleration of the curing reaction. The curing mechanism of this system was investigated by using model compounds. Test pieces from the neat resins and the glass fiber reinforced resins were evaluated in terms of thermal and mechanical properties, respectively. It was found that heat resistance and mechanical properties were improved by increasing the amount of PHPMI in the hardener.     

自韧Si3N4陶瓷的显微结构及其性能研究

利用热压的方法制得室温断裂韧性和抗弯强度分别为１１．２ＭＰａ·ｍ￣（１／２）、８２３ＭＰａ，高温（１３５０℃）断裂韧性和抗弯强度分别为２３．９ＭＰａ·ｍ￣（１／２）、６３０ＭＰａ的自韧Ｓｉ＿３Ｎ＿４陶瓷。研究了显微结构和力学性能之间的关系。结果表明：玻璃相的含量、β－Ｓｉ＿３Ｎ＿４的长径比等对性能有重要影响。分析了自韧Ｓｉ＿３Ｎ＿４陶瓷的增韧机理，通过ＳＥＭ明显观察到Ｓｉ＿３Ｎ＿４中存在裂纹偏转、分支和β－Ｓｉ＿３Ｎ＿４拔出现象。     

超低膨胀陶瓷K_（2x）Ba_（1－x）Zr_4（PO_4）_6系统的X射线衍射

用高温Ｘ射线衍射方法对磷酸锆钡钾系统陶瓷材料的各向异性热膨胀作了研究．对七个组份试样的７７套高温Ｘ射线衍射图作了仔细的指标化和精密点阵常数测定．点阵常数随温度作非线性变化·对Ｋ_２ｘＢａ_１－ｘＺｒ_４（ＰＯ_４）_６的不同组份不同温度（３００～１３００Ｋ）的热膨胀系数。α_ａ、α_ｃ、　作了测定·该系统零膨胀陶瓷的组份为Ｋ_１．１６Ｂａ_０．４２Ｚｒ_４（ＰＯ_４）_６（ｘ＝０．５８）     