Anchoring single Pt atoms on hollow Ag3VO4 spheres for improved activity towards photocatalytic H2 evolution reaction

The high cost of noble metal catalysts has been a great bottleneck for the catalyst industry. Using the noble metal at a single-atom level for catalytic applications could dramatically decrease the cost. The impacts of single Pt atoms on the photocatalytic performance of Ag₃VO₄ have been investigated and reported. In this report, single Pt atoms were anchored on the surface of Ag₃VO₄ (AVO) as a cocatalyst, and the resultant composite photocatalyst has been studied for photocatalytic H₂ production from water driven by visible light. The as-prepared AVO particles are hollow nanospheres in the monoclinic phase with a bandgap of 2.20 eV. The light absorption edge of AVO/Pt is slightly red-shifted compared to that of the pristine AVO, indicating more visible light absorption of AVO/Pt. The XPS peaks of Ag, V, and Pt exhibit a significant shift after AVO and Pt get into contact, suggesting the strong interaction between the surface Ag and V atoms, and single Pt atoms. After 3-h illumination, the photocatalytic H₂ evolution amount from AVO/Pt is improved up to 1400 μmol, which is 2.8 times that on the bare AVO. Such efficient photocatalytic H₂ evolution on AVO/Pt is still maintained after five reaction cycles. The better photocatalytic performance of AVO/Pt has been attributed to the more efficient visible light utilization and the lower interfacial charge transfer resistance, as demonstrated in the DRS and EIS spectra. The presence of the surface Pt atoms also leads to a higher amount of reactive radicals, which could efficiently promote the surface redox reactions.     

Compiler compatible 5.66 Mb/mm2 8T 1R1W register file in 14 nm FinFET technology

1-read/1-write (1R1W) register file (RF) is a popular memory configuration in modern feature rich SoCs requiring significant amount of embedded memory. A memory compiler is constructed using the 8T RF bitcell spanning a range of instances from 32 b to 72 Kb. An 8T low-leakage bitcell of 0.106 μm² is used in a 14 nm FinFET technology with a 70 nm contacted gate pitch for high-density (HD) two-port (TP) RF memory compiler which achieves 5.66 Mb/mm² array density for a 72 Kb array which is the highest reported density in 14 nm FinFET technology. The density improvement is achieved by using techniques such as leaf-cell optimization (eliminating transistors), better architectural planning, top level connectivity through leaf-cell abutment and minimizing the number of unique leaf-cells. These techniques are fully compatible with memory compiler usage over the required span. Leakage power is minimized by using power-switches without degrading the density mentioned above. Self-induced supply voltage collapse technique is applied for write and a four stack static keeper is used for read Vmin improvement. Fabricated test chips using 14 nm process have demonstrated 2.33 GHz performance at 1.1 V/25 °C operation. Overall V_min of 550 mV is achieved with this design at 25 °C. The inbuilt power-switch improves leakage power by 12x in simulation. Approximately 8% die area of a leading 14 nm SoC in commercialization is occupied by these compiled RF instances.     

LWIP协议在STLite/OS20操作系统中的移植

介绍了免费的TCP/IP协议栈LWIP开发工具和环境,分析了如何实现LWIP的移植,并给出了一种嵌入式系统与网络互联的新思路。     

ZnO基薄膜晶体管的研究

ZnO是一种宽带隙的光电半导体材料,能应用于很多领域,如可用在压敏变阻器、声表面波器件、气敏元件、紫外光探测等。ZnO也可以作为有源层应用于薄膜晶体管(TFT)中。ZnO基薄膜晶体管具有以下突出优势:对于可见光部分平均具有80%以上的透射率,迁移率可以高达36cm2/V·s,开/关电流比大于106,可在较低温度(甚至室温)下制备。基于这些优点,ZnOTFT具有取代有源矩阵液晶显示器中常规a-SiTFT的趋势。同时对ZnOTFT的研究也推动了透明电子学的发展。本文阐述了ZnOTFT优越的电学性能,指出了其目前尚存在的不足,并对其发展前景进行了展望。     

Encapsulation and Ostwald Ripening of Au and Au–Cl Complex Nanostructures in Silica Shells

We report a general template strategy for rational fabrication of a new class of nanostructured materials consisting of multicore shell particles. Our approach is demonstrated by encapsulating Au or Pt nanoparticles in silica shells. Other superstructures of these hollow shells, like dimers, trimers, and tetramers can also be formed by nanoparticle‐mediated self‐assembly. We have also used the as‐prepared multicore Au–silica hollow particles to perform the first studies of Ostwald ripening in confined microspace, in which chloride was found to be an efficient mediating ligand. After treatment with aqua regia, Au–Cl complex is formed inside the shell, and is found to be very active under in situ transmission electron microscopy observations while confined in a microcell. This aspect of the work is expected to motivate further in situ studies of confined crystal growth.     

高分散度Pt/C电催化剂的制备

Cabot公司Vulcan XC-72型炭黑，经过H2O2氧化处理后作为Pt的载体，H2PtCl6作为金属前驱体制备了高度分散的Pt/C催化剂。讨论了不同条件下H2PtCl6在炭黑上的吸附性能。载体经过H2O2氧化处理24h,H2PtCl6在pH=9下吸收48h，H2 350℃还原2h，可以制备出铂晶粒平均大小为1.8nm的Pt/C电催化剂。     

继电器微机检测装置的软件设计

继电器作为主要电气元件之一，广泛应用于各个领域。对继电器的检测主要包括机械参数和电气参数的检测。电气参数由于其项目多，实现微机测试比较困难，据此，开发了电磁继电器电参数的自动测试装置，本文仅介绍其软件设计。     

Anatase Sol Prepared from Peroxotitanium Complex Aqueous Solution Containing Niobium or Vanadium

Niobium- or vanadium-doped anatase sols were prepared by hydrothermal treatment of 0.1 mol/dm³ peroxotitanium complex aqueous solutions dissolving 0–10 mol% niobium or vanadium at 100°C for 8 h. Niobium-doping caused the increase of lattice constants of anatase and the shape change of anatase crystal from spindle-like to cubic-like structure, but no change of the optical absorbance. Vanadium-doping caused the decrease of lattice constant of c -axis, the miniaturization of anatase crystal and the increase of optical absorbance at the wavelength from 350–700 nm.