苛化法制备亚微米纺锤形碳酸钙联产氢氧化钠

为了解决制碱白泥所带来的二次污染问题,在苛化法的基础上改进出一种新工艺。该工艺在制碱过程中不再副产白泥,而是将原料中的钙转化生成高附加值的亚微米纺锤形特种碳酸钙,并联产高含量的液体氢氧化钠。研究了消化与苛化工艺条件对碳酸钙粒径和氢氧化钠含量的影响,采用扫描电镜（SEM）对样品形貌做了表征。结果表明：在柠檬酸钠添加量为1%（质量分数）、消化水温为84 ℃、闷灰时间为40 min、加料时间为20 min的条件下,制备出颗粒短径为180 nm、粒径分布为150~200 nm、长径比为3的亚微米纺锤形碳酸钙,并联产出高含量的液体氢氧化钠。     

基于纳米氢氧化铝颗粒的Pickering乳液制备

以异丙醇铝为原料,采用醇盐水解?水热法制备勃姆石型纳米氢氧化铝颗粒,优化制备条件;以所制颗粒为稳定剂、角鲨烯为油相,通过超声破碎法制备Pickering乳液,考察了颗粒浓度、水相成分、超声时间及功率对Pickering乳液粒径及稳定性的影响。结果表明,水热温度200℃、水热时间2 h条件下,可制得结晶度高且均一的勃姆石型纳米氢氧化铝颗粒,平均粒径为55.70?9.20 nm,多分散性指数(PDI)为0.187?0.011;所制Pickering乳液平均粒径为1870?55 nm,PDI=0.120?0.010,可在室温下稳定储存120 d以上,且生物相容性良好,有望应用于生物医药领域。     

氢氧化镁的固相制备及其表面改性

采用固相法合成了纯度较高的Mg(OH)2,并利用XRD、SEM等进行了表征.以硬脂酸钠、油酸对其进行表面处理得到改性Mg(OH)2,沉降实验表明其与液体石蜡中有较好的相容性,而且油酸改性Mg(OH)2显示出更好的效果.     

PAC混凝沉降法处理凉果废水的研究

凉果废水引起的污染已经成为严峻的问题.研究了潮安县康辉集团凉果厂综合排放废水的性质,采用混凝沉降工艺处理该废水.为了强化凉果废水的混凝预处理效果,试验研究了混凝剂聚合氯化铝(PAC)的最佳投加量.实验表明:采用PAC工艺处理凉果废水的效果较好,投药后经混凝沉降,废水的COD去除率可以达到46.73%,出水COD可以降至...     

人禽流感裂解疫苗对小鼠的免疫原性观察

目的观察人禽流感裂解疫苗对小鼠的免疫原性。方法将不同血凝素含量(20、30、45μg/ml)的铝佐剂和无佐剂人禽流感裂解疫苗各3批分别经腹腔注射免疫小鼠,0.5 ml/只,每批疫苗又分为1针、2针和3针组,每组10只,每针间隔1周,同时设空白对照组。首针免疫后21 d,分别采血,分离血清,检测血凝抑制抗体效价和中和抗体效价。结果 1针、2针组各3批无佐剂疫苗免疫小鼠的血凝抑制抗体效价和中和抗体效价分别小于1∶40和1∶200;2针、3针组各3批铝佐剂疫苗的血凝抑制抗体效价均大于1∶50,2针组20、30μg/ml血凝素铝佐剂疫苗的中和抗体效价均大于1∶200;2针、3针组20、30与45μg/ml血凝素铝佐剂疫苗的血凝抑制抗体效价和中和抗体效价差异均无统计学意义(P>0.05);且2针、3针组3批铝佐剂疫苗的血凝抑制抗体效价和中和抗体效价均明显高于相应的3批无佐剂疫苗。结论铝佐剂疫苗对小鼠的免疫原性明显优于无佐剂疫苗,且20、30μg/ml血凝素铝佐剂疫苗接种2针可获得理想的免疫效果。     

锂离子电池用双草酸硼酸锂的固相合成

详细介绍了固相法合成的一种新型电解质锂盐--双草酸硼酸锂（LiBOB）。制备过程采用草酸、氢氧化锂、硼酸为原料,其物质的量比为2.1∶[KG-*2]1∶[KG-*2]1,经球磨混合后高温烧制,烧制温度为120 ℃、脱水温度为240 ℃,所得产品经乙酸乙酯提纯后即得产物。产物通过分析测定可知,其杂质含量少且晶体结构完整;并通过热分析证实其热稳定性优于六氟磷酸锂。用其制备的电解液组装的电池,循环性能较好,所制双草酸硼酸锂达到用作电池电解质锂盐的标准。     

聚硅酸氯化铝镁絮凝剂的制备及废水处理研究

将聚硅酸( Psi)、聚合氯化铝(PAC)和氢氧化镁浆料复合,制得了不同铝硅摩尔比和盐基度的聚硅酸氯化铝镁(PACSM)絮凝剂,并用于含油废水和造纸废水的处理,且与PAC、聚硅酸氯化铝(PACS)的处理效果进行了对比.结果表明,在n(Al)∶n(Si)为10～15时,PACSM对2种废水的浊度、色度和有机物的去处效率都较高,并且处理过后的水中残留的铝含量也较低;PACSM各方面处理效果都要好于PACS和PAC絮凝剂,而PACS絮凝剂又要好于PAC絮凝剂.     

Thermal decomposition of coal fly ash by concentrated sulfuric acid and alumina extraction process based on it

The industrial applications of acidic leaching processes for alumina extraction from coal fly ash (CFA) have been limited due to its excessive usages of acid and fluoride. This limitation can be lifted by calcining the CFA with the concentrated sulfuric acid at high temperature. When CFA was mixed with the concentrated sulfuric acid of same amount and calcined at 300 °C, most of its aluminum components were transformed into aluminum sulfate. Excessive sulfuric acid was recycled by collecting sulfur trioxide produced during heating process. Morphological and X-ray diffraction evidence indicated that mullite inside CFA was thermally decomposed. Alumina and mullite were transformed into aluminum sulfate. A practical process of alumina extraction from CFA was developed based on this observation. The adoption of calcination process significantly reduced the sulfuric acid usage, shortened the process cycle, and eliminated the use of fluoride. The alumina extraction efficiency was improved up to 85%.     

Formation, densification, and selected mechanical properties of hot pressed Al4SiC4, Al4SiC4 with 30 vol.% WC, and Al4SiC4 with 30 vol.% TiC

Powders of Al₄C₃ and SiC were combined by high-energy milling to produce Al₄SiC₄, Al₄SiC₄ + 30 vol.% TiC, and Al₄SiC₄ + 30 vol.% WC. Five different temperatures were used to hot press the constituents. XRD, SEM, relative density, and hardness measurements showed that formation of single-phase Al₄SiC₄ occurred at 1450 °C and full densification (99%) was achieved at 1500 °C. Both of these temperatures are lower than previously reported. Adding TiC and WC increases hardness, while WC improves densification (99.5%).     

纳米氢氧化铝镁的制备及其吸附性能研究

以结晶氯化铝（AlCl3@·6H2O）、结晶氯化镁（MgCl2·6H2O）为主要原料,采用前驱体溶胶超临界流体干燥方法（SCDF）制备了纳米氢氧化铝镁超细粉俸,借助透射电子显微镜（TEM）、X-射线衍射仪（XRD）仪器对纳米氢氧化铝镁超细粉体进行了表征;同时研究纳米氢氧化铝镁超细粉体对CP吸附性能。