室内研究和现场应用表明,聚乙烯醇类防塌剂表现出较明显的增粘负效应,可引起钻井液粘度的急剧增加,严重影响其推广应用.通过金属盐催化降解和阳离子化反应,研制出了抑制性好且增粘负效应低的阳离子化改性多元醇防塌剂.考察了阳离子化试剂、反应温度、反应时间对取代度、反应效率和产品主要性能的影响,得出了阳离子化多元醇防塌剂最佳制备条件,即：PVA与阳离子化试剂物质的量比为1：1,反应温度为50℃,反应时间为4 h,阳离子度可达0.435.     

香豆胶衍生物的化学结构及稳定性研究

将市售商品溶于水,用异丙醇沉析提纯,溶于0.1 mol/L NaNO3纯水溶液中,经0.5μm滤膜过滤后用水相凝胶渗透色谱法(GPC)测定,测得香豆胶(FG)、羟丙基香豆胶(HPFG)、阳离子香豆胶(CFG)的数均、重均相对分子质量Mn、Mw分别为:1.19×105、3.36×105,8.52×104、2.85×105,9.33×104、2.87×105。用甘露聚糖链在碱性条件下醚化时发生降解,解释两种改性FG的相对分子质量较FG低而多分散性(Mw/Mn)较FG高的测试结果。认为商品FG的1%水溶液黏度(1300 mPa.s)高于商品HPFG和CFG(分别为705和610 mPa.s)的原因是前者相对分子质量较高且残渣含量也较高(~10%,后二者为1%~2%)。HPFG的取代度为0.12,根据文献发表的13C-NMR数据确认HPFG分子链上羟丙基取代位置为C6。讨论了香豆胶(半乳甘露聚糖)的化学结构。热重分析法测定的热稳定性,HPFG高于CFG,CFG又高于FG。图6表3参13。     

氧化铝丝的研制

氧化铅丝生产过程中最关键的工艺是连续阳极氧化。氧化膜击穿电压决定于氧化膜厚度。控制膜厚度的三要素为:电解液(成份、浓度及温度),槽电压和铝丝走速。     

Two-tier architecture for unconstrained handwritten character recognition

In this paper, we propose an approach that combines the unsupervised and supervised learning techniques for unconstrained handwritten numeral recognition. This approach uses the Kohonen self-organizing neural network for data classification in the first stage and the learning vector quantization (LVQ) model in the second stage to improve classification accuracy. The combined architecture performs better than the Kohonen self-organizing map alone. In the proposed approach, the collection of centroids at different phases of training plays a vital role in the performance of the recognition system. Four experiments have been conducted and experimental results show that the collection of centroids in the middle of the training gives high performance in terms of speed and accuracy. The systems developed also resolve the confusion between handwritten numerals.     

镍代钴矿用硬质合金的新进展

概述了镍代钴矿用硬质合金的国内外进展情况．     

Tannins/melamine–urea–formaldehyde (MUF) resins substitution of chrome in leather and its characterization by thermomechanical analysis

A new sulfonated melamine–urea–formaldehyde (MUF) resin of relatively low melamine content, prepared according to a sequential formulation, has been shown to be highly effective when coupled with different natural vegetable tannins to produce leather with the same good characteristics of leather prepared with chrome salts. In particular, the antishrinkage effectiveness of the leather prepared according to the new approach is comparable to that obtained with chrome tanned leathers. The comparison of the traditional leather shrinkage temperatures test method with a new thermomechanical analysis (TMA) test method in tension yields thermograms presenting three major modulus of elasticity (MOE) peaks. These are closely connected to molecular level phenomena determining the shrinkage temperature of leather. The three determining parameters appear to be as follows: (1) The average value of the temperatures at which the three MOE peaks occur: the higher the value of this average, the lower is the shrinkage of leather. (2) The average of maximum MOE values of the TMA peaks: the higher this average is, the better is the leather in regard to antishrinkage effectiveness. This means the leather maximum MOE at each peak is a measure of the resistance to the contraction force induced by heat. (3) The relative intensity of the first TMA peak in relation to the second: the higher the value of the MOE for the first TMA peak is in relation to the second peak, the lower the leather shrinkage appears to be. However, it has not been possible to better define or quantify this latter effect. This new TMA test method in tension has also yielded a mathematical relationship correlating the thermogram peak temperatures and MOE averages with the traditional shrinkage temperature to a high degree of confidence. A previous TMA test method, in compression, has proven to yield more problematic and finally not very reliable results when one needs to apply it to a wide variety of different cases. © 2003 Wiley Periodicals, Inc. J Appl Polym Sci 88: 1889–1903, 2003     

What is being masked in object substitution masking?

Object substitution masking (OSM) is said to occur when a perceptual object is hypothesized that is mismatched by subsequent sensory evidence, leading to a new hypothesized object being substituted for the first. For example, when a brief target is accompanied by a longer lasting display of nonoverlapping mask elements, reporting of target features may be impaired. J. T. Enns and V. Di Lollo (2000) considered it an outstanding question whether OSM masks some or all aspects of a target. The authors report three experiments demonstrating that OSM can selectively affect target features. Participants may be able to detect a target while being unable to report other aspects of it or to report the color but not the orientation of a target (or vice versa). We discuss these findings in relation to two other visual phenomena. (PsycINFO Database Record (c) 2010 APA, all rights reserved)     

高度有序多孔氧化铝模板的制备工艺与生长机制的研究

采用二次氧化法制备出高度有序的多孔氧化铝模板，结合扫描电镜和原子力显微镜对其结构、形貌进行观察和表征。研究了铝箔预处理和温度等对多孔氧化铝模板孔洞有序性的影响，讨论了有序孔洞的自组织生长机理。     

Optimization of anodic oxidation and Cu–Cr oxide catalyst preparation on structured aluminum plates processed by electro discharge machining

This paper describes the optimization of three processes applied in fabrication of a microstructured reactor for complete oxidation of volatile organic compounds. The first process involves the optimization of the electro discharge machining (EDM) method to produce a set of microchannels with a high length to diameter ratio of 100, with a standard deviation from the average diameter below 0.2%, and with a surface roughness not higher than 2.0 μm. To satisfy these criteria, fabrication of microchannels must be carried out with two machining passes in the Al51st alloy. Then, the effect of several parameters on the anodization current efficiency with respect to oxide formation was studied. The best process conditions to get a 30 μm porous alumina layer in a 0.4 M oxalic acid electrolyte, were found to be a temperature of 1 °C, an anodic current density of 5 mA/cm², and 23 h oxidation time. At last, the resulting coatings were impregnated with an aqueous solution of copper dichromate followed by drying and calcination at 450 °C to produce active catalysts. The effect of a copper dichromate concentration, number of impregnation cycles (1 or 2), and different after-treatments on catalytic activity and stability in complete oxidation of n-butane were studied. The catalytic activity of the obtained coatings is superior to that of alumina supported pelletized catalysts even at much lower loadings of active metals.     

Production of silver‐doped analcime by isomorphous substitution technique

BACKGROUND: Metal‐exchanged zeolites have been reported to have significant limitations on cayalytic activity, such as counterbalancing the negative framework charges and limitation of active space. Alternative methods of incorporating silver ions into the framework of zeolites are therefore necessary. This paper reports on a technique for producing silver doped analcime by isomorphous substitution of silver ion into the framework of analcime. The amount of aluminium in the gel composition was reduced by a factor of 5%, 10% and 20% and an equivalent amount of silver was added to the gel and treated in a conventional manner for zeolite crystallisation. Some of the aluminium in the reaction gel was replaced with the silver. The silver‐doped analcime samples where characterised by X‐ray diffraction (XRD), scanning electron microscopy (SEM), energy dispersive X‐rays (EDX), Fourier transform infrared (FTIR) spectroscopy and inductively coupled plasma‐atomic emission spectroscopy (ICP‐AES) analysis. RESULTS: The amount of silver ions loaded for each reduction of aluminium as determined by EDX were found to be (w/w) 0.29%, 1.41% and 2.10%, respectively. XRD pattern SEM images of the silver‐doped analcime showed the presence of zeolite P in addition to analcime. CONCLUSION: Silver‐doped analcime was successfully produced with different silver loadings and may exhibit higher anti‐microbial activities than silver‐exchanged counterparts. Copyright © 2008 Society of Chemical Industry